• Polymer(Korea)
• /
• v.26 no.4
• /
• pp.477-482
• /
• 2002

In order to control the micro-pore structure of glassy carbon (GC), an activation agent of KOH was introduced as the glassy carbon was prepared from phenolic resin with a curing agent of phosphoric acid. The yield and properties of GC were investigated as a function of KOH content. Although the GC produced without KOH had nonporous structure except the trace of bubble formation, the GC with KOH had very porous structure. The surface area of GC with KOH increased continuously up to 870 $m^2$/g with the increase of KOH content. The carbonization yield and apparent density measured in water reduced from 40 to 15% and iron 1.5 to 0.9 g/$cm^3$, respectively, and the electrical resistivity increased from $50{\times}10^{-4}$ to $60{\times}10^{-4}$$\Omega$.cm with the increase of KOH content.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.118-125
• /
• 2011

The size and distribution of concrete void was one among the factor determining durability of concrete. Recently, there was a lot of researches related to the High-Fludity Concrete(HFC) with field applications. However, the research about the void structure having an effect on durability of concrete is insufficient. Therefore, in this research, Conventional Concrete(CC) and HFC using lime stone powder and fly-ash of 30 MPa range was manufactured and observed the void structure of CC and HFC. Experimental results showed that average pore diameter in the case of the 30 MPa range HFC was to be lower than CC and SEM analyzed result, HFC was firmer inner structure than CC.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.05a
• /
• pp.38-38
• /
• 2001

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.130.2-130
• /
• 2003

• Applied Microscopy
• /
• v.46 no.3
• /
• pp.160-163
• /
• 2016

Effect of dealloying condition on the formation of nanoporous structure in melt-spun $Al_{60}Ge_{30}Mn_{10}$ alloy has been investigated in the present study. In as-melt-spun $Al_{60}Ge_{30}Mn_{10}$ alloy spinodal decomposition occurs in the undercooled liquid during cooling, leading to amorphous phase separation. By immersing the as-melt-spun $Al_{60}Ge_{30}Mn_{10}$ alloy in 5 wt% HCl solution, Al-rich amorphous region is leached out, resulting in an interconnected nano-porous $GeO_x$ with an amorphous structure. The dealloying temperature strongly affects the whole dealloying process. At higher dealloying temperature, dissolution kinetics and surface diffusion/agglomeration rate become higher, resulting in the accelerated dealloying kinetics, i.e., larger dealloying depth and coarser pore-ligament structure.

• Membrane Journal
• /
• v.20 no.2
• /
• pp.135-141
• /
• 2010

Various asymmetric Polysulfone membranes were prepared for a MBR process. Ether-typed alcohols (co-solvent) were added into a dope solution in order to control the pore size of membrane, whose effect on water permeability were investigated. Pore size of the prepared membranes were more affected by molecular-structure of co-solvent than by boiling point of theirs. With the increasing order of methoxy ($CH_3$-O-) < secondary propanol ($-CH_2$-CH(OH)$-CH_3$) < ethoxy ($CH_3-CH_2$-O-), water permeability of the prepared membrane increased. The phenomenon might attribute to the difference of molecularly steric hinderance of co-solvent (eg, Methoxy propanol, Ethoxy ethanol, Methoxy ethanol) in dope solution during the phase inversion. By the addition of ether typed alcohol into a dope solution, the pore size of MF (microfiltration) could be controlled. Also, Membrane prepared was applied to a MBR process and the system was stably operated for 2 months.

• Journal of the Korean Ceramic Society
• /
• v.28 no.11
• /
• pp.926-934
• /
• 1991

The effect of aggregates on the forming and sintering behaviors of BaTiO3 was studied. Aggregates and deaggregates of fine crystallite were obtained by thermal decomposition of oxalate coprecipitates and subsequently crushing them with a press, respectively. Large voids formed by packing of aggregates were not easily eliminated despite the successive destruction of aggregates with increasing forming pressure. As a result, compacts of aggregates showed inhomogeneity with larger mid-pore size and broader pore size distribution with respect to those of deaggregates. This inhomogeneity caused differential shrinkage and consequental internal stress, which retarded densification. The differential sintering increased the size of mid-pores in the initial stage, and formed duplex structure composed of dense region with abnormally grown grains and porous region with fine grains. The driving force of this abnormal grain growth shown in the specimens of aggregates was attributed to the minimization of the elastic strain energy due to internal stress.

• Computers and Concrete
• /
• v.4 no.2
• /
• pp.157-166
• /
• 2007

The paper considers a theoretical model to study sulfate ion diffusion in saturated porous media - cement based mineral composites, accounting for simultaneous effects, such as filling micro-capillaries (pores) with ions and chemical products and liquid push out of them. Pore volume change and its effect on the distribution of ion concentration within the specimen are investigated. Relations for the distribution of the capillary relative radius and volume within the composite under consideration are found. The numerical algorithm used is further completed to consider capillary size change and the effects accompanying sulfate ion diffusion. Ion distribution within the cross section and volume of specimens fabricated from mineral composites is numerically studied, accounting for the change of material capillary size and volume. Characteristic cases of 2D and 3D diffusion are analyzed. The results found can be used to both assess the sulfate corrosion in saturated systems and predict changes occurring in the pore structure of the composite as a result of sulfate ion diffusion.

• Journal of Powder Materials
• /
• v.9 no.2
• /
• pp.96-102
• /
• 2002

In the present study, equiatomic porous TiNi shape-memory alloys have been successfully prepared by self-propagating high-temperature synthesis (SHS) using elemental titanium and nickel powders. The porous TiNi alloys thus obtained have an open porous structure with about 64 vol.% porosity, and the pore size is about 1.8 mm. The effect of preheating temperature on the microstructure have been investigated. It is found that the pore size increases with increasing preheating temperature. Moreover, the preheating temperature was shown to have a significant effect on the microstructrue of the SHS-synthesized porous TiNi shape memory alloys.

• Carbon letters
• /
• v.22
• /
• pp.70-80
• /
• 2017

Activated carbons (ACs) have been used as electrode materials of electric double-layer capacitors (EDLC) due to their high specific surface areas (SSA), stability, and ecological advantages. In order to make high-energy-density ACs for EDLC, petroleum pitch (PP) pre-carbonized at $500-1000^{\circ}C$ in $N_2$ gas for 1 h was used as the electrode material of the EDLC after KOH activation. As the pre-carbonization temperature increased, the SSA, pore volume and gravimetric capacitance tended to decrease, but the crystallinity and electrode density tended to increase, showing a maximum volumetric capacitance at a medium carbonization temperature. Therefore, it was possible to control the crystalline structure, SSA, and pore structure of AC by changing the pre-carbonization temperature. Because the electrode density increased with increasing of the pre-carbonization temperature, the highest volumetric capacitance of 28.4 F/cc was obtained from the PP pre-carbonized at $700^{\circ}C$, exhibiting a value over 150% of that of a commercial AC (MSP-20) for EDLC. Electrochemical activation was observed from the electrodes of PP as they were pre-carbonized at high temperatures above $700^{\circ}C$ and then activated by KOH. This process was found to have a significant effect on the specific capacitance and it was demonstrated that the higher charging voltage of EDLC was, the greater the electrochemical activation effect was.