• Journal of the Korean Society for Railway
• /
• v.7 no.1
• /
• pp.14-19
• /
• 2004

The effect of surface damage on fatigue properties of catenary wires were investigated to estimate their service lift. As surface defects of the wires caused by surface corrosion increase, surface roughness gets worse, and as roughness increases, it is easy for moisture coming from rain and dew to be condensed around uneven parts of the surface. The condensed moisture causes a locally severe corrosion which leads to damage of the wires. Corrosion of catenaty wires can make their actual lifetime shorter than that originally designed. The amount of decrease was more prominent as environmental conditions became more corrosive. They are also vibrated with some amplitude everytime pantographs touch contact line. The frequent cyclic load on the wire may result in a fatigue fracture. Surface damage by corrosion can make formation of crack initiation at fatigue. In the present study, the fatigue life of the used wire was measured 35 to 50% compared with that of new one in average.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.1
• /
• pp.167-174
• /
• 2003

Fatigue damage of 2.2Ni-1Cr-0.5Mo steel used fir high strength pressure tubes and vessels was evaluated using uniaxial specimens subjected to strain-controlled fatigue loading. Based on the fatigue test results from different strain ratios of -2. -i 0, 0.5, 0.75, the fatigue damage of the steel was represented by using a cyclic strain energy density. Mean stress relaxation depended on the magnitude of the applied strain amplitude. The high pressure vessel steel exhibited the cyclic softening behavior. Total strain energy density consisting of the plastic strain energy density and the elastic tensile strain energy density described fairly well the fatigue life of the steel, taking the mean stress effects into account. Compared to other fatigue damage parameters, fatigue life prediction by the cyclic strain energy density showed a good correlation with the experimental fatigue lift within a factor of 3.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.2 s.257
• /
• pp.197-204
• /
• 2007

Fretting is a contact damage process that occurs between two contact surfaces. Fretting fatigue reduces fatigue strength of the material due to low amplitude oscillatory sliding and changes in the contact surfaces of strongly connected machine and structure such as bolt, key, pin, fixed rivet and connected shaft, which have relative slip of repeatedly extreme low frequency amplitude. In this research, the fretting fatigue behavior of 2024-T3511 and 7050-T7451 aluminum alloys used mainly in aircraft and automobile industry were experimentally estimated. Based on this experimental wort the following results were obtained: (1) A significant decrease of fatigue lift was observed in the fretting fatigue compared to the plain fatigue. The fatigue limit of 2024-T3511 aluminum alloy decreased about 59% while 7050-T7451 aluminum alloy decreased about 75%. (2) In 7050-T7451 specimen using ATSI4030 contact pad, crack was initiated more early stage than using 2024-T3511 contact pad. (3) In all specimens, oblique cracks were initiated at contact edge. (4) Tire tracks and rubbed scars were observed in the oblique crack region of fracture surface.

• Journal of the Korean Society for Precision Engineering
• /
• v.25 no.8
• /
• pp.96-103
• /
• 2008

In this study, we performed the biomechanical analysis of cervical plate systems by using a computer simulation based on finite element method to derive reliable model by analysis of design variables and fatigue behavior. To simulate the cervical spine movement in-vivo state by surgery, we modeled the cervical plate system which consisted of screws, rings, rivets, and plate and Ultra High Molecular Weight Polyethylene (UHMWPE) Block. The experiment of cervical plate system followed the ASTM F1717 standards that covered the materials and methods for the static and fatigue testing. The result of computer simulation is compared with experimented test. We expected this study is to derive reliable results by analysis of design variables and fatigue behavior for developing a new model.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2006.11a
• /
• pp.89-94
• /
• 2006

In this paper, the effects of the system parameters on the high cycle fatigue life based on structural dynamic analysis of a turbine blade are investigated. Conventional studies have forcused on the fatigue life of turbine blades with specific system parameters. However, each parameter has statistical deviation because of inhomogeneity of material property, tolerance, and operating conditions. Therefore a methodology that estimates the effects of system parameter on the fatigue lift deviation is demonstrated.

• Journal of the Korean Society for Precision Engineering
• /
• v.23 no.6 s.183
• /
• pp.143-150
• /
• 2006

Recently, in proportion to increased demand on environmentally-friendly heat source, efficient management of district heating(DH) system becomes one of important issue. The objectives of this paper are to systematize data processing of transition temperature, investigate the effect of temperature variations on thermal fatigue and find out a way to improve design fractures of Korean DH pipes. For this purpose, reliable fatigue lift evaluation procedures are examined and applied to quantify thermal fatigue lives. Also, as a prototypal optimization analysis results, mean value of original cross sectional area of selected pipes was reduced 18.6% sustaining their sufficient margins against fatigue failure. So, it is anticipated that the output of this research can be used as useful information of optimal design and operation in the future.

• Journal of the Korean Society of Safety
• /
• v.15 no.4
• /
• pp.163-169
• /
• 2000

This paper mainly deals with fatigue lift estimation and prediction in notched structures. The fatigue crack initiation life and the fatigue crack growth behavior in the DEN specimens were predicted using S.I.F. K solution derived in this study and the Paris' crack growth equation. Predicted results showed good agreement with experimental crack growth behaviors under constant-load-amplitude.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.2 s.233
• /
• pp.341-349
• /
• 2005

Damage often occurs on the surface of railway wheel by wheel-rail contact fatigue. It should be removed before reaching wheel failure, because wheel failure can cause derailment with loss of life and property. The increase or decrease of the contact fatigue life by the metal removal of the contact surface were shown by many researchers, but it has not explained precisely why fatigue life increases or decreases. In this study, the effect of metal removal depth on the contact fatigue life for railway wheel has been evaluated by applying finite element analysis. It has been revealed that the residual stress and the plastic flow are the main factors determining the fatigue life. The railway wheel has the initial residual stress formed during the manufacturing process, and the residual stress is changed by thermal stress induced by braking. It has been found that the initial residual stress determines the amount of metal removal depth. Also, the effects of the initial residual stress and metal removal on the contact fatigue lift has been estimated, and an equation is proposed to decide the optimal metal removal depth for maximizing the contact fatigue life.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.8
• /
• pp.1690-1697
• /
• 2002

The effects of re-peening on the fatigue damaged material are studied in this paper. The effects of re-peening process on surface hardness, surface roughness, surface compressive residual stress, and fatigue life are investigated. The results can be summarized in brief as follows: The depth of hardening layer was increased by re-peening process. There is no large variation of the surface roughness by re-peening process. The compressive residual stress of shot-peened specimen decreases under the fatigue loading and then increases again by re-peening process. Re-peening process increases the fatigue lifo of shot-peened and fatigue damaged specimen. The increase of fatigue lift under high stress level is much higher than under low stress level.

• Journal of the Korean Society for Precision Engineering
• /
• v.22 no.12 s.177
• /
• pp.149-155
• /
• 2005

The rotating components such as turbine rotors in service are generally subjected to multiaxial cyclic loading conditions. The prediction of fatigue lift for turbine rotor components under complex multiaxial loading conditions is very important to prevent the fatigue failures in service. In this paper, axial and torsional low cycle fatigue tests were preformed for 3.5NiCrMo steels serviced low pressure turbine rotor of nuclear power plant. Several methods to predict biaxial fatigue life such as Tresca, von Mises and Brown & Miller's critical plane approach were evaluated to correlate the experimental results for serviced NiCrMoV steel. The fracture mode and fatigue characteristics of NiCrMoV steel were discussed based on the results of fatigue tests performed under the axial and torsional test conditions. In particular, the Brown and Miller's critical plane approach was found to best correlate the experimental data with predictions being within a factor of 2.