In this paper, AZO thin film was deposited on polyethylene terephthalate(PET) substrate by r. f. magnetron sputtering method from a ZnO target mixed with 2[wt%] Al2O3. The flexible film-typed dye sensitized solar cell(F-DSC) was fabricated and photo-electric conversion efficiency was investigated. The results showed that the minimum resistivity and the maximum deposition rate of AZO conducting film were recorded as $1.8{\times}10^{-3}[{\Omega}{\cdot}cm]$ and 25.5[nm/min], respectively at r.f. power of 220[W]. From the analysis of XPS data an improvement of electrical resistivity or an increase in carrier concentration with increasing sputtering power may be related to the generation of lattice imperfections as a result of increasing component ratio of O1s/Zn2p, which generates donor carriers or active growth of crystalline grain. The photo-electric conversion efficiency of F-DSC with AZO conducting electrode was over 2.79[%], which was comparable as that with commercially available ITO electrode.

• Korean Journal of Materials Research
• /
• v.30 no.10
• /
• pp.566-572
• /
• 2020

In the recent years, thin film solar cells (TFSCs) have emerged as a viable replacement for crystalline silicon solar cells and offer a variety of choices, particularly in terms of synthesis processes and substrates (rigid or flexible, metal or insulator). Among the thin-film absorber materials, SnS has great potential for the manufacturing of low-cost TFSCs due to its suitable optical and electrical properties, non-toxic nature, and earth abundancy. However, the efficiency of SnS-based solar cells is found to be in the range of 1 ~ 4 % and remains far below those of CdTe-, CIGS-, and CZTSSe-based TFSCs. Aside from the improvement in the physical properties of absorber layer, enormous efforts have been focused on the development of suitable buffer layer for SnS-based solar cells. Herein, we investigate the device performance of SnS-based TFSCs by introducing double buffer layers, in which CdS is applied as first buffer layer and ZnMgO films is employed as second buffer layer. The effect of the composition ratio (Mg/(Mg+Zn)) of RF sputtered ZnMgO films on the device performance is studied. The structural and optical properties of ZnMgO films with various Mg/(Mg+Zn) ratios are also analyzed systemically. The fabricated SnS-based TFSCs with device structure of SLG/Mo/SnS/CdS/ZnMgO/AZO/Al exhibit a highest cell efficiency of 1.84 % along with open-circuit voltage of 0.302 V, short-circuit current density of 13.55 mA cm^-2, and fill factor of 0.45 with an optimum Mg/(Mg + Zn) ratio of 0.02.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.61.1-61.1
• /
• 2010

$CuIn_{1-x}-GaxSe_2$ based materials with direct bandgap and high absorption coefficient are promising materials for high efficiency hetero-junction solar cells. CIGS champion cell efficiency(19.9%, AM1.5G) is very close to polycrystalline silicon(20.3%, AM1.5G). A reduction in the price of CIGS module is required for competing with well matured silicon technology. Price reduction can be achieved by decreasing the manufacturing cost and by increasing module efficiency. Manufacturing cost is mostly dominated by capital cost. Device properties of CIGS are strongly dependent on doping, defect chemistry and structure which in turn are dependent on growth conditions. The complex chemistry of CIGS is not fully understood to optimize and scale processes. Control of the absorber grain size, structural quality, texture, composition profile in the growth direction is important to achieving reliable device performance. In the present work, CIS nanoparticles were prepared by a simple wet chemical synthesis method and their structural and optical properties were investigated. XRD patterns of as-grown nanopowders indicate CIS(Cubic), $CuSe_2$(orthorhombic) and excess selenium. Further, as-grown and annealed nanopowders were characterized by HRTEM and ICP-OES. Grain growth of the nanopowders was followed as a function of temperature using HT-XRD with overpressure of selenium. It was found that significant grain growth occurred between $300-400^{\circ}C$ accompanied by formation of ${\beta}-Cu_{2-x}Se$ at high temperature($500^{\circ}C$) consistent with Cu-Se phase diagram. The result suggests that grain growth follows VLS mechanism which would be very useful for low temperature, high quality and economic processing of CIGS based solar cells.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.58.1-58.1
• /
• 2010

Stainless Steel의 유연한 기판을 사용하여 ZnO:Al/Ag의 후면전극에서 Ag 증착 실험조건 변화를 통해서 light trapping을 개선한 n-i-p 구조의 플렉서블 미세결정질 실리콘 박막 태양전지를 제작하였다. 실험 방법으로 마그네트론 스퍼터를 사용하여 Stainless Steel 기판 위에 ZnO:Al/Ag를 증착하여 후면전극으로 사용되는 back reflector를 제작하였으며 그 위에 미세결정질 실리콘 박막을 증착하였다. Back reflector에서 Ag 박막의 증착 온도가 증가할수록 표면결정 성장으로 roughness가 증가하여 반사도를 증가하였다. 또한, Ag 박막 증착 두께와 압력 변화에 따른 광학적 특성변화를 Atomic Force Microscope(AFM), Scanning Electron Microscopy(SEM),UV-visible-nIR spectrometry로 조사하여 최적의 조건을 찾았으며 개선된 back reflector의 특성이 n-i-p 구조의 플렉서블 미세결정질 실리콘 박막 태양전지에 적용하여 light trapping의 증가가 태양전지에서 광학적인 특성 변화 및 효율 향상에 영향을 주는지 Photo IV와 EQE(External Quantum Efficiency)를 통하여 조사하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.62.1-62.1
• /
• 2010

CIS(CuInSe2)계 화합물 태양전지는 높은 광흡수계수와 열적 안정성 및 조성 조절을 통한 밴드갭 조절이 용이해 고효율 박막 태양전지로 각광 받고 있다. 또한 CIGS 태양전지는 기존의 유리기판 대신 유연한 기판을 사용해 flexible 태양전지 제조가 가능하다. 이러한 유연기판은 보통 stainless steel과 같은 금속 기판이 많이 사용되는데 기존의 soda-lime glass 기판과는 달리 금속기판에는 Na이 첨가되어 있지 않아 별도의 Na첨가를 필요로 한다. Na은 CIGS 흡수층의 조성조절을 용이하게 하여 태양전지의 변환 효율을 향상시키는 역할을 한다. 본 연구에서 기판은 Na이 첨가되어있지 않은 corning glass를 사용 하였으며 NaF를 이용해 Mo가 증착된 기판에 NaF의 두께를 달리하며 증착해 CIGS 흡수층의 grain 사이즈를 비교 하였으며 그 후 태양전지 소자를 제조해 광전특성을 분석하였다. 후면 전극으로 약60nm 두께의 Mo를 DC Sputtering 방법을 이용해 증착 하였다. buffer층으로는 약 50nm의 CdS층을 CBD방법을 이용하여 제조 하였으며 TCO 층으로 약 50nm의 i-ZnO와 약 450nm의 Al-ZnO를 RF Sputtering방법으로 증착 하였다. 마지막으로 앞면 전극으로 약 $1{\mu}m$의 Al을 Thermal Evaporation방법으로 증착하였다. 태양전지 소자의 면적은 $0.49cm^2$로 효율을 비교 분석하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.3.2-3.2
• /
• 2011

In recent years, inkjet printing technology has received significant attention as a micro/nanofabrication technique for flexible printing of electronic circuits and solar cells, as well for biomaterial patterning. It eliminates the need for physical masks, causes fewer environment problems, lowers fabrication costs, and offers good layer-to-layer registration. To fulfill the requirements for use in the above applications, however, the inkjet system must meet certain criteria such as high frequency jetting, uniform droplet size, high density nozzle array, etc. Existing inkjet devices are either based on thermal bubbles or piezoelectric pumping; they have several drawbacks for flexible printing. For instance, thermal bubble jetting has limitations in terms of size and density of the nozzle array as well as the ejection frequency. Piezoelectric based devices suffer from poor pumping energy in addition to inadequate ejection frequency. Recently, an electrohydrodynamic (EHD) printing technique has been suggested and proposed as an alternative to thermal bubble or piezoelectric devices. In EHD jetting, a liquid (ink) is pumped through a nozzle and a strong electric field is applied between the nozzle and an extractor plate, which induce charges at the surfaces of the liquid meniscus. This electric field creates an electric stress that stretches the meniscus in the direction of the electric field. Once the electric field force is larger than the surface tension force, a liquid droplet is formed. An EHD inkjet head can produce droplets smaller than the size of the nozzle that produce them. Furthermore, the EHD nano-inkjet can eject high viscosity liquid through the nozzle forming tiny structures. These unique features distinguish EHD printing from conventional methods for sub-micron resolution printing. In this presentation, I will introduce the recent research results regarding the EHD nano-inkjet and the printing system, which has been applied to solar cell or thin film transistor applications.

• Current Photovoltaic Research
• /
• v.11 no.1
• /
• pp.8-12
• /
• 2023

In this work, we investigated the thickness of Ag precursor layer to improve the performance of flexible CIGSe solar cells grown on stainless steel (STS) substrates through three-stage co-evaporation with Ga grading followed by alkali treatments. The small amount of incorporated Ag in CIGSe films showed enhancement in the grain size and device efficiency. With an optimal 6 nm-thick Ag layer, the best cell on the STS substrate yielded more than 16%, which is comparable to the soda-lime glass (SLG) substrate. Thus, the addition of controlled Ag combined with alkali post-deposition treatment (PDT) led to increased open-circuit voltage (VOC), accompanied by the increased built-in potential as confirmed by capacitance-voltage (C-V) measurements. It is related to a reduction of charge recombination at the depletion region. The results suggest that Ag alloying and alkali PDT are essential for producing highly efficient flexible CIGSe solar cells.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.125.1-125.1
• /
• 2011

빛 에너지를 전기에너지로 변환하는 발전소자인 태양전지는 청정 재생 에너지원으로 최근 Si 박막 태양전지의 고 효율화를 위해 여러 기술적인 면에서 개발되어지고 있다. 현재 박막형 태양전지는 실리콘계가 주류를 이루고 있으며, 유리 혹은 유연성기판(금속 or 고분자)에 비정질 실리콘 박막을 형성시킨 태양전지와 실리콘웨이퍼의 양면에 태양전지를 형성함으로써 효율을 극대화시킨 이종접합태양전지 등이 연구되고 있다. 특히 flexible 태양전지는 hard 기판에 비해 비교적 저가인 플라스틱 필름과 금속 foil을 기판으로 이용함으로서 저가화가 용이하며, 가볍고 유연성을 갖추고 있어 휴대와 시공에 있어 매우 우수한 장점을 가지고 있다. 본 연구에서는 flexible 기판(stainless steel)을 이용하여 태양전지 내 반사막 층이 미치는 영향을 알아보기 위하여 AZO/Ag 이중구조 박막의 특성을 연구하였다. RF magnetron sputtering system을 이용하였으며, 상온에서 Ag/AZO 이중구조 박막을 제조하였다. stainless steel 기판 위에 Ag층을 25nm 두께로 증착하였으며 연속공정으로 AZO 박막을 100~500nm의 두께경사를 가지도록 성장시켰다. 이 때의 AZO/Ag 이중구조 박막의 표면 morphology는 AFM 분석결과 7nm~3nm의 값을 나타내었으며, AZO 박막의 두께가 증가할수록 rms 값이 감소하는 경향을 보여주었다. 본 발표에서는 flexible 기판 상에 성장된 AZO/Ag 이중구조 박막의 전기적, 광학적 특성 등에 관하여 추가적으로 토론한 후 태양전지 효율 중 흡수층 내 반사막 층이 미치는 역할을 알아보겠다.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1485-1486
• /
• 2011

A layer of $TiO_2$ thin film less than ~500nm in thickness, as a blocking layer, was coated by sol-gel method directly onto the anode electrode to be isolated from the electrolyte in dye-sensitized solar cells (DSCs). This is to prevent the electrons from back-transferring from the electrode to the electrolyte (I-/I3-). The effects of heat treatment conditions of the gel and as-coated film on the thickness and consolidation to substrate were studied. The flexible DSCs were fabricated with working electrode of Ti thin foil coated with blocking $TiO_2$ layer, dye-attached mesoporous $TiO_2$ film, gel electrolyte and counter electrode of Pt-deposited indium doped tin oxide/polyethylene naphthalate (ITO/PEN). The photo-current conversion efficiency of the cell was 5.3% ($V_{oc}=0.678V$, $J_{sc}=12.181mA/cm^2$, ff=0.634) under AM1.5, 100 mW/$cm^2$ illumination.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.336-336
• /
• 2011

Over the past decades, organic semiconductors have been investigated intensely for their potential in a wide range of optoelectronic device applications since the organic materials have advantages for very light, flexible and low cost device fabrications. In this study, we fabricated small-molecule organic solar cells (OSCs) based on chloro[subphthalocyaninato]boron(III) (SubPc) as an electron donor and $C_{60}$ as an electron acceptor material. Recently SubPc, a cone-shaped molecule with $14{\pi}$-electrons in its aromatic system, has attracted growing attention in small-molecule OSC applications as an electron-donating material for its greater open-circuit voltage (VOC), extinction coefficient and dielectric constant compared to conventional planar metal phthalocyanines. In spite of the power conversion efficiency (PCE) enhancement of small-molecule OSC using SubPc and $C_{60}$, however, the study on the interface between donor-acceptor heterojunction of this system is limited. In this work, SubPc thin films at various thicknesses were deposited by organic molecular beam deposition (OMBD) and the evolution of surface morphology was observed using atomic force microscopy (AFM) and field emission scanning electron microscopy (FE-SEM). We also investigated the influence of film thickness and surface morphology on the PCE of small-molecule OSC devices.