• Journal of the Korean Wood Science and Technology
• /
• v.34 no.3
• /
• pp.22-29
• /
• 2006

The overlaid panels are important materials in interior and construction with added surface layers (PVC films, decorative paper, decorative veneer). Generally, the adhesive for decorative veneer to wood-based panel is urea-formaldehyde (UF) adhesive which cause the emission of formaldehyde during not only the manufacturing process, but also service life. In this study, environment-friendly SIS-based hotmelt pressure-sensitive adhesive (PSA) was evaluated as a adhesive for bonding a decorative veneer. The various SIS-based hotmelt PSA was blended as a function of diblock content, softening point of tackifier, tackifier content, and applied to bonding the decorative veneer.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.22-28
• /
• 1997

This research was carried out to obtain the fundamental data for the development of the technology and practical use of far-infrared radiation(IR) drying of quarter-sliced decorative veneers of walnut and red oak. The average drying rates of IR drying were about one and half to four times those of kiln drying and this tendency was prominent in thin veneer. The end wavinesses of the IR-dried veneers were smaller than those of kiln-dried veneers. These were largely recovered by the cold treatments after drying. The consumed electric power for IR drying was about one-fifth to two-fifthes compared to that for kiln drying.

• Journal of the Korea Furniture Society
• /
• v.11 no.1
• /
• pp.61-68
• /
• 2000

This study was carried out to investigate the effect of grain and veneer thickness on drying rate, required energy consumption, and drying defects such as checking, end waving, and burning during a far-infrared radiation drying process of decorative veneers of hard maple and beech. Most of the veneer could be dried from green to in-use moisture content within 30 to 360 seconds. The drying rates were significantly affected by veneer thickness, but there was little difference between edge-and flat-sliced veneers. The formation of checking during drying test was none or very slight. The percentages of the veneers defected by checks were higher in the flat-sliced veneers than in the edge-sliced veneers. The maximum end wavinesses in the flat-sliced veneers were almost 1.6 to 3 times larger than that in the edge-sliced veneers. All veneers were fee from burned marks during drying test.

• Journal of the Korea Furniture Society
• /
• v.10 no.2
• /
• pp.29-36
• /
• 1999

During a radio-frequency/vacuum plus press drying process of some hardwood veneers for decoration we investigated the effect of a grain and thickness of a veneer sheet on drying rates, variations of final moisture content within a bundle of veneer sheets, and formation of checking, end waving, and burning mark. About thirty three hundreds sheet of veneer could be dried in sixty five hours from green to in0-use moisture content, and a final moisture content was significantly effected by initial moisture content of veneer. There were nearly variations in a final moisture content among the veneer sheets in the same bundle. A checking was never found in a edge-sliced veneer, and very slight in a flat-sliced veneer of ash and red oak. There were no end waving and no burning mark in all veneer sheets.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.2
• /
• pp.39-45
• /
• 2008

Formaldehyde and volatile organic compounds (VOCs) are emitted from wood-based panels that have been made using wood particles, wood fiber, wood chips, formaldehyde-based resins and so on. In this study, we examined formaldehyde and total VOCs (TVOC) emission behaviors for plywood overlaid with water-soluble phenolic resin impregnated linerboard (PL), and two kinds of surface materials (decorative veneer and pre-impregnated finishing foil) that were adhered onto the PL that named DPL and PPL. EVA (ethyl vinyl acetate) was used to overlay the decorative veneer and pre-impregnated finishing foil on the plywood with water-soluble phenolic resin impregnated linerboard by a hot press instrument. The debonding test and accelerated aging test were conducted to assess their mechanical properties. Formaldehyde and TVOC emission concentrations were measured using the FLEC method and a VOC Analyzer, respectively. The debonding test results of PL, DPL and PPL were 1.2, 1.5, and $0.5N/mm^2$, respectively. The surface appearance of the samples were not changed after the accelerated aging test. The PL and DPL exhibited reduced formaldehyde and TVOC emission levels, respectively. In the case of PPL, the VOC value was relatively higher than those of PL and DPL.