• Journal of the Korean Chemical Society
• /
• v.35 no.4
• /
• pp.422-426
• /
• 1991

In order to synthesize high-purity alpha alumina fine powder, the aluminum hydroxide and ammonium aluminum sulfate(alum) precursor were prepared from natural alumino-silicate(halloysite). The thermal decomposition mechenism for both precursors was elucidated by DTA/TG, XRD and IR analysis. The microstructure, specific surface area and purity of ${\alpha}-Al_2O_3$ were characterized by SEM, and BET analysis. The particle size of ${\alpha}-Al_2O_3$ was determined to be ${\phi}$ = 0.1∼0.5 ${\mu}$m. However, the specific surface area for the alum derived ${\alpha}-Al_2O_3$(89.0 m$^2$/g) was extremely higher than that for the aluminum hydroxide derived one(7.3 m$^2$/g).

• Korean Chemical Engineering Research
• /
• v.48 no.1
• /
• pp.75-79
• /
• 2010

The precursor powders with thin wall structure were prepared by spray pyrolysis from the spray solution with ethylenediaminetetraacetic acid, citric acid and $NH_4Cl$ flux. The $BaMgAl_{10}O_{17}:Eu$ phosphor powders formed from the spray solution without organic additives and flux material had sizes of $1{\sim}5{\mu}m$ and hollow structure with high thickness at post-treatment temperature of $1,200^{\circ}C$. However, $BaMgAl_{10}O_{17}:Eu$ phosphor powders formed from the spray solution with ethylenediaminetetraacetic acid, citric acid and $NH_4Cl$ flux had fine size and plate-like shape. The mean crystallite sizes of the phosphor powders with fine sizes were 23, 35, and 33 nm when the content of $NH_4Cl$ flux were 0, 6, 35 wt% of phosphor. The photoluminescence intensity of the phosphor powders formed from the spray solution with the optimum amount of $NH_4Cl$ flux as 35 wt% was 215% of that of the phosphor powders formed from the spray solution without flux material.