• Restorative Dentistry and Endodontics
• /
• v.9 no.1
• /
• pp.101-106
• /
• 1983

It was the purpose of this study to investigate the fracture mode of dental amalgam by observing the crack propagation, and to relate this to the microstructure of the amalgam. Caulk 20th Century Regular, Caulk Spherical, Dispersalloy, and Tytin amalgam alloys were used for this study. After each amalgam alloy and Hg measured exactly by the balance was triturated by the mechanical amalgamator (Capmaster, S.S. White), the triturated mass was inserted into the cylindrical metal mold which was 4 mm in diameter and 12 mm in height and was pressed by the Instron Universal Testing Machine at the speed of 1mm/min with 120Kg. The specimen removed from the mold was stored in the room temperature for a week. This specimen was polished with the emery papers from #100 to #200 and finally on the polishing cloth with 0.06${\mu}Al_2O_3$ powder suspended in water. The specimen was placed on the Instron testing machine in the method similar to the diametral tensile test and loaded at the crosshead speed of 0.05mm/min. The load was stopped short of fracture. The cracks on the polished surface of specimen was examined with scanning electron microscope (JSM-35) and analyzed by EPMA (Electron probe microanalyzer). The following results were obtained. 1. In low copper lathe-cut amalgam, the crack went through the voids and ${\gamma}_2$ phase, through the ${\gamma}_1$ phase around the ${\gamma}$ particles. 2. In low copper spherical amalgam, it was observed that the crack passed through the ${\gamma}_2$ and ${\gamma}_1$ phase, and through the boundary between the ${\gamma}_1$ and ${\gamma}$ phase. 3. In high copper dispersant (Dispersalloy) amalgam, the crack was found to propagate at the interface between the ${\gamma}_1$ matrix and reaction ring around the dispersant (Ag-Cu) particles, and to pass through the Ag-Sn particles. 4. In high copper single composition (Tytin) amalgam, the crack went through the ${\gamma}_1$ matrix between ${\eta}$ crystals, and through the unreacted alloy particle (core).

• The Journal of the Korea Contents Association
• /
• v.10 no.11
• /
• pp.228-234
• /
• 2010

Ni-Cr and Co-Cr alloy uncontained Be element for using as dental porcelain alloy were analyzed the mechanical properties through bonding strength and fracture test after the bonding with porcelain. The bonding strengths between alloy and ceramic were measured through the shear bond strength test. Consequently, the T-3 group contained Be element that had shear strength of 41.13(${\pm}5.11$)MPa was showed the highest shear strength than the other groups. The second highest group was a verabond contained Be element that had shear strength of 40.72(${\pm}5.98$)MPa. The results of the other groups according to the shear strength were Wirobond(38.40(${\pm}9.66$)MPa) belonged to Co-Cr alloy, and Verabond 2V(32.77(${\pm}4.31$)MPa), Bellabond N(28.63(${\pm}6.39$)MPa), Bellabond plus(24.97(${\pm}6.13$)MPa), Argeloy N.P. Star(22.69(${\pm}3.41$)MPa) uncontained Be element, respectively. The morphological aspects of the fracture surface between alloys and ceramic were observed that all groups were caused mixed failure as conformation attached ceramic fragments to metallic surface by fracture process.

• Restorative Dentistry and Endodontics
• /
• v.8 no.1
• /
• pp.89-96
• /
• 1982

The purpose of this study is to identify the phases of four different types, low-copper lathe cut (Type II, class 1) and spherical (Type II, class 2) amalgam alloys which are made by Caulk company and high copper Dispersalloy (Type II, class 3) made by Johnson & Johnson and Tytin (Type I, class 2) made by S.S. White and to determine the Vickers hardness number on the individual phase and four different types of dental amalgam. After each amalgam alloy and Hg measured exactly by the balance was triturated by the mechanical amalgamator (De Trey), the triturated mass was inserted into the cylindrical metal mold which was 4 mm in diameter and 12mm in height and was pressed by the Instron Universal Testing machine (Model 1125) at the speed of 1mm/minute with 143$kg/cm^2$ according to the A.D.A. Specification No. 1. The Specimen removed from the mold, mounted and stored in the room temperature for 7 days. The speciman was polished with the emery paper from #220 to #1200 and finally on the polishing cloth with 0.3 and 0.05 um $Al_2O_3$ powder suspended in water. And then each specimen was etched by Allan's method and washed with Sodium Bisulfinite for 30 seconds. Finally differentiation and metallography on each phase were obtained by using metallographical microscope (Versamet, Union) and microhardness was obtained by using microhardness tester (MVH-2, Torsee). The results were as follows: 1. In the low-copper amalgam, the ${\gamma}$, ${\gamma}_1$ and ${\gamma}_2$ phase were observed and in the high-copper amalgam, the ${\gamma}$, ${\gamma}_1$. ${\epsilon}$ and ${\eta}$ phases were observed but ${\gamma}_2$ phase was not observed. 2. Among the microhardness of each amalgam phase measured under pressing a vickers diamond indenter with 2.0gm load for 30 seconds, e phase has the highest V.H.N (314 ${\pm}$ 20), and in low-copper amalgam 12 phase has the lowest V.H.N. (29${\pm}$1) and ${\eta}$ phase which was observed in high-copper amalgam has 230${\pm}$13 V.H.N and this phase is considerd to contribute to strengthen the handness in amalgam. 3. The V.H.N. measured under pressing a Vickers diamond indenter with 300.0gm load for 30 seconds in low-copper amalgam was lower than that of high-copper amalgam.

• The Journal of Korean Academy of Prosthodontics
• /
• v.28 no.2
• /
• pp.53-76
• /
• 1990

The purpose of this study was to evaluate the tensile bond strength of adhesive resins to successively recast Rexillium III and Degudent-U. Recasting was done 4times successively. Specimen $A_1$, were cast by new metal, and $A_2$ by surpus of $A_1$, $A_3$ by surplus of, $A_2$ $A_4$ by surplus of $A_3$, $A_5$ by surplus of $A_4$ plus 50% new metal. The types of surface treatment for resinbonded restoration in this experiment were electrolytic etching by OXY-ETCH(Oxy dental products, Inc., Hillside, New Jersey, U.S,A.), aluminum oxide blasting, anodic oxidation by EZ-OXISOR( Towagiken Co., Kyoto, Japan), electrotinplating by Kura Ace(Kuralay Co., Kyoto, Japan). Three kinds of cementing resin used in this study were Comspan(K.P. Cauil Co, Milford Delaware, U.S.A.), Super Bond C&B(Sun-Medical Co. Ltd., Kyoto,Japan), Panavia EX(Kuralay Co., Ltd., Osaka, Japan). Tensile bond strength was measured by Instron Universal testing machineModel 1125) and all the specimen were observed with SEM(JEOL, JSM-T2000) and mode of bond failure were recorded. The obtained results were as follows : 1. In electrolytic etched group, tensile bond strength was decreassed when recast alloy was used, and tensile bond strength of Compan and panavia EX were not significantly different(P>0.05). 2. In remaining group treated by aluminum oxide blasting, EZ-OXIOR, Kura Ace, tensile bond strength were not changed when recast alloy were used, and tensile bond strength of SuperBond(C&B and Panavia EX were not significantly different(P>0.05). 3. IN SEM evaluation, electrolytic etched group and electrotinplated group exhibited different image when recast alloy was used, and remaining groups treated by aluminum oxide blasting, EZ-OXISOR exhibited the same. 4. IN observation of bond failure, electrolytic etched group exhibited adhesive failure and remaing groups treated by aluminium oxid blasting, EZ-OXISOR, Kura Ace exhibited adhesive and cohesive failure.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.2
• /
• pp.169-181
• /
• 2007

Statement of problem: Titanium is well known as a proper metal for the dental restorations, because it has an excellent biocompatibility, resistance to corrosion, and mechanical property. However, adhesion between titanium and dental porcelains is related to the diffusion of oxygen to the reaction layers formed on cast-titanium surfaces during porcelain firing and those oxidized layers make the adhesion difficult to be formed. Many studies using mechanical, chemical and physical methods to enhance the titanium-ceramic adhesion have been actively performed. Purpose: This study meant to comparatively analyse the adhesion characteristics depending on different titanium surface coatings after coating the casts and wrought titanium surfaces with Au and TiN. Material and method: In this study, the titanium specimens (CP-Ti, Grade 2, Kobe still Co. Japan) were categorized into cast and wrought titanium. The wrought titanium was cast by using the MgO-based investment(Selevest CB, Selec). The cast and wrought titanium were treated with Au coating($ParaOne^{(R)}$., Gold Ion Sputter, Model PS-1200) and TiN coating(ATEC system, Korea) and the ultra low fusing dental porcelain was fused and fired onto the samples. Biaxial flection test was done on the fired samples and the porcelain was separated. The adhesion characteristics of porcelain and titanium after firing and the specimen surfaces before and after the porcelain fracture test were observed with SEM. The atomic percent of Si on all sample surfaces was comparatively analysed by EDS. In addition, the constituents of specimen surface layers after the porcelain fracture and the formed compound were evaluated by X-ray diffraction diagnosis. Result: The results of this study were obtained as follows : 1. The surface characteristics of cast and wrought titanium after surface treatment(Au, TiN, $Al_2O_3$ sandblasting) were similar and each cast and wrought titanium showed similar bonding characteristics. 2. Before and after the biaxial flection test, the highest atomic weight change of Si component was found in $Al_2O_3$ sandblasted wrought titanium(28.6at.% $\rightarrow$ 8.3at.%). On the other hand, the least change was seen in Au-Pd-In alloy(24.5at.% $\rightarrow$ 9.1at.%). 3. Much amount of Si components was uniformly distributed in Au and TiN coated titanium, but less amount of Si's was unevenly dispersed on Al2O3 sandblasting surfaces. 4. In X-ray diffraction diagnosis after porcelain debonding, we could see $Au_2Ti$ compound and TiN coating layers on Au and TiN coated surfaces and $TiO_2$, typical oxide of titanium, on all titanium surfaces. 5. Debonding of porcelain on cast and wrought titanium surface after the biaxial flection is considered as a result of adhesion deterioration between coating layers and titanium surfaces. We found that there are both adhesive failure and cohesive failure at the same time. Conclusion: These results showed that the titanium-ceramic adhesion could be improved by coating cast and wrought titanium surfaces with Au and TiN when making porcelain fused to metal crowns. In order to use porcelain fused to titanium clinically, it is considered that coating technique to enhance the bonding strength between coating kKlayers and titanium surfaces should be developed first.

• Journal of Periodontal and Implant Science
• /
• v.29 no.1
• /
• pp.209-231
• /
• 1999

Even though titanium(Ti) and its alloys are the most used dental implant materials, there are some problems that Ti wears easily and interferes normal osteogenesis due to the metal ions. Ti coated with bioactive ceramics such as hydroxyapatite has also such problems as the exfoliation or resorption of the coated layer, Recent studies on implant materials have been proceeding to improve physical properties of the implant substrate and biocompatibility of the implant surfaces. The purpose of the present study was to examine the physical property and bone tissue compatibility of bioinert nitrides ion plated Ti, Button type specimens(14mm in diameter, 2.32rrun in height) for the abrasion test and cytotoxicity test and thread type implants(3.75mm in diameter, 6mm in length) for the animal experiments were made from Ti(grade 2) and 316LVM stainless steel. Ti specimens were ion plated with TiN, ZrN by the low temperature arc vapor deposition, and the depth profile of the TiN/Ti, ZrN/Ti ion plated surface was examined by Auger Electron Spectroscopy. Three kind of button type specimens .of TiN/Ti, ZrN/Ti and Ti were used for abrasion test, and HEPAlClC7 cells and CCD cells were cultivated for 4 days with the specimens for cytotoxicity test. Thread type implants of TiN/Ti, ZrN/Ti, Ti, 316LVM were implanted on the femur of 6 adult dogs weighing 10kg-13kg. Two dogs were sacrified for histological examination after 45 days and 90 days, and four dogs were sacrified for the removal torque test of the implant') after 90 days. The removal torque force was measured by Autograph (Shimadzu Co., AGS-1000D series, Japan). Abrasion resistance of TiN/Ti was the highest, and that of ZrN/Ti and Ti were followed. The bioinert nitride ion plated Ti had much better abrasion resistance, compared with Ti, In the cytotoxicity test, the number of both cells were increased in all specimens, and there were no significant difference in cytotoxic reaction among all groups (p>0.1), In histological examination, 316LVM showed the soft tissue engagement in interface between the implant and bone, but the other materials after 45 days noted immature new bone formation in the medullary portion along the implant surface, and those after 90 days showed implant support by new bone formation in both the cortical and the medullary portion, The removal torque force of Tilv/Ti showed significantly higher than that of Ti(p(O,05). The difference in removal torque force between TiN/Ti and ZrN/Ti was not significant(p>0.05), and that of 316LVM was lowest among all groups(p<0.05). These results suggest that bioinert nitrides ion plated Ti can resolve the existing problems of Ti and bioactive ceramics, and it may be clinically applicable to human.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.4
• /
• pp.562-572
• /
• 2005

Statement of problem : Titanium is widely used as an implant material lot artificial teeth. Also, studies on surface treatment to form a fine passive film on the surface of commercial titanium or its alloys and improving bioactivity with bone have been carried out. However, there is insufficient data about the biocompatibility of the implant materials in the body. Purpose: The purpose of this study was to examine whether the precipitation of apatite on titanium metal is affected by surface modification. Materials and methods: Specimens chemically washed for 2 minute in a 1:1:1.5 (in vol%) mixture of 48% HF 60% $HNO_3$ and distilled water. Specimens were then chemically treated with a solution containing 97% $H_2SO_4$ and 30% $H_2O_2$ at $40^{\circ}C$S for 1 hour, and subsequently heat-treated at $400^{\circ}C$ for 1 hour. All specimens were immersed in the HBSS with pH 7.4 at $36.5^{\circ}C$ for 15 days, and the surface were examined with TF-XRD, SEM, EDX and XPS. Also, commercial purity Ti specimens with and without surface treatment were implanted in the abdominal connective tissue of mice for 4 weeks. Conventional aluminium and stainless steel 316L were also implanted for comparison. Results and conclusions : The results obtained were summarized as follows. 1. An amorphous titania gel layer was formed on the titanium surface after the titanium specimen was treated with a $H_2SO_4$ and $H_2O_2$ solution. The average roughness was $2.175{\mu}m$ after chemical surface treatment. 2. The amorphous titania was subsequently transformed into anatase by heat treatment at $400^{\circ}C$ for 1 hour. 3. The average thickness of the fibrous capsule surrounding the specimens implanted in the connective tissue was $46.98{\mu}m$ in chemically-treated Ti, and 52.20, 168.65 and $100.95{\mu}m$ respectively in commercial pure Ti, aluminum and stainless steel 316L without any treatment.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.77-77
• /
• 2017

Titanium and its alloys offer attractive properties in a variety of applications. These are widely used for the field of biomedical implants because of its good biocompatibility and high corrosion resistance. Titanium anodizing is often used in the metal finishing of products, especially those can be used in the medical devices with dense oxide surface. Based on SAE/AMS (Society of Automotive Engineers/Aerospace Material Specification) 2488D, it has the specification for industrial titanium anodizing that have three different types of titanium anodization as following: Type I is used as a coating for elevated temperature forming; Type II is used as an anti-galling coating without additional lubrication or as a pre-treatment for improving adherence of film lubricants; Type III is used as a treatment to produce a spectrum of surface colours on titanium. In this study, we have focused on Type II anodization for the medical (dental and orthopedic) application, the anodized surface was modified with gray color under alkaline electrolyte. The surface characteristics were analyzed with Focused Ion Beam (FIB), Scanning Electron Microscopy (SEM), surface roughness, Vickers hardness, three point bending test, biocompatibility, and corrosion (potentiodynamic) test. The Ti-6Al-4V alloy was used for specimen, the anodizing procedure was conducted in alkaline solution (NaOH based, pH>13). Applied voltage was range between 20 V to 40 V until the ampere to be zero. As results, the surface characteristics of anodic oxide layer were analyzed with SEM, the dissecting layer was fabricated with FIB method prior to analyze surface. The surface roughness was measured by arithmetic mean deviation of the roughness profile (Ra). The Vickers hardness was obtained with Vickers hardness tester, indentation was repeated for 5 times on each sample, and the three point bending property was verified by yield load values. In order to determine the corrosion resistance for the corrosion rate, the potentiodynamic test was performed for each specimen. The biological safety assessment was analyzed by cytotoxic and pyrogen test. Through FIB feature of anodic surfaces, the thickness of oxide layer was 1.1 um. The surface roughness, Vickers hardness, bending yield, and corrosion resistance of the anodized specimen were shown higher value than those of non-treated specimen. Also we could verify that there was no significant issues from cytotoxicity and pyrogen test.

• The Journal of Korean Academy of Prosthodontics
• /
• v.58 no.1
• /
• pp.14-22
• /
• 2020

Purpose: The aim of this study is to evaluate the effectiveness of MnO₂-diatom microbubbler (DM) on the surface of prosthetic materials as a mouthwash by comparing the biofilm removal effect with those previously used as a mouthwash in dental clinic. Materials and methods: DM was fabricated by doping manganese dioxide nanosheets to the diatom cylinder surface. Scanning electron microscopy (SEM) was used to observe the morphology of DM and to analyze the composition of doped MnO₂. Stereomicroscope was used to observe the reaction of DM in 3% hydrogen peroxide. Non-precious metal alloys, zirconia and resin specimens were prepared to evaluate the effect of biofilm removal on the surface of prosthetic materials. And then Streptococcus mutans and Porphyromonas gingivalis biofilms were formed on the specimens. When 3% hydrogen peroxide solution and DM were treated on the biofilms, the decontamination effect was compared with chlorhexidine gluconate and 3% hydrogen peroxide solution by crystal violet staining. Results: Manganese dioxide was found on the surface of the diatom cylinder, and it was found to produce bubble of oxygen gas when added to 3% hydrogen peroxide. For all materials used in the experiments, biofilms of the DM-treated groups got effectively removed compared to the groups used with chlorhexidine gluconate or 3% hydrogen peroxide alone. Conclusion: MnO₂-diatom microbubbler can remove bacterial membranes on the surface of prosthetic materials more effectively than conventional mouthwashes.