• Journal of the Korean Society for Heat Treatment
• /
• v.5 no.4
• /
• pp.195-200
• /
• 1992

SCM 415 has been vacuum carburized in the carburizing pressure of 60-65kpa and the carburizing temperature of 1233k and 1273k after varied to 0-20 in the ratio of $N_2/C_3H_8$ and then diffusion treated for various times at 1123k. The results obtained from the experiment are as follows. 1. With increasing from 0 to 20 in ratio of $N_2/C_3H_8$ the sooting formation of surface after carburizing considerably decreased. 2. The hardness control and surface carbon content of carburizing surface has been modified by the addition of nitrogen to the propan. 3. The appoximate value of k is indirectry calculated at 1123k which results are obtained to $0.58{\times}10^{-2}(wt.%.S^{-1/2})$. 4. A great deal of propan by addition of nitrogen gas in carburizing gas was possible to saving without considerable change in case hardening depth. 5. The effective carburizing depth range is obtained to 0.8-1.1mm by diffusion temperature of 1123k after carburization at 1273k-3.6ks, and the surface hardness is increased as the increasing of $T_D/T_c$ in our experimental condition, and the maximum hardness as reachin distance from surface is decreased.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.4
• /
• pp.53-60
• /
• 1991

This study has been performed to investigate into the internal oxidation characteristics of low carbon steel with respect to the added amount of air in nitrogen-propane atmosphere after gas carburizing for various times at $930^{\circ}C$. The results obtained from the experiment are as follows ; (1) Optical micrographs have shown that the internal oxidation is unlikely to occur in the gas atmosphere without air and that oxidized zone in the outer surface layer is formed in the gas atmosphere with air revealing that the depth of oxidized zone increases with increasing the added amount of air. (2) The formation of internally oxidized zone in the outer surface layer has been found to be inhibited as Ni content increases, i. e, the amount of alloying element increases. (3) The depth of oxidation has been measured to increase with almost parabolically gas carburizing time of up to 6 hours.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.4
• /
• pp.272-276
• /
• 2017

The response of AISI 310 type austenitic stainless steel to the novel low temperature plasma carburizing process has been investigated in this work. This grade of stainless steel shows better corrosion resistance and high temperature oxidation resistance due to its high chromium and nickel content. In this experiment, plasma carburizing was performed on AISI 310 stainless steel in a D.C. pulsed plasma ion nitriding system at different temperatures in $H_2-Ar-CH_4$ gas mixtures. The working pressure was 4 Torr (533Pa approx.) and the applied voltage was 600 V during the plasma carburizing treatment. The hardness of the samples was measured by using a Vickers micro hardness tester with the load of 100 g. The phase of carburized layer formed on the surface was confirmed by X-ray diffraction. The resultant carburized layer was found to be precipitation free and resulted in significantly improved hardness and corrosion resistance.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.5
• /
• pp.262-269
• /
• 2006

The development of eco-friendly low pressure carburizing system with high pressure gas quenching(LPC-GQ, 500kg/charge) led to new stage in the fundamental case-hardening treatments. This is due to its ability to provide tighter tolerances on the carburizing process with notable reductions in distortion of the carburized and hardened workpiece. This system is characteristics by high uniformity and reproducibility of heat treatment results, absence of an intergranular oxidation layer, carburizing of complex shapes, reduced cycle time, low operating costs, simplified production, eliminate post washing, and reduced grinding costs.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.3
• /
• pp.116-121
• /
• 2009

The 2-step low temperature plasma processes (the combined carburizing and post-nitriding) offer the increase of both surface hardness and thickness of hardened layer and corrosion resistance than the individually processed low temperature nitriding and low temperature carburizing techniques. The 2-step low temperature plasma processes were carried out for improving both the surface hardness and corrosion resistance of AISI 316L stainless steel. The influence of gas compositions on the surface properties during nitriding step were investigated. The expanded austenite (${\gamma}_N$) was formed on all of the treated surface. The thickness of ${\gamma}_N$ and concentration of N on the surface increased with increasing both nitrogen gas and Ar gas levels in the atmosphere. The thickness of ${\gamma}_N$ increased up to about $20{\mu}m$ and the thickness of entire hardened layer was determined to be about $40{\mu}m$. The surface hardness was independent of nitrogen and Ar gas contents and reached up to about 1200 $HV_{0.1}$ which is about 5 times higher than that of untreated sample (250 $HV_{0.1}$). The corrosion resistance in 2-step low temperature plasma processed austenitic stainless steels was also much enhanced than that in the untreated austenitic stainless steels due to a high concentration of N on the surface.

• Journal of the Korean Society for Heat Treatment
• /
• v.3 no.3
• /
• pp.13-20
• /
• 1990

SCM 21 and D.P steel were carburized in vacuum using prophane at a temperature ranging from 1228k to 1308k under a gas pressure ranging from 21.3kpa to 61.8kpa, and the following results were obrained. 1) D.P. steel has considerable efficiency in depressing the grain growth during the high temperature carburizing and it has fine structure even at 1268k for 14.4ks when carburizied. Therefore this steel is expected to be suitable for vacuum carburizing at a high temperature. 2) Case depth was increased as the carburizing temperature increases and it was 3.2mm at max, temperature of 1308k, for max, time of 14.4ks and under max, pressure of 61.8kpa. Thus vacuum-carburizing was considered effective for the materials which need case depth, which is necessary for machine structure use. 3) The rate of case depth of SCM 21 was faster than D.P. steel under same carburizing conditions and the increasing rate of the case depth was constant. 4) Case depth was increased as the gas pressure becomes high under same carburizing temperature. 5) Case carbon concentration, $C_s$, of SCM 21 obeys to a formula, $$C_s=kt^{1/2}+C_0$$ Where k is $2.15{\times}10^{-2}$($wt%.S^{-1/2}$) and this value is a little bit lower than that of SNCM 815.

• 한국연소학회:학술대회논문집
• /
• 2003.12a
• /
• pp.109-113
• /
• 2003

Low pressure or vacuum carburizing(LPC) has undergone major further developments since 1980 and now it has achieved industrial maturity. The advantage of low pressure vacuum carburizing over gas carburizing is not only the creation of surface entirely free of oxide and environmentally friendly but also a reduction in batch times, lower gas and energy consumption and the prevention of soot. In this study the experiment was carried out to investigate the effects of vacuum atmosphere in the heating furnace. Heat transfer rate and uniformity of temperatures of test samples in the pressure range of a few 0.1torr was examined on a test charge of 100kg. It is found that the fuel saving rate due to decreasing heating time reach to 20% in the vacuum heating mode as compared with atmospheric heating mode. Also the uniformity of temperatures in the samples was improved significantly in the vacuum heating mode. Also the effects of the RC fan for stirring atmosphere inside furnace was examined. Results shows RC fan appears to provide a reasonable tool for improving uniformity of temperature in the atmospheric heating mode.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.707-713
• /
• 1998

The influence of plasma carburizing process on the surface hardness of SCM415 low-alloy steel (0.15% C) was investigated under the various process conditions of gas composition. gas pressure, plasma current density. temperature and time. The effective case depth was found to depend on the amount of methan gas containing carbon. thus the deepest case depth and the uniform hardeness were obtained with the 100% methan gas. The case depth increased with the plasma current density. The effective plasma carburizing temperature of SCM415 steel was found to be higher than 85$0^{\circ}C$, and the case depth was proportional to the square root of carburizing time under the same current density. The bending fatigue strength of the plasma carburized specimen is' higher than those of as- received specimen or reheat-quenched specimen.

• Korean Journal of Metals and Materials
• /
• v.46 no.3
• /
• pp.125-130
• /
• 2008

Conventional plasma carburizing or nitriding for austenitic stainless steels results in a degradation of corrosion resistance. However, a low temperature plasma surface treatment can improve surface hardness without deteriorating the corrosion resistance. The 2-step low temperature plasma processes (the combined carburizing and post nitriding) offers the increase of both surface hardness and thickness of hardened layer and corrosion resistance than the individually processed low temperature nitriding and low temperature carburizing techniques. In the present paper, attempts have been made to investigate the influence of the introduction of Ar gas (0~20%) in nitriding atmosphere during low temperature plasma nitriding at $370^{\circ}C$ after low temperature plasma carburizing at $470^{\circ}C$. All treated specimens exhibited the increase of the surface hardness with increasing Ar level in the atmosphere and the surface hardness value reached up to 1050 HV0.1, greater than 750 $HV_{0.1}$ in the carburized state. The expanded austenite phase (${\gamma}_N$) was observed on the most of the treated surfaces. The thickness of the ${\gamma}_N$ layer reached about $7{\mu}m$ for the specimen treated in the nitriding atmosphere containing 20% Ar. In case of 10% Ar containing atmosphere, the corrosion resistance was significantly enhanced than untreated austenitic stainless steels, whilst 20% Ar level in the atmosphere caused to form CrN in the N-enriched layer (${\gamma}_N$), which led to the degradation of corrosion resistance compared with untreated austenitic stainless steels.

• Korean Journal of Metals and Materials
• /
• v.50 no.7
• /
• pp.517-522
• /
• 2012

In this study, a super carburizing treatment was applied to improve roller pitting fatigue life. It produced excellent properties of surface hardness and temper softening resistance by forming precipitation of fine and spherodized carbides on a tempered marstensite matrix through the repeated process of carburization and diffusion after high temperature carburizing step 1. The cycle II performed two times carburizing/diffusion cycle (process) after super carburization at $1,000^{\circ}C$ had fine and spherodized carbides to subsurface $200{\mu}m$. In this case, the carbide was $(Fe,Cr)_3C$ and there was not any massive carbides. In the case of Cycle II, the roller pitting fatigue life had a 6.15 million cycles. It was improved 48% compared to normal gas carburizing treatment.