• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.9
• /
• pp.199-206
• /
• 2019

Experimental study on the durability characteristics to examine the feasibility of concrete with high water-tightness and self-healing performance to minimize maintenance of concrete for artificial ground is as follows. 1) When blending agent, swelling agents, and curing accelerator were added on the ternary system cement with blast-furnace slag fine particles and fly ash to give a self-healing property, higher blending strengths by 82% at design standard strength of 24MPa and by 74% at design strength of 30MPa, respectively could be obtained. 2) The permeability test for the specimens having high water-tightness and no shrinkage showed that the permeability was reduced at maximum of 98%. However, the permeability was decreased as the design strength was increased, showing the reduction rate of 87% at the design strength of 50MPa. 3) The depth of carbonation of blast-furnace slag and fly ash was increased in all the specimens compared with those of OPC only. However, as the material age was increased, carbonation penetration depth was decreased compared with the reference blend. 4) Compared with the reference blending using only OPC, the freeze-thaw resistance was higher in the case of blending with 40% of blast-furnace slag and 10% of fly ash at the design standard strength of 50MPa. In addition, the freeze-thaw resistance in general was superior in the design standard strength of 50MPa with the lower water-binder ratio (W/B) as compared with the design standard strength of 24MPa and 30MPa with the high water-binder ratios.

• Journal of the Korea Concrete Institute
• /
• v.23 no.5
• /
• pp.609-615
• /
• 2011

MgO concrete containing lightly burnt MgO powder at $850{\sim}1,000^{\circ}C$ may have a long-term expansibility characteristic. Such expansibility of MgO concrete can compensate the shrinkage at later ages since the hydration of the MgO is very slow. However, the addition of MgO delays the initial hydration of cement and increases the setting time of cement. Also, the porosity and pore-size distribution of the MgO concrete are different from OPC concrete. Therefore, in order to use MgO in practice, both mechanical and durability properties of MgO concrete should be carefully examined. In this study, durability tests on carbonation, freezing-thawing, and diffusion of chloride were carried out after 56 days of underwater curing at $20^{\circ}C$ to compare durability characteristics of 5% MgO-mixed concrete with those of OPC concrete. The results showed that MgO concrete shows a greater durability than the concrete with no MgO, because the micro structure in the MgO concrete is much denser due to its expansibility characteristic.

• Journal of the Korea Concrete Institute
• /
• v.26 no.4
• /
• pp.499-506
• /
• 2014

A number of studies on eco-friendly and healthy building materials are being conducted as modern people are becoming more conscious about health and the environment they live in. Among those materials, studies on Hwangtoh are the most prevalent but due to its strength, crack coming from drying shrinkage, and susceptibility to water, the usage of Hwangtoh is incomplete and limited to be used as a common building material. Cement concrete, considered as one of the most widely used building materials, is extensively used in construction because it is economical, easily accessible and moldable and has proper compressive strength. Due to carbon dioxide created in the process of making cement concrete, it is recognized as pollution. Accordingly, there are a lot of studies on reduction of carbon dioxide in cement concrete industry. There are increasing numbers of researches as well as developments on Hwangtoh or traditional construction materials used in South Korea to reduce the environmental problems. Therefore, this study suggests the basic features of the construction material that can replace cement concrete in the future with the non-sindtered cement mixed with non-sintering hwangtoh which is made with the furnace slag and multiple stimulants.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.59-67
• /
• 2017

The objective of this paper is to investigate experimentally the effect of replacement of recycled coarse aggregates with 5~13mm in size on a field applicability of concretes through Mock-up test. Seven different mock-up specimens were prepared with the size of $1200{\times}800{\times}800mm$ simulating column and wall. For the concrete mixtures, 24MPa, 27MPa and 40MPa of nominal strength were adopted with 30% and 70%(only for 24MPa) of 5~13mm recycled coarse aggregate (RCA) replacement and without 5~13mm RCA(Plain). For test items, slump, slump flow, compressive strength with different curing conditions, core drilling, rebound numbers and drying shrinkage were measured. Test results indicated that 30% of 5~13 mm RCA replacement resulted in increase in slump, slump flow and resistance against segregation, while air contents decreased compared to those of plain mixture. Compressive strength of concrete with 30% of 5~13mm RCA was shown to be higher than that of plain mixture due to optimum packing effect associated with presence of well graded aggregates. Rebound number of the mock-up specimen with 30% of 5~13mm RCA had lower fluctuation according to hitting location than that of plain mock-up specimen. It is believed from the results of the study that replacement of 30% of 5~13mm RCA brings desirable improvement in various aspect of concrete performance due to associated dense packing effect.

• Journal of the Korean Society for Precision Engineering
• /
• v.28 no.7
• /
• pp.777-782
• /
• 2011

Micro features on the surface are well-known to have significant effects on optical or mechanical properties such as the optical interference, reflectance at the surface, contact angle, interfacial friction, etc. These surface micro features are increasingly employed to enhance the functionality of the applications in various application areas such as optical components for LCD or solar panel. Diverse surface features have been proposed and some of them are showing excellent efficiency or functionality, especially in optical applications. Most applications employing the micro features need manufacturing process for mass production and the injection molding and roll-to-roll forming, which are typical processes for mass production adopting polymeric materials, may be also preferred for micro patterned plastic product. Since the functionality or efficiency of the surface structures generally depends on the shape and the size of the structure itself or the array of the structures on the surface, it would be very important to replicate the features very precisely as being designed during the molding the micro pattern applications. In this paper, a series of research activities is introduced for roll-to-roll forming of micro patterned film including filling of patterns with UV curable resin, demolding of surface structures from the roll tool, control of surface energy and cure shrinkage of resin and dispose time and intensity of the UV light for curing of UV curable resin.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.83-90
• /
• 2017

Concrete structure for nuclear power plant is mass concrete structure with large wall depth and easily permits cracking in early age due to hydration heat and drying shrinkage. It always needs cooling water so that usually located near to sea shore. The crack on concrete surface permits rapid chloride intrusion and also causes more rapid corrosion in the steel. In the study, the effect of age and crack width on chloride diffusion is evaluated for the concrete for nuclear power plant with 6000 psi strength. For the work, various crack widths with 0.0~1.4 mm are induced and accelerated diffusion test is performed for concrete with 56 days, 180days, and 365 days. With increasing crack width over 1.0mm, diffusion coefficient is enlarged to 2.7~3.1 times and significant reduction of diffusion is evaluated due to age effect. Furthermore, apparent diffusion coefficient and surface chloride content are evaluated for the concrete with various crack width exposed to atmospheric zone with salt spraying at the age of 180 days. The results are also analyzed with those from accelerated diffusion test.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.538-544
• /
• 2006

Two kinds of novel bifunctional methacrylated prepolymers (170-2MA and 631-2MA) which have similar structure with 2,2-bis[4- (2'-hynroxy-3'-methacryloyloxypropoxy)phenyl] propane (Bis-GMA) was synthesized for dental applications as an alternative to Bis-GMA containing bisphenol A that is doubtful as an endocrine disrupter. The organic matrices were prepared by mixing a diluent and/or a monomer with the synthesized methacrylated prepolymers. The yield, viscosity, and chemical structures of the prepolymers and the physical and methanical properties of the organic matrices were evaluated. The yields of the prepolymers synthesized through a ring-opening reaction of epoxy compound and methacrylic acid were above 90% and the viscosities of the prepolymers were much lower than that of the Bis-GMA control. From the results of $^1H-NMR$ and FTIR analyses, the chemical structures of the prepolymers were similar to that of Bis-GMA. In addition, the curing time, poly-merization shrinkage, photoconversion, polymerization depth, and compressive strength of the organic matrices formulated with 170-2MA and 631-2MA prepolymers exhibited comparable to or better than those of the existing Bis-GMA-based one. These results suggest that the novel methacrylated prepolymers which have no endocrine disrupter can be an alternative to Bis-GMA and be applicable to dental polymer materials.

• Composites Research
• /
• v.32 no.1
• /
• pp.21-28
• /
• 2019

Recently, according to environmental regulations, the automobile industry has been conducting various research on the use of composite materials to increase fuel efficiency. However, there has not been much research on lightweight chassis components. Therefore, in this research, the purpose of this study is to apply composite materials to the sub-frame of chassis components to achieve equivalent levels of stiffness, strength, NVH performance and 50% lightweight compared to the steel sub-frame. First, the Natural frequency of steel and composite specimens was compared to the damping characteristics of composite materials. Then, in this study, the Lay-up Sequence was derived to maximize the stiffness and strength of the sub-frame by applying composite materials. And this lay-up Sequence is proposed to avoid heat shrinkage due to curing during manufacturing. This process was designed based on a FEM structural analysis, and a Natural frequency and frequency response function graph was confirmed based on a modal analysis. The prototype type composite sub-frame was manufactured based on the design and the F.E.M analysis was verified through a modal experiment. Furthermore, it was fitted to the actual vehicle to verify the natural frequency and the indoor noise vibration response, including idling and road noise. This result was confirmed to be equivalent to the steel sub-frame. Finally, the composite sub-frame weight was confirmed to be about 50% of the steel sub-frame.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.3
• /
• pp.330-337
• /
• 2021

3D printing is not only at the fundamental study and small-scale level, but has recently been producing buildings that can be inhabited by people. Buildings require a lot of cost and labor to work on the form work, but if 3D printing is applied to the building, the construction industry is received attention from technologies using 3D printing as it can reduce the construction period and cost. 3D printing technology for buildings can be divided into structural and non-structural materials, of which 3D printing is applied to non-structural materials. Because 3D printing needs to be additive manufacturing, control such as curing speed and workability is needed. Since cement mortar has a large shrinkage due to evaporation of water, cement polymer dispersion is used to improve the hardening speed, workability, and adhesion strength. The addition of polymer dispersion to cement mortar improves the tensile strength and brittleness between the cement hydrate and the polymer film. Cement mortar using polymer materials can be additive manufacturing but it has limited height that can be additive manufacturing due to its high density. When light-weight materials are mixed with polymer cement mortar, the density of polymer cement mortar is lowered and the height of additive manufacturing, so it is essential to use light-weight materials. However, the use of EVA redispersible polymer powder and light-weight materials, additional damage such as cracks in cement mortar can occur at high temperatures such as fires. This study produced a test specimen incorporating light-weight materials and EVA redispersible polymer powder to produce exterior building materials using 3D printing, and examined flame resistance performance through water absorption rate, length change rate, and cone calorimeter test and non-flammable test. From the test result, the test specimen using silica sand and light-weight aggregate showed good flame resistance performance, and if the EVA redispersible polymer powder is applied below 5%, it shows good flame resistance performance.

• Journal of Wetlands Research
• /
• v.26 no.2
• /
• pp.139-146
• /
• 2024

Various injection materials, such as asphalt-based injection materials, urethane-based injection materials, cement- based injection materials, and acrylic-based injection materials, are used for the repair of aged conduits and underground structures with cracks. In this study, research was conducted on an environmentally friendly acrylic- based leak repair material that exhibits good curing properties even in humid conditions and stability in temperature fluctuations. To compare the performance of the improved acrylic leak repair material with the existing acrylate injection material, experiments were conducted using KS standard methods, including underwater length change rate tests, underwater leakage resistance tests, and chemical performance tests. The comparative experiments revealed that the improved acrylic leak repair material showed no changes in shrinkage due to humidity, temperature variations, or chemical reactions compared to the existing acrylate injection material. In the underwater resistance test, the improved acrylic leak repair material did not show any leakage. Additionally, to assess the environmental impact of the improved acrylic leak repair material, acute fish toxicity tests and acute oral toxicity tests were conducted, and the results showed no mortality and no specific concerns with the test specimens. The experimental results led to the conclusion that the improved acrylic leak repair material is considered to be superior in performance, environmentally safe, and harmless to the human body. Based on various experimental results, it is inferred that the improved acrylic leak repair material is suitable for use as a repair material for cracks in manholes and underground structures compared to the existing acrylate repair material. This study aims to propose valuable data for future technological development by evaluating the applicability of acrylic leak repair materials.