• 한국산업융합학회 논문집
• /
• 제2권2호
• /
• pp.61-68
• /
• 1999

The variety of crystalline structure and mechanical properties of PP filament treated with dry heat treatment at different draw ratio has been studied. Crystalline structure and mechanical properties of annealed PP filament at different draw ratio has been examined by XRD, UTM, and density method. Heat treatment has been carried out $100^{\circ}C$, $120^{\circ}C$ $140^{\circ}C$ for 30min. in dry oven. From the results of this study, it found the following facts. It was found that the crystallinity and crystallite size of (110) plane of sample were increased with increasing of annealed temperature and draw ratio. The crystalline form of annealed sample which was undrawn showed ${\alpha}$, ${\beta}$ mixing form below $120^{\circ}C$ and showed ${\alpha}$ form at $140^{\circ}C$. But the crystalline form of annealed sample which was drawn showed ${\alpha}$ form at $120^{\circ}C$. Initial modulus and tensile strength were increased with increasing of annealing temperature, and the degree of orientation was decreased with decreasing of annealing temperature.

• 한국염색가공학회지
• /
• 제9권4호
• /
• pp.7-19
• /
• 1997

The purpose of the study was to investigate the shrinkage and creep behavior of PET filaments which were prepared at various spinning speeds(3,300, 4,000, 5,000, 6,000, and 7,000m/min) and anneal($120^{\circ}$, 30min & $150^{\circ}$, 40min). In order to determine the shrinkage and creep behavior with the crystallinity change, PET filaments were treated with low(12$0^{\circ}C$, 30min) and high($150^{\circ}$, 40min) temperature conditions with hot air dryer under the constant tension. The results of the study were as follows: as the spinning speed increased, the degree of shrinkage and elongation of the sample treated by wet condition decreased. The sample with 0.01g/d of load under various spinning speeds showed shrinkage behavior and highest shrinkage ratio at $76^{\circ}$ which was Tg of PET. The degree of shrinkage and elongation of the treated sample was less than those of the untreated sample by wet treatment. Especially, there was less degree of shrinkage and elongation of the sample treated by higher temperature condition. In 3,300m/min of spinning speed the draw ratio of undrawn yarn of a mixture of a-axis orientation and c-axis orientation was 2.0, which is similar to the value of the traditional drawn yarn. Finally, there was a big range of shrinkage and elongation by wet treatment in 3,300 m/min of spinning speed.