• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.1
• /
• pp.84-95
• /
• 2001

Titanium is widely used in dentistry for its low density, high strength, fatigue resistance, corrosion resistance, and biocompatibility. But it has a tendency of surface damage under circumstance of friction and impact for its low hardness of the surface. Coating is one of methods fir increasing surface hardness. Its effect is to improve surface physical characteristics without change of titanium. Diamond-like carbon and titanium nitride are known for its high hardness of the surface. So that this study was aimed at the wear test and the cytotoxicity test of the commercially pure titanium and Ti-6Al-4V alloy which were deposited by diamond-like carbon film or titanium nitride film to acertain improvement of the surface hardness and the biocompatibility. A disk (25mm diameter, 2mm thickness) was made of commercially pure titanium and Ti-6Al-4V alloy and these substrates were deposited by diamond-like carbon film or titanium nitride film. Diamond-like carbon film was deposited by the method of radiofrequency plasma assisted chemical vapor deposition and titanium nitride film was deposited by the method of reactive arc ion plating. Then these substrates were tested about wear characteristics by the pin-on-disk type wear tester in which ruby ball was used as a wear causer under the load of 32N, The fracture cycles were measured by rotating the substrates until their films were fractured. The wear volume was measured after 150 cycles and 3,000 cycles using surface profiler. The cytotoxicity test was peformed by the method of the MTT assay. The results were as follows : 1. In the results of the wear volume test, commercially pure titanium and titanium alloy which were coated by diamond-like carbon film or titanium nitride aim had higher resistance against wear than the substrates which were not coated by any films (P<0.05). 2. In the results of the fracture cycle test and the wear volume test, diamond-like carbon film had higher resistance against wear than titanium nitride film (P<0.05). 3. In both coatings of diamond-like carbon aim and titanium nitride film, Ti-6Al-4V alloy had higher resistance against wear than commercially pure titanium (P<0.05) 4. In the results of the cytotoxicity test, diamond-like carbon film and titanium nitride film had little cytotoxicity as like commercially pure titanium or Ti-6Al-4V alloy (P>0.05).

• Korean Journal of Materials Research
• /
• v.12 no.11
• /
• pp.835-839
• /
• 2002

Metal-Ferroelectric-Metal(MFM) capacitors were prepared using $Bi_{3.3}$ $La_{0.7}$ $Ti_3$$O_{12}$ (BLT) ferroelectric thin films which were spin coated on $Pt/Ti/SiO_2$/Si substrates by the Sol-Gel method. BLT thin films annealed at above $650^{\circ}C$ showed polycrystalline structures with typical c-axis preferred orientation. The grain size and surface roughness were increased as the annealing temperature increased from $650^{\circ}C$ to $700^{\circ}C$. In addition, the full width at half maximum (FWHM) values were decreased with increasing annealing temperatures, indicating the improvement of crystallinity. The remanent polarization (2Pr= $Pr^{+}$ $+Pr^{-) }$ and leakage current of the BLT film annealed at $650^{\circ}C$ were about 29.3 $\mu$C/cm$^2$ and $2.3$\times$10^{-8}$$ A/cm^2$ at 3V. There were no distinct changes in the retention charges after $10^{10}$ polarization switching cycles, showing good fatigue property of the annealed BLT films.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.7
• /
• pp.514-520
• /
• 1999

Ferroelectric PZT(30/70)/PZT(70/30) heterolayered thin films were fabricated by spin-coating method on the $Pt/Ti/SiO_2Si$ substrate alternately using(30/70) and PZT(70/30) alkoxide solutions prepared by sol-coating method. The coating and heating procedure was repeated six times to form PZT heterolayered films, and thickness of the film obtained by one-times drying/sintering process was about 40-50 nm. All PZT heterolayered films, showed dense and homogeneous structure without the presence of rosette sturctrue. The relative dielectric constant, remanent polarization and leakage current density of PZT heterolayered films were superior to those of single composition PZT(30/70) and PZT(70/30) films, and those values for the PZT-6 film were 975, $21 \muC/cm^2\; and\; 8\times10^{-9}\; A/cm^2$, respectively. And the PZT-6 heterolayered film showed fairly good fatigue characteristics of remanent polarization and coercive field after application of $10^8$ switching cycles.

• Journal of Korean Academy of Nursing
• /
• v.34 no.7
• /
• pp.1326-1333
• /
• 2004

Purpose: The purpose of this study was to determine the changes on Index of Nausea, Vomiting, & Retching (INVR) during a cycle of chemotherapy, Methods: Forty-three patients hospitalized for chemotherapy at C University Hospital during a period of 5 days from March to May, 2003 were examined, Scores of INVR were measured once a day, Anxiety, anorexia, fatigue, and sleep satisfaction were measured before chemotherapy, Data was analyzed by repeated measures of ANOVA, Results: The score of INVR increased over time during the days of hospitalization and showed a peak on the third day, The score was significantly higher on the third and consecutive cycles than on the first and second cycle, The score was significantly higher in patients in their forties and fifties rather than in their sixties, The score was higher in women than in men, and also increased as the sleep satisfaction decreased, Conclusion: These results suggested that specific interventions for relief of nausea & vomiting were needed in middle age, women, the third chemotherapy cycle, and the third day after chemotherapy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05d
• /
• pp.72-76
• /
• 2003

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode(Pt/$TiO_2/SiO_2$/Si) using RF magnetron sputtering method. The structural and electrical properties of SBT capacitors were influenced with annealing atmosphere. In the XRD pattern, the SBT thin films in all annealed atmosphere had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized in all annealing atmosphere and grains largely grew in oxygen annealing atmosphere. The maximum remanent polarization and the coercive electric field in oxygen annealing atmosphere are $12.40[{\mu}C/cm^2]$ and 30[kV/cm] respectively. The fatigue characteristics of SBT capacitors did not change up to $10^{10}$ switching cycles.

• Electrical & Electronic Materials
• /
• v.11 no.10
• /
• pp.46-52
• /
• 1998

In this study, polarization switching characteristics of Pb(ZrxTil-x)O3 (PZT) thin films were investigated. Switching times(ts) were found to be decreased as the Zr mol% was increased. But, the switching peak currents(Imax) showed the largest value at 50 mol% Zr. As a result of this experiment, ts was found to be depended on the remanent polarization and coercive field and also Imax strongly depended on the dielectric constant of PZT thin films. In order to investigate the partial switching kinetics of PZT thin films, short and relatively small voltage pulses were applied to the MFM(metalferroelectric metal) PZT capacitors and polarization switching curves were measured with a variation of the total width of the applied pulses. Also, the switching curves were measured at different applied voltages(4, 8, 10, 12 and 14 volts). As the applied voltages increased, ts and Imax were found to be decreased and increased, respectively. In case of fatigued specimen which we applied $\pm$10 volts square pulse for 1010 cycles, ts and Imax were found to be shorter and smaller than those of virgin specimens. This is due to the decrease of the remanent polarization and the increase of the coercive field.

• Electrical & Electronic Materials
• /
• v.8 no.3
• /
• pp.261-266
• /
• 1995

In this study, PZT solutions added impurities of Yttrium acetate were prepared by sol-gel processing and were deposited on Pt/ $SiO_{2}$/Si substrates at 5000 rpm for 20 sec. using spin-coating method. Coated films were annealed at 700-750.deg. C for 30 min. using conventional furnace method. Variations of the crystallographic structure and microstructure of PZT thin films with adding impurities were observed using XRD and SEM, and the electrical properties, such as relative permittivity, tan .delta., hysteresis curves and leakage currents, were measured. As the yttrium contents were increased, the remanent polarization and coercive field were decreased. Variations of remanent polarizations and coercive fields of pure and yttrium doped specimens according to polarization reversal cycles were observed using hysteresis measurement. PZT thin films added $Y^{3+}$ ions were completely crystallized at 750.deg. C. $Y^{3+}$ ions, as donor impurity, substituted Pb.sup 2+/ ions located at A-site of perovskite structure. By substitution of $Y^{3+}$ ions, leakage currents became less by decreasing the space charges. Degradation of remanent polarizations of Yttrium added specimens after fatigue was not observed and coercive fields increased more than those of pure PZT thin films.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.1
• /
• pp.24-35
• /
• 1997

The hydraulic or pneumatic valve spools become essential as the important components on the production of automatic hydraulic or pneumatic as mechanical industry has been rapidly developed. The machining precision is in necessity for manufacturing the valve spools. They could be unstable in the quality by the conventional are welding. And also they have a lot of technical problems in manufacturing because their shapes are generally small. By the precision casting process such as lost wax process, the production cost may be increased. But by the friction welding technique, they will be able to be manufactured without such problems. This paper deals with the development of dissimilar friction welding optimization for the hydraulic or pneumatic valve spool by friction welding and a new approach of on real-time qualify evaluation by AE techniques.

• Composites Research
• /
• v.27 no.3
• /
• pp.83-89
• /
• 2014

The purpose of this study is to improve the strength and thermal conductivity of polybutylene terephthalate (PBT) by embedding various additives. Specimens were prepared using PBT pellets embedded with glass fibers (GF) and boron nitride (BN) powders. The test results showed that tensile strength decreased, and thermal conductivity increased with increasing BN contents. with thermal shock cycles conducted, unfilled PBT showed a considerable decrease in failure strain and strength, whereas strength and thermal conductivity of glass fiber and BN particle-embedded PBT had little differeces. With increasing BN, the thermal conductivity of PBT composites was highly improved.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.5
• /
• pp.370-375
• /
• 2001

PZT thin films (3500${\AA}$) ahve been prepared onto Pt/Ti/corning glass (1737) substrates with a RF magnetron sputtering system using Pb$\sub$1.50/(Zr$\sub$0.52/,Ti$\sub$0.48)O$_3$ ceramic target. We used two-step annealing techniques, PZT thin films were grown at a 300$^{\circ}C$ substrate temperature and then subjected to an RTA treatment. In case of 500$^{\circ}C$ RTA temperature show pyrochlore phase. The formation of Perovskite phase started above 600$^{\circ}C$ and PZT thin films generated (101) preferred orientation. As the RTA time and temperature increased, crystallization of PZT films were enhanced. The PZT capacitors fabricated at 650$^{\circ}C$ for 10 minutes RTA treatment showed remanent polarization 30 ${\mu}$C/$\textrm{cm}^2$, saturation polarization 42${\mu}$C/$\textrm{cm}^2$, coercive field 110kV/cm, leakage current density 2.83x10$\^$-7/A/$\textrm{cm}^2$, remanent polarization were decreased by 30% after 10$\^$9/ cycles.