• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.5
• /
• pp.66-71
• /
• 1998

It is required the superior materials for the parts of machines or structures, which could be endurable in severe load and environment. According to advancement of casting technology, nodular graphite cast iron is used as suitable for such condition. But nodular graphite cast iron is scattering of fatigue strength and low reliability. Therefore in this study, the effect of matrix structure and number of nodular graphite on the initiation of fatigue crack and fatigue strength. It was found that the material which has relatively high ferrite volume fraction was more easily cracked than other materials and fatigue limit was low. The material which has not found pinhole on the surface, the crack was initiated in graphite went through ferrite and propagated into through graphite, but separated graphite and ferrite grain boundary and combined with other cracks to fro large one.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.4 no.4
• /
• pp.147-155
• /
• 1996

The purpose of present paper is to estimate the static and fatigue bending strengths of CFRP(carbon fiber reinforced plastic) laminates having impact damage(FOD). The specimens which are formed with the different stacking composition, EPOXY and PEEK matirx and orthotropic and quasi-isotropic laminated plates, are prepared for this experiment. A steel ball is impacted on CFRP laminates, generating impact damages, and the three-point fatigue bending test is carried out by using the impacted laminates to investigate the influence of the stackin composition on the fatigue strength of CFRP laminates.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.12 no.1
• /
• pp.38-44
• /
• 2003

In this study, endurance limit and fatigue behavior of load carrying fillet welded cruciform joints depending on commonly used welding methods such as SMAW, SAW, MIG and FCAW are investigated. In respect of endurance limit SMAW specimen showes highest result, and then MIG, SAW, FCAW in descending order. However, SMAW specimen showes lowest crack growth rate and it followed by MIG, FCAW, SAW. By these results, it is needed to use SMAW or MIG welding methods for welding structures with small welding capacity and SAW or FCAW methods for large welding structures with respect to economic benefits and operation efficiency of welding. It was also shown fatigue crack growth rate was more influenced by the strenght of welding materials than the endurance limit of welding materials.

• Journal of the Korean Society for Precision Engineering
• /
• v.5 no.3
• /
• pp.71-80
• /
• 1988

This paper dealt with experimentally the effect of $N_2$ and $H_2$ gas mixtures ratio in the fatigue characteristics of SM45C on Ion-nitrided. The specimen were treated water cooling after Ion-nitriding at $500^{\circ}C$ and 5 torr. in 80% $N_2$and 50% $N_2$gas mixtures ratio in the atmosphere for 3 hrs. The hardness distribution and the depth of nitriding layer shows more increase in 80% $N_2$gas mixture ratio than 50% $N_2$. Ion-nitrided specim- en for 80% $N_2$gas mixture ratio show more increase infatigue strenght in the $>1.5{\times}10^5$ cycles region than 50% $N_2$. In the $<1.5{\times}10^5$cycles region, fatigue failure is due to cracking of the brittle nitrided case, and the propergation of the surface cracks into the core. But in the $>1.5{\times}10^5$cycles region, it is found that cracks propagate from the non-metallic inclusions in the subsurface.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.12-20
• /
• 1997

구조의 용접접합부에는 재료의 항복응력 크기의 용접잔류응력이 발생되고, 이 잔류응력 상태에서는 응력비(최소응력/최대응력)의 영향이 거의 없다는 것이 일정 진폭 하중조건의 피로실험결과로부터 알려져 있다. 이와 관련하여, 용접구조의 설계 단계에서는 초기 용접잔류응력이 그래도 잔류한 소형실험편의 일정진폭하중 상태의 피로실험 결과로부터 도출된 피로설계선도(S-N 선도)를 이용, 변동하중에 의한 응력 진폭의 밀도분포만으로 일생동안의 누적피해도를 구해 피로강도를 평가하는 것이 일 반적이다. 지금까지는 선박용접구조의 경우도 이러한 개념으로 피로강도 평가를 수행 하였으나, 일반적인 육상 또는 해상 용접구조물과는 달리, 화물의 적재 등의 정하중 이력에 의한 응력변동폭은 피로를 유발하는 파랑 응력변동폭보다 상당히 크다. 그리 고, 정하중에 의해 용접접합부에 인장응력을 발생시키는 하중이력을 받을 경우, 초기 용접잔류 응력은 상당히 저하될 것으로 생각된다. 본 연구에서는 인장응력을 유발하는 정하중 이력에 의해 저하된 용접잔류응력분포와 이러한 잔류응력분포를 가진 선측 종늑골 용접접합부의 피로강도를 검토한다.