• Applied Chemistry for Engineering
• /
• v.8 no.6
• /
• pp.1022-1028
• /
• 1997

This work was performed to study the characteristics of electrochemical intercalation reactions occurring at the interface between the organic electrolyte and tungsten trioxide thin film (thickness of $4000{\AA}$) prepared by e-beam evaporation method as cathodically coloring oxide with regard to the electrochromism by the intercalating reactions of the lithium cation in the 1M $LiClO_4/PC$ organic solution. The characteristics of electrochemical intercalation reactions were investigated by various DC electrochemical methods such as cathodic Tafel polarization test, multiple and the single sweep cyclic voltammetry and the coulomety titrations method. The surfaces of thin films were observed with the patterns of X ray diffraction after the coloring and bleaching reactions. In comparison with the previous results that $WO_3$ thin film intersely detached from the surface of electrode when the hydrogen cation was intercalated into $WO_3$ thin film in the o.1N $H_2SO_4$ aqueous solution, the intercalation reaction of lithium cation into $WO_3$ thin film in the 1M $LiClO_4/PC$ organic solution was shown that the stable bleaching and coloration was appeared within 1.0V of the applied overpotential. When the overpotential of electrochromic reaction for lithium cation in the 1M $LiClO_4/PC$ organic solution had been applied up to 1.5V, the accumulation phenomenon of lithium in amorphous $WO_3$ thin film layer occurred because the inserted lithium into amorphous $WO_3$ thin layer for coloring process was not fully removed from the thin layer to the electrolyte during bleaching process. It was found that there is a limitation of applied overpotential for coloring process by the reduction of the current densities of bleaching and coloration after few number of coloring and bleaching cycles.

• Journal of the Korean Chemical Society
• /
• v.41 no.11
• /
• pp.594-599
• /
• 1997

Lithium nickel oxide ($Li_{2x}Ni_{1-x}O$) thin films have been prepared by the RF sputtering of lithiated nickel oxide target, where the film microstructure was controlled by the sputtering atmosphere $(Ar/O_2)$ and the substrate temperature ($T_s=50/230^{\circ}C$). From the transmission electron microscopic analysis, it is found that the most porous film with the grain size of $∼80\AA$ could be fabricated under the sputtering atmosphere of $P(O_2)=8{\times}10^2$ mbar with the $$T_s$=50^{\circ}C.$ In the optical and electrochemical studies, the$Li_{2x}Ni_{1-x}O$ films exhibit a significant electrochromic property in association with the lithium insertion/deinsertion process. The amount of charge insertion ($Q_i$) and the optical density (OD) variation depend on the crystallinity of the film as well as its thickness, and for the $Li_{2x}Ni_{1-x}O$ film (170 nm thickness) prepared under $O_2$ atmosphere and $T_s=50^{\circ}C$, the OD could be increased up to ∼1.3 by the charge insertion with $Q_i=30\;mC/cm^2.$

• Applied Chemistry for Engineering
• /
• v.7 no.6
• /
• pp.1078-1086
• /
• 1996

The peroxo-polytungstic acid was formed by the direct reaction of tungsten powder with the hydrogen peroxide solution. Peroxo-polytungstic powder were prepared by rotary evaporator using the fabricated on to ITO coated glass as substrate by dip-coating method using $2g/10mL(W-IPA/H_2O)$ sol solution. A substrate was dipped into the sol solution and after a meniscus had settled, the substrate was withdrawn at a constant rate of the 3mm/sec. Thicker layer could be built up by repeated dipping/post-treatment 15 times cycles. The layers dried at the temperature of $65{\sim}70^{\circ}C$ during the withdrawn process, and then tungsten oxides thin film was formed by final heating treatment at the temperature of $230{\sim}240^{\circ}C$ for 30min. A linear rotation between the thickness of thin film and the number of dipping/post-treatment cycles for tungsten oxides thin films made by dip-coating was found. The thickness of thin film had $60{\AA}$ after one dipping. From the patterns of XRD, the structure of tungsten oxides thin film identified as amorphous one and from the photographs of SEM, the defects and the moderate cracks were observed on the tungsten oxides thin film, but the homogeneous surface of thin films were mostly appeared. The electrochemical characteristic of the $ITO/WO_3$ thin film electrode were confirmed by the cyclic voltammetry and the cathodic Tafel polaization method. The coloring bleaching processes were clearly repeated up to several hundreds cycles by multiple cyclic voltammetry, but the dissolved phenomenon of thin film revealed in $H_2SO_4$ solution was observed due to the decrease of the current densities. The diffusion coefficient was calculated from irreversible Randles-Sevick equation from the data obtained by the cyclic voltammetry with various scan rates.