• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1177-1178
• /
• 2006

Magnetic Properties of dust cores made of mixtures of atomized pure iron powder and pure alumina powder has been investigated in the temperature range from 673 to 1073K. The effect of annealing on coercivity has been positive effect up to 973K and thus coercivity is gradually reduced form 280A/m (as-compressed) to 160A/m (973K). However, dust cores annealed at 1073K displayed a 15% increasing of coercivity by annealing at 973K. Hysteresis loss shows a tendency similar to coercivity. Microstructure observation of specimens shows grain refinement by recrystallization in the temperature range from 773 to 1073K.

• 한국자기학회지
• /
• 제15권5호
• /
• pp.270-275
• /
• 2005

가스분무법으로 제조한 $35\~180\;{\mu}m$ 크기의 $Fe-6.0wt\%Si$ 합금분말에 대하여 인산염계 절연물질을 피막처리하고 $600\~900^{\circ}C$에서 1시간 동안 열처리한 후 압축성형한 압분자심(분말코아)의 자기적 성질 및 기계적 특성을 조사하였다. 대체적으로 열처리온도가 증가할수록 압축강도가 감소하였으며, 자심손실 또한 낮아졌다. $800^{\circ}C$에서 열처리한 경우 압축성형강도가 15 kgf, 100 kHz에서 실효투자율은 74, 품질계수는 26, 50 Oe의 직류자장 하에서 퍼센트투자율은 78 정도의 값을 나타내었으며, 50 kHz-0.1 T에서 자심손실은 $750\;mW/cm^3$였다. 그리고 투자율-주파수 곡선 상에서의 cut-off 주파수는 거의 200 kHz 이상에 이르는 것으로 나타났다. $Fe-6.0wt\%Si$ 합금 압분자심의 이러한 제반 특성은 인산염 피막의 양호한 전기절연효과와, 고규소농도에 따른 합금의 결정자기이방성 및 포화자기변형의 감소, 전기비저항의 증대 등 기초 물성의 변화에 기인하는 것으로 사료되었다.

• 한국자기학회지
• /
• 제12권6호
• /
• pp.218-223
• /
• 2002

가슨 분무법으로 제조한 High-Flux형 $Ni_{x}Fe_{100-x}$(x=40~50, wt.%) 퍼멀로이 분말 및 압분 코아의 자기적 특성을 조사하였다. 포화자화는 45%Ni조성에서 최대 값을 보이며 이보다 보 함량이 낮아지면 인바 효과의 작용에 의해 급격하게 감소하였다. 압분 코아의 투자율은 Ni 농도가 낮아지면 현저히 증가하는 바 이는 자기변형의 감소에 기인하는 것으로 사료되었으며, 자심손실은 Ni=45%에서 가장 낮은 값을 나타내었다. Ni농도가 50%에서 45%로 낮아짐에 따라 자심손실이 감소하는 주원인은 전기 비저항의 증대에 따른 와전류 손실의 감소에 있는 것으로 생각되었다. Ni=45% 분말 합금으로 만든 압분 코아는 Ni=50%의 경우보다 더 우수한 투자율의 주파수 의존성, 큰 Q 값, 그리고 더 나은 직류 바이어스 특성을 나타내어 상용 High-Flux 코아(50%Ni-50%Fe)에 비해 더 좋은 압분 자심 재료가 될 수 있음을 확인하였다.