• 한국항공우주학회지
• /
• 제31권7호
• /
• pp.112-117
• /
• 2003

본 연구에서는 재생 냉각용 연소기에 적용되고 있는 동합금과 2상 스테인리스강의 최적 브레이징 조건을 구하였다. 모재는 C18200 동합금과 S31803 2상 스테인레스강을, 삽입금속으로 두께가 각각 50${\mu}m$, 80${\mu}m$인 AMS4764를 사용하였다. 브레이징한 시제에 대하여 X선 검사, 강도/기밀 및 파괴시험, 파단면 관찰을 한 결과 두께 50${\mu}m$인 삽입금속을 사용한 경우 강도특성과 접합면이 양호함을 확인하였다. 반면 두께 80${\mu}m$인 삽입금속을 사용한 경우는 강도특성은 양호하였으나 냉각유로의 막힘 현상과 유로 확대를 확인하였다.

• 한국표면공학회지
• /
• 제51권3호
• /
• pp.172-178
• /
• 2018

In this paper, effects of potassium permanganate, pottasium dichromate, sodium molybdate on lean duplex stainless steel were studied by GDOES, OCP, potentiodynamic curves. The stainless steels were chemically passivated in each nitric acid solutions containing 4wt.% oxidants for 1 hour. As a result, when potassium dichromate or sodium molybdate was added, content of Fe was decreased and content of Cr was increased. Consequently, corrosion resistance of passive film was increased. But in case of potassium permanganate was added, contrastively, content of Fe was increased and content of Cr was decreased. So corrosion resistance was decreased. Adding sodium molybdate in nitric acid for chemical surface treatment process was the most effective among oxidants and also it showed the most stable anti-corrosion in SST.

• Journal of Welding and Joining
• /
• 제31권5호
• /
• pp.20-25
• /
• 2013

This study was carried out to investigate the influence of a sigma phase precipitation on the pitting corrosion resistance and microstructural change of super duplex stainless steels(UNS S32750). The welds made by FCAW (Flux Cored Arc Welding) were heat treated ($930^{\circ}C$, $1080^{\circ}C$, $1230^{\circ}C$) and quenched. Based on the microstructural examination, it was found that the ${\sigma}$ phase was formed in base metals and welds heat treated at $930^{\circ}C$ while there were little ${\sigma}$phases formed in base metals and weld metal experienced the relatively fast cooling from $1080^{\circ}C$ and $1230^{\circ}C$. On the other hand, the most weight loss due to pitting corrosion occurred in base and weld metals heat treated at $930^{\circ}C$. It was confirmed that the pitting corrosion occurred in the phase boundaries of ferrite/sigma and austenite/sigma. The pitting corrosion resistance decreased owing to an increase in Cr, Mo depleted areas adjacent to the intermetallic phases such as ${\sigma}$phases. The hardness was greatly increased due to the precipitation ${\sigma}$phases.

• 한국표면공학회지
• /
• 제27권3호
• /
• pp.123-133
• /
• 1994

Oxidation behavior of STS 304 and 430, produced by POSCO, Korea, was studied in order to study the surface defects formed during manufacturing processes. Oxidation experiments were carried out in a preheat-ed furnace at 850~$1, 250^{\circ}C$ in air and in a simulated coke oven gas(COG) atmosphere. The reaction products were examined by XRD, SEM and EDX on their surfaces and cross sections. Protective $Cr_2O_3$-primary oxide film was formed initially, but at critical point this film was broken and a duplex scale consisting of $Fe_2O_3$- and Fe$Cr_2O_4$- was formed. It was more severely attacked in a simulated COG atmosphere than in air, and STS 304 was superior to STS 430 in oxidation resistance.

• Nuclear Engineering and Technology
• /
• 제47권6호
• /
• pp.712-718
• /
• 2015

Cast duplex stainless steels are susceptible to thermal aging during long-term service at temperatures ranging from $280^{\circ}C$ to $450^{\circ}C$. To analyze the effect of thermal aging on leak-before-break (LBB) behavior, three-dimensional finite element analysis models were built for circumferentially cracked pipes. Based on the elasticeplastic fracture mechanics theory, the detectable leakage crack length calculation and J-integral stability assessment diagram approach were carried out under different bending moments. The LBB curves and LBB assessment diagrams for unaged and thermally aged pipes were constructed. The results show that the detectable leakage crack length for thermally aged pipes increases with increasing bending moments, whereas the critical crack length decreases. The ligament instability line and critical crack length line for thermally aged pipes move downward and to the left, respectively, and unsafe LBB assessment results will be produced if thermal aging is not considered. If the applied bending moment is increased, the degree of safety decreases in the LBB assessment.