• Textile Coloration and Finishing
• /
• v.23 no.4
• /
• pp.304-311
• /
• 2011

For sound absorption and sound insulation in automobile industry, the sound absorption materials based on meltblown nonwovens were prepared by SMS (spunbond-meltblown-spunbond) technique. And the sound absorption coefficient (${\alpha}$) of the meltblown nonwoven, produced with isotatic-polypropylene(PP), was examined for the various processing conditions such as die-to-collector distance(DCD), nonwoven weight(GSM), and air suction conditions. The meltblown nonwoven for sound absorption materials was composed of bulky microfiber web, increasing with increases in weight and DCD. The sound absorption coefficient(${\alpha}$) was excellent as a sound absorption materials of PAD type composed of SMS(spunbond-meltblownspunbond) nonwovens.

• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.267-273
• /
• 2006

We have prepared PP/Ba-ferrite composite fabrics by a melt-blown spinning method and investigated the relationship between the properties of PP/Ba-ferrite composite fabrics and melt-blown processing factors. A PP composite containing Ba-ferrite as a magnetic particulate filler was prepared in the form of pellet from PP resin and Ba-ferrite powder by melt compounding using a single extruder. Screw turning force (rpm), DCD (die-to-collector distance), and Ba-ferrite content were changed. We measured diameters of fiber, mechanical, thermal, and magnetic properties for the composited PP fabrics. The elongation was increased and a fiber diameter and tensile strength were decreased as the spinning distance increased or screw turning force decreased. The crystallinity was increased with increasing spinning distance according to XRD. It was assumed that the orientation of crystalline domain in the neat PP without ferrite was increased by drawing in mechanical direction, however, the orientation in the PP composite was decreased according to XRD analysis. We measured a magnetic property of PP nonwoven fabric containing Ba-ferrite powder. A coercive force, maximum magnetization, and residual magnetization are reduced with the spinning distance. According to the result of TGA measurement, the heat resistance was increased with the Ba-ferrite powder content and with decreasing the spinning distance.

• Proceedings of the KAIS Fall Conference
• /
• 2001.05a
• /
• pp.84-86
• /
• 2001

본 논문에서는 고성능 활성탄의 악취 및 유해가스 흡착효율과 멜트브로운(M/B)부직포의 여과성능에 의한 복합적인 고기능 방진특성을 갖는 활성탄 부착 M/B 국산화 여과재를 제조개발하였다. 고성능 활성탄은 고순도의 일반활성탄에 금속염, 유기물 등을 담지시켜 활성화시킨 활성탄이고, M/B여과재의 웹(web)제조조건은 M/B 방사기에서 방사온도 250℃, 방사속도 150m/sec, 고온공기온도 250℃ 그리고 DCD(die to collector distance) 20cm가 적합함을 알 수 있었다. 또한 M/B 여과재에 활성탄 부착은 열롤러시스템에 의한 열적결합방법을 이용하여 균일한 분포의 점접착결합구조를 갖도록 하였고, 개발된 복합기능 여과재가 방진마스크용 여과재로의 이용이 가능하다는 것을 분진포집효율, 투과율, 흡기저항 등 여과재 성능기준실험 결과를 통해 확인하였다.