• 한국건축시공학회지
• /
• 제7권1호
• /
• pp.107-113
• /
• 2007

This study investigates the filed application in Daebul Free Trade Zone applying both a flowing method using drying shrinkage-reducing superplasticizer(SRS) and an insulating curing method using double layer bubble sheet. Test results showed that fresh concrete satisfied target slump and air content. A structure adding SRS significantly decreased the total bleeding capacity and accelerated the setting time. As for the crack occurrence, the structure applying the flowing method and double bubble sheets simultaneously exhibited the most favorable crack endurance, while conventional concrete showed more than 1mm size of crack in overall. In addition, a structure applying the flowing concrete method partially presented the micro crack. For the area proportion of crack occurrence, the structure using the double bubble sheets indicated 9.8%, while others applying flowing concrete method was 28%, compared with that of conventional one. For the compressive strength of specimens, standard curing specimens indicated $3{\sim}33%$ higher value than that of specimens cured besides the field construction. The specimens containing SRS improved the strength of $2{\sim}6MPa$, which is $10{\sim}22%$ higher than that of conventional concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2006년도 추계 학술논문 발표대회 논문집
• /
• pp.13-16
• /
• 2006

This study investigates filed application in Daebul Free Trade Zone of a flowing method using drying shrinkage-reducing superplasticizer(SRS) and an insulating curing method using double bubble sheets. Test showed that fresh concrete satisfied target slump and air content. A structure adding SRS significantly decreased the total bleeding capacity and accelerated the setting time. As for the crack occurrence, the structure applying the flowing method and double bubble sheets simultaneously exhibited the most favorable crack endurance, while conventional concrete showed more than 1mm size of crack in overall, and a structure applying only the flowing method partially presented micro crack. For the area proportion of crack occurrence, the structure using the double bubble sheets indicated 9.8%, while others applying flowing method was 28%, compared with 100% of conventional one. Standard curing specimens had about $3{\sim}6%$ higher compressive strength than that of specimens cured at adjacent field construction. In addition, using SRS improved about $5{\sim}7MPa$, than that of conventional concrete at 91 days elapse.

• Geomechanics and Engineering
• /
• 제2권4호
• /
• pp.321-335
• /
• 2010

This article describes a laboratory research on stabilizing tropical peat using ordinary Portland cement (OPC) as a binding agent, and polypropylene and steel fibres as chemically inert additives. California bearing ratio (CBR) and unconfined compressive strength (UCS) tests were carried out to evaluate the increase in the strength of the stabilized samples compacted at their optimum moisture contents and air cured for up to 90 days. The results show that the UCS values of stabilized peat samples increased by as high as 748.8% by using OPC (5%), polypropylene fibres (0.15%), and steel fibres (2%). The CBR values of the samples stabilized with OPC (5%), polypropylene fibres (0.15%), and steel fibres (4%) showed an increase of as high as 122.7%. The stabilized samples showed a shrinkage in volume upon air curing and this shrinkage was measured by an index called, volume shrinkage index (VSI). The highest VSI recorded was 36.19% for peat without any additives; and the minimum was 0% for the sample containing 30% OPC, 0.15% polypropylene fibres and 2% steel fibres. The technique of stabilizing peat with OPC, polypropylene and fibres, coupled with air curing, appears to be cost-effective compared with other frequently used techniques.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.501-504
• /
• 2004

This paper proposes degree of hydration based shrinkage prediction model of 40MPa HPC. This model shows degree of hydration which is defined as the ratio between the hydrated cement mass and the initial mass of cement is very closely related to shrinkage deformation. In this study, degree of hydration was determined by CEMHYD-3D program of NIST. Verification of the predicted degree of hydration is performed by comparison between test results of compressive strength and estimated one by CEMHYD-3D. Proposed model is determined by statistical nonlinear analysis using the program Origin of Origin Lab. Co. To get coefficients of the model, drying shrinkage tests of four specimen series were followed with basic material tests. Testes were performed in constant temperature /humidity chamber, with difference moisture curing ages to know initial curing time effect. Verification with another specimen, collected construction field of FCM bridge, was given in the same condition as pre-tested specimens. Finally, all test results were compared to propose degree of hydration based model and other code models; AASHTO, ACI, CEB-FIP, JSCE, etc.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2006년 창립20주년기념 정기학술대회 및 국제워크샵
• /
• pp.233-236
• /
• 2006

A dilatometer was used to investigate the effect of cure conditions and the presence of filler in an epoxy system. These studies showed shrinkage in the cured epoxy when heating it through the glass transition temperature region. The magnitude of the shrinkage, related to stress build up in the epoxy during curing, was influenced by the processing conditions, filler presence and the nature of the mold used to contain the resin. Cure and cyclic cure at a lower temperature, prior to a post cure, decreased the magnitude of observed shrinkage. Cure shrinkage decreased with number of cyclic cure. Post cured samples outside the mold led to less shrinkage compared with sample in the mold. And sample containing kaolin filler showed less shrinkage than unfilled sample.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.125-126
• /
• 2021

In order to improve the housing culture, construction changes for the utilization of diverse and multifunctional spaces are appearing in response to the increasing diverse needs of consumers. Cellular Light-weight Concrete (CLC) is being developed for use in fire-resistant heat-insulating walls and non-bearing walls. However, manufacturing non-uniformity has become a problem as a drawback due to the use of foamed bubbles and normal temperature curing, and additional research is required. Therefore, in order to suppress cracks due to drying shrinkage, silica sand is mixed with CLC to try to understand its characteristics. In the experiment, the compressive strength from 7 to 28 days of age was measured via a constant temperature and humidity chamber, and the drying shrinkage was analyzed according to each condition using a strain gauge. The compressive strength of matrix tends to decrease as the substitution rate of silica sand increases. This is judged by the result derived from the fact that the specific surface area of silica sand is smaller than that of slag. Based on KS F 2701 (ALC block), the compressive strength of 0.6 products is 4.9 MPa or more as a guide, so the maximum replacement rate of silica sand that satisfies this can be seen at 60%. Looking at the change in drying shrinkage for just 7 days, the shrinkage due to temperature change and drying is 0.7 mm, and the possibility of cracking due to shrinkage can be seen, and it seems that continuous improvement and supplementation are needed in the future.

• 대한건축학회논문집:구조계
• /
• 제34권5호
• /
• pp.27-34
• /
• 2018

Concrete placed under hot weather condition suffers from larger slump loss, rapid moisture evaporation due to high air temperature. Proper measures for material, transportation and curing should be taken to prevent the quality deterioration of the concrete under hot weather condition. In Korea, Although the period of hot weather concrete in Korea occupies only 2 months, there are a lot of quality problems including plastic, drying shrinkage and cold joint. Therefore, the objective of this paper is to investigate and compare the temperature history and crack occurrence of the concrete, which was placed in the actual apartment house construction field under hot weather condition, in response to the application of surface covered curing blankets including PE film, single layer clear bubble sheet, white colored bubble sheet and aluminum metalized bubble sheet. Test results indicated that the application of white colored bubble sheet and aluminum metalized bubble sheet showed most favorable results in terms of reduction in temperature rise and crack occurrence as well as easiness in handling. But, due to light reflection by aluminum metalized bubble sheet, it is believed that white colored bubble sheet is preferable.

• 폴리머
• /
• 제35권4호
• /
• pp.320-324
• /
• 2011

폴리카프로락톤디올을 디이소시아네이트와 반응하여 우레탄 아크릴레이트를 합성하였고 부틸 아크릴레이트 혹은 부착증진제를 배합하여 그 물성을 조사하였다. 이소포론 디이소시아네이트를 사용한 자외선 경화형 수지에 부틸 아크릴레이트를 일정성분비로 첨가하여 경화 시 수축현상 개선의 정도를 조사해 본 결과 부틸 아크릴레이트의 함량이 15 wt%일 때가 가장 좋은 물성을 발현하였다. 자외선 경화형 수지의 부착력을 증진시키기 위해 2-에틸 헥실 아크릴레이트와 에틸 아크릴레이트를 $85^{\circ}C$에서 4시간동안 합성하여 부착증진제를 얻었으며 이를 자외선 경화형 수지에 일정성분비로 첨가하여 물성을 확인해 보았다. 부착증진제의 함량이 높아질수록 부착력이 증가하였지만 15 wt% 이후로는 연성의 성질이 지나치게 강하여 오히려 부착력이 감소함을 확인할 수 있었다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제18권2호
• /
• pp.99-107
• /
• 2014

본 연구에서는 순환골재 콘크리트의 성능에 대한 양생방법의 영향에 대하여 실험적으로 고찰하였다. 순환골재 콘크리트 제조를 위하여 부순골재에 순환골재를 0, 25, 50, 75 및 100%로 대체하였으며, 증기양생한 콘크리트의 압축 및 쪼갬인장강도, 투수공극, 염소이온 침투저항성 및 건조수축을 소정의 재령에서 측정하여 수중양생한 콘크리트의 성능과 비교하였다. 실험결과에 따르면, 양생방법에 관계없이 순환 골재 대체율이 증가할수록 콘크리트의 역학적 성능은 감소하였다. 한편, 초기재령에서 증기양생된 콘크리트는 수중양생된 콘크리트와 비교하여 매우 우수한 성능을 나타내었다. 그러나, 장기재령 (28일)에서 증기양생의 효과는 초기재령에 비하여 두드러지게 나타나지 않음을 알 수 있다. 결론적으로, 본 연구의 범위 내에서 순환골재 콘크리트의 성능향상을 위하여 증기양생법의 적용이 유용할 것으로 판단된다.

• 대한치과보철학회:학술대회논문집
• /
• 대한치과보철학회 1999년도 Asian Academy of Prosthodntics. Korean Academy of Prosthodontics
• /
• pp.91.1-91.1
• /
• 1999