• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.139-142
• /
• 2009

In this study, the performance degradation of SOFC single cell caused by the delamination between a cathode and an electrolyte is investigated. As the delamination rate increases, the voltage sharply decreases due to the decrease of reaction sites and losses increase. The current is concentrated to the intact area so that the current density is increased and the ohmic loss and the activation loss become higher. Most part of loss is due to the ohmc loss of electrolyte.

• Proceeding of EDISON Challenge
• /
• 2016.03a
• /
• pp.167-174
• /
• 2016

Recently laminated plates like composite materials has been used in a various field to grow the specific strength of the composition. However, delamination area caused by barely visible impact damage has potential risk that it can raise buckling of the delaminated plate. Because it can interrupt compressive behavior of laminated plates and reduce their strength, the whole structure can't be constituted by these materials. Many studies assume that behavior of the delaminated plate which is in lamanated plates equals theoretical buckling but their actual motion doesn't coincide because of initial imperfections of materials like deflection, residual stress, eccentricity and so on. In this paper, we change laminated plates with initial delamination into a beam of rectangular cross section with the initial crack and analyze compressive behavior according to initial imperfections through finite element method(FEM). Consequently analysis results show that behavior of laminated plates involving delamination differs from ideal buckling of the delaminated plate in actual conditions and we can predict its motion through imperfections relationship.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.9
• /
• pp.12-20
• /
• 2022

Delamination and burr defects are important problems in drilling fiber reinforced plastics. A method for measuring FRP drilling defects has been studied. Delamination and burr factors were defined as the relative length or area. Using these factors, the effects of tool shape and drilling conditions on delamination and burr were studied. In this study, the defects that occur when drilling a glass-carbon fiber hybrid composite were compared in terms of three factors. In the glass-carbon fiber hybrid composite, the effects of the feed rate and tool point angle on the delamination and burr factors were similar to those in previous studies. The diameter of the tool did not affect the defect factor. A circular burr was generated in a drill tool with a point angle of 184°, and a relatively small deburring factor was observed compared with a tool with a point angle of 140°.

• Structural Engineering and Mechanics
• /
• v.81 no.1
• /
• pp.39-50
• /
• 2022

Layer separation (delamination) is an essential threat to fiber-reinforced polymer (FRP) plates under dynamic, static, and fatigue loads. Under compressive load, the growth of delamination will lead to structural instability. The aim of this paper is to present a method using shape memory alloy (SMA) stitches to suppress the delamination growth in a FRP plate and to improve the buckling behavior of the plate with a rectangular hole. The present paper is divided into two parts. Firstly, a closed-form (CF) formulation for evaluating the buckling load of the FRP plate is presented. Secondly, the finite element method (FEM) will be employed to calculate the buckling loads of the plates which serves to validate the results obtained from the closed-form method. The novelty of this work is the development of the closed-form solution using the p-Ritz energy approach regarding the stress-dependent phase transformation of SMA to trace the equilibrium path. For the FEM, the Lagoudas constitutive model of the SMA material is implemented in FORTRAN programming language using a user material subroutines (VUMAT). The model is simulated in ABAQUS/Explicit solver due to the nature of the loading type. The cohesive zone model (CZM) is applied to simulate the delamination growth.

• Composites Research
• /
• v.25 no.6
• /
• pp.236-240
• /
• 2012

The purpose of this study was to investigate the feasibility on the detection of dental composite delamination using a lock-in thermography method. Amplitude and phase images of detected thermal signals were analyzed according to the lock-in frequencies. At a lock-in frequency of 0.05 Hz, the ligament thickness of 0.5 mm in the specimen exhibited the highest amplitude contrast between defective area and sound area. For ligament thicknesses of 1 mm and 1.5 mm, delamination detection was possible at 0.025 Hz and 0.01 Hz through the amplitude differences. At lock-in frequencies of 0.006 Hz and 0.01 Hz, ligament thickness 0.5 mm exhibited the highest phase contrast. For ligament thicknesses of 1 mm and 1.5 mm, the phase contrast exhibited possible detection of delamination at 0.006-0.1 Hz.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.74-77
• /
• 2001

The impact response and damage of CLAS panel was investigated experimentally. The facesheet material used was RO4003 woven-glass hydrocarbon/ceramic and the core material was Nomex honeycomb with a cell size of 3.2mm and a density of 96 kg/$\textrm{m}^{3}$. The shield plane used was RO4003 and 2024-T3 aluminum. Static indentation and impact test was conducted to characterize the type and extent of the damage observed in two CLAS panels, and the performance of antenna used in a wireless LAN system. Correlation of peak contact force, residual indentation and the delamination area shows impact damage of the panel with an aluminum shield plane is larger than that of the panel with RO4003 shield plane, although tile former is more penetration resistant. The damage was observed by naked eye, ultrasonic inspection and cross sectioning. The shape and size of delamination was estimated by ultrasonic inspection, and the area of delamination linearly increases as impact energy increases. The performance of impact damaged antenna was estimated by measuring return loss and radiation pattern.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.6
• /
• pp.48-56
• /
• 2001

In this paper, this study aims at the evaluation on the characteristics of CFRP laminate plates using a falling weight impact tester. The experiment was conducted on several laminates of different orientation. A system was built far measur- ing the impact strength of CFRP laminates in consideration of stress wave propagation theory using a falling weight impact tester. Delamination areas of impacted specimens for the different ply orientation were measured with ultrasonic C- scanner to find correlation between impact energy and delamination area. Absorbed energy of quasi-isotropic specimen having flour interfaces was higher than that of orthotropic laminates with two interfaces. The more interfaces, the greater the energy absorbed. The absorbed energy oft hybrid specimen containing a GFRP layer was higher than that of normal specimens.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.6
• /
• pp.109-115
• /
• 2001

This paper investigates the mechanical characteristics of angle-ply laminates with non-woven carbon tissue. The lami- nates were made by inserting non-woven carbon tissue at the interface. Specimens were rounded near the tabs by grinding and polishing to reduce the stress concentration. Cyclic loads were applied to the specimens and the stress and fatigue life curves were obtained. The matrix crack density was also evaluated to check the effects of non-woven carbon tissue on the fracture resistance of composite laminates. C-Sean technique was used to evaluate the delamination, and SEM was used to understand the fracture mechanisms of the laminates. Experimental results show that the fatigue strength and life of composite laminates were increased by inserting non- woven carbon tissues. The results also show that the matrix crack density and delamination area were reduced by inserting non-woven carbon tissues.

• Steel and Composite Structures
• /
• v.17 no.2
• /
• pp.159-172
• /
• 2014

A finite element model with the consideration of damage initiation and evolution has been developed for the analysis of the dynamic response of a composite sandwich panel subject to low velocity impact. Typical damage modes including fiber breakage, matrix crushing and cracking, delamination and core crushing are considered in this model. Strain-based Hashin failure criteria with stiffness degradation mechanism are used in predicting the initiation and evolution of intra-laminar damage modes by self-developed VUMAT subroutine. Zero-thickness cohesive elements are adopted along the interface regions between the facesheets and the foam core to simulate the initiation and propagation of delamination. A crushable foam core model with volumetric hardening rule is used to simulate the mechanical behavior of foam core material at the plastic state. The time history curves of contact force and the core collapse area are obtained. They all show a good correlation with the experimental data.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.2 no.6
• /
• pp.66-75
• /
• 1994

In this paper, the effects of temperature change on the impact damages of CF/PEEK laminates are experimentally investigated. Composite laminates used in this experiment are CF/PEEK orthotropic laminated plates, which have two-interfaces$[0^{\circ}_4/90^{\circ}_4]_{9+} A steel ball launched by the air gun collides against CFRP laminates to generate impact damage. The delamination damages are oberved by a scanning acoustic microscope. And various relations are experimentally observed including the impact energy vs. delamination area, the specimen temperature vs. transverse crack, and the impact energy vs. residual bending strength of carbon fiber peek composite laminates subjected to FOD(Foreign Object Damage) under high temperatures.