• Elastomers and Composites
• /
• v.46 no.2
• /
• pp.144-151
• /
• 2011

Intermittent CSR testing was used to investigate the degradation of a hydrogenated NBR(HNBR) O-rings, and also the prediction of its life-time. The cure system of HNBR O-ring was controlled as sulfur cure and peroxide cure system. An intermittent CSR jig was designed taking into consideration the O-ring's environment under use. The testing allowed observation of the effects of friction, heat loss, and stress relaxation by the Mullins effect. Degradation of O-rings by thermal aging was observed between 100 and $120^{\circ}C$. In the temperature range of $100-120^{\circ}C$, O-rings showed linear degradation behavior and satisfied the Arrhenius relationship. The activation energy of HNBR-S was about 70.6 kJ/mol. From Arrhenius plots, predicted life-times of HNBR-S O-ring were 31.1 years and 33.7 years for 50% and 40% failure conditions, respectively. In case of HNBR-P, the activation energy was about 72.1kJ/mol, and predicted life-times were 34.0 years and 36.5 years for 50% and 40% failure conditions, respectively. The peroxide cure system showed slower degradation rate and higher activation energy than the sulfur cure system.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.403-409
• /
• 2009

In the 1840s, Goodyear found out sulfur cure system, but cure time was too slow. So producing of rubber product takes a long time. In 1904, Oenslager et al. found that aniline is accelerated sulfur cure system. Recently, many rubber industries needed high yield and good quality. So, many researchers have studied a rubber system with fast vulcanization time and good mechanical properties. In this study, cure characteristics and mechanical properties of NR/BR compounds by accelerator with MBTS(2,2' Dithiobisbenzothiazole), TMTM(Tetramethylthiuram Monosulfide), ZDMC (Zinc dimethyldithiocarbamate), CBS(N-Cyclohexyl benzothiazolyl-2-sulfenamide), DPG(Diphenylguanidine) were evaluated. The results of the study indicate that cure charateristics($t_{90}$: 235 sec, $T_{max}$: 5.77 Nm) and mechanical properties (100, 300% modulus : 2,180, 5.656 Mpa and tear strength: 59.58 kgf/cm) of NR/BR compounds shows efficient acceleration with MBTS 1.5 phr, TMTM 0.5 phr, DPG 0.15phr. This is due to the synergistic activity of ternary accelerator system in rubber vulcanization.

• Macromolecular Research
• /
• v.10 no.1
• /
• pp.34-39
• /
• 2002

Cure behavior of an epoxy resin was investigated at different cure temperatures (110, 120, 130, 140, and 150 $^{\circ}C$) and cure times in the presence of 2 wt% of an N-benzylpyrazinium hexafluoroantimonate (BPH) cationic catalyst by means of differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). The glass transition temperature ( $T_{g}$) and chemical conversion (x) at the different temperatures were determined from DSC thermograms. The $T_{g}$ and x vs. In time data were superposed up to $T_{g}$ = 10$0^{\circ}C$ and x = 0.70 by shifting horizontally at a reference temperature of $T_{g}$ = 13$0^{\circ}C$. It is interesting that the $T_{g}$ and x of the superposed data increase rather slowly in the early stage of cure and rapidly thereafter. Therefore, the increase of the $T_{g}$ and x can be divided into two regions; $R_{I}$= -18.4(= $T_{go}$ ) ~5$^{\circ}C$ and $R_{II}$ = 5 ~ 10$0^{\circ}C$ in $T_{g}$, and $R_{I}$ : 0~0.24 and $R_{II}$ : 0.24~0.70 in x. The $R_{I}$ is closely related to the initiation reactions between BPH and epoxy and between hydroxy group and epoxy in this epoxy/catalyst system. From the kinetic analysis of the $T_{g}$-shift, activation energy was 12.5 kcal/mol. The relationship between $T_{g}$ and x was also considered. The gelation and vitrification times for different cure temperatures were obtained from DMA curves.urves. DMA curves.urves.

• Macromolecular Research
• /
• v.12 no.3
• /
• pp.282-289
• /
• 2004

We have extensively characterized the fluorescence behavior of unsaturated polyester (UP) resin in the absence and presence of a 1,3-bis-(l-pyrenyl)propane (BPP) fluorescent probe at various dynamic and isothermal cure histories by means of a steady-state fluorescence technique using a front-face illumination equipment. In addition, we explored the effect of the fluorescence intensity on the relaxation of the fluorescent probe in the UP resin by resting the dynamically and isothermally cured resin at ambient temperature and pressure for 24 h. The monomer fluorescence intensity, which has two characteristic peaks at 376 and 396nm, changed noticeably depending on the cure temperature and time and provided important information with respect to the molecular and photophysical responses upon curing. The result of the fluorescence study indicates that the increased local viscosity and restricted molecular mobility of the UP resin surrounding the BPP probe after curing are both responsible for the enhancement of the monomer fluorescence intensity. Our results also demonstrate that once the BPP probe has enough time to rearrange and become isolated prior to fluorescence, a sufficient amount of fluorescence is emitted. Therefore, we note that the fluorescence behavior of this UP resin system is influenced strongly by the relaxation process of the fluorescent probe in the resin as well as process used to cure the resin.

• Restorative Dentistry and Endodontics
• /
• v.20 no.1
• /
• pp.33-54
• /
• 1995

The degree of conversion of composite resin was known to have influence on the mechanical properties of composite materials such as hardness, strength, wear resisitance, dimensional and color stability. Also unreacted monomer was reported to be harmful to the pulp. So the degree of conversion was a very important factor in the success of composite resin restorations. In recent, the dual cure resin cement was developed with the advocations that it could increase the curing rates in the sites where the curing ligt could not reach. Moreover many manufactors added some adhesive components in the resin cement. This study was undertaken to observe the effects of curing depth and light curing times on the degree of conversion of dual cure resin cements. CR INLAY CEMENT, DUAL CEMENT and OPTEC BOND, by the Fourier transform Infrared analysis, changing the curing depth 1mm, 2mm and 3mm, and varying the light curing time 20 seconds, 40 seconds and 80 seconds at each depth. The cytotoxicity of dual cure resin cements was tested by the in vitro MTT method using L929 cell. The results was evaluated and compared statistically. The results were obtained as follows : 1. The dual cure resin cements reavealed various degree of conversion, CR INLAY CEMENT and DUAL CEMENT had a tendency to be more reactive to the light cure and OPTEC BOND was a more chemical one. 2. CR INLAY CEMENT and DUAL CEMENT showed the lowest degree of conversion in 2 mm depth, and in 3mm depth the degree of conversion increased, which were due to the chemical cure of dual cures, but OPTEC BOND showed decreasing degree of conversion with increasing curing dept h and all experimental groups showed lower degree of conversion than CHEMICAL group which cured in dark room with no light, so the weak light-curing of dual cure resin cement prevented the chemical cure. (P<0.05) 3. CR INLAY CEMENT and DUAL CEMENT showed increasing degree of conversion in 1 mm and 3 mm, according to the increasing cure times, but in 2 mm depth the degree of conversion decreased with increasing light-curing times and OPTEC BOND showed contrary tendency, but there was no ststistical importance in the differences among the experimental group.(P>0.05) 4. The optical density by MTT assay of extractions of CR INLAY CEMENT, DUAL CEMENT and OPTEC BOND revealed no statitically important differences comparing with optical density of negative control.(P>0.05) 5. CR INLAY CEMENT showed a tendency of increaing cytotoxicity with days and DUAL CEMENT and OPTEC BOND showed higher cytotoxicity in 2 days than in 4 days, but there was no statistical importance in the differences.(P>0.05).

• Elastomers and Composites
• /
• v.35 no.2
• /
• pp.132-137
• /
• 2000

The cure and physical properties of EPDM foam containing ground rubber and carbon black as filler were studied. The cure time reduced with the addition of filler. This result means reducing the operation time. In case of ground rubber was used, blowing ratio, tensile strength, and elongation were decreased rapidly at above 30 phr. On the other hand, in case of carbon black, they showed similar physical properties until 70 phr was used limited to 30 phr to make a good foam, which should be due to low interfacial interaction between EPDM and ground rubber. All the EPDM foams showed excellent thermal stability.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.595-595
• /
• 2001

As the interest for esthetic restoration is increasing, the usage of composite resin is increasing. The usage of composite resin is not limited to anterior teeth but is spreading to posterior area using direct ＆ indirect methods. Generally, dual or chemical cure resin cement has been used for setting composite or porcelain inlay restoration. However, chemical cure resin cement has limited working time and it's difficult to remove excess cement from the tooth and the restoration. The dual cured composite is also difficult to remove from the tooth surface.(omitted)

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.199-207
• /
• 2001

In the present study the cure behavior of diglycidyl ether of bisphenol-A(DGEBA) using an anhydride-based hardener in the presence of N,N-dimethyl benzyl amine (BDMA) or 1-cyanoethyl-2-ethyl-4-methyl imidazole (2E4MZ-CN) as an accelerator has been monitored and interpreted from the viewpoint of photophysical properties by means of fluorescence spectroscopy. To do this, 1,3-bis-(1-pyrene)propane (BPP) was well incorporated in the epoxy resin system by mechanical blending. The BPP probe, which is very sensitive to conformational change of the molecule influenced by the surrounding medium, successfully formed intramolecular excimer fluorescence. It is susceptible to the micro-viscosity or local viscosity and molecular mobility according to the epoxy cure. The cure behavior was explained with monomer fluorescence intensity ($I_{M}$ ), excimer fluorescence intensity ($I_{E}$ ) and $I_{M}$ /$I_{E}$ ratio as a function of cure time, cure temperature and accelerator. The present work agreed with the previous report on the cure behavior of an epoxy-anhydride system studied using DSC or torsion pendulum method. This study also suggests that the use of fluorescence technique may provide information on cure behavior of a thermosetting resin in a low temperature region, which has not been well interpreted by other analytical methods.

• Restorative Dentistry and Endodontics
• /
• v.20 no.1
• /
• pp.303-315
• /
• 1995

An adequate and homogeneous cure of light-activated restroative material is very important for improvement of marginal adaptation and prevention of marginal leakage, secondary caries and pulpal irritation as well as expressing natural physical property of that material. The purpose of this study was to evaluate the change of surface hardness and cure uniformity of light-activated glass ionomer cements. Restorative(Fuji II LC, Vitremer) and lining(Baseline VLC, Vitrebond) light-activated glass ionomer cements were investigated for this study. The surface hardness of the top and bottom surfaces and cure uniformity of each 1mm, 1.5mm, 2mm, 2.5mm & 3mm in the thickness of specimen were measured immediately, at 1 hour, 24 hours and 1 week after light activation. The surface hardness change and cure uniformity of all the specimens were measured by Knoop hardness tester. The results were as follows. 1. The surface hardness of top and bottom surfaces in all groups increased with time(p<0.01). 2. Both top and bottom surfaces hardness of Vitrebond group measured immediately after light-activation were significantly lower than those of the other groups(p<0.01). 3. The surface hardness of top and bottom surfaces of restorative light -activated glass ionomer cements was higher than those of lining materials at 1 week(p<0.10). 4. Surface hardness of Vitremer group decreased as the specimen thickness increased, except top and bottom surfaces hardness of the specimen at 1 week(p<0.01). There was no significant difference in the surface hardness of Fuji II LC with changes in the thickness except bottom surface hardness of specimen at 24 hours and 1 week (p>0.05). 5. Surface hardness of Vitrebond group significantly decreased as the specimen thickness increased(p<0.01). There was no significant difference in the surface hardness of Baseline VLC group with changes in the thickness except bottom surface hardness of specimen measured immediately after light -activation(p>0.05). 6. The hardness ratio of top against bottom surface in all groups decreased with time(p<0.05). 7. There was no significant difference in the hardness ratio of top against bottom surface with changes of the thickness except Vitrebond group, 24 hours and 1 week of Vitremer group and 1 week of Baseline VLC group (p>0.05). These results suggest that surface hardness of restorative ligh-activated glass ionomer cements were highter than those of lining light-activated materials. In all groups, the surface hardness and cure uniformity continuously increased with time.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.04a
• /
• pp.53-58
• /
• 2000

During the curing process of thick glass/epoxy laminates, a substantial amount of temperature lag and overshoot at the center of the laminates is usually experienced due to the large thickness and low thermal conductivity of the glass/epoxy composites. Also, it requires a longer time for full and uniform consolidation. In this work, temperature, degree of cure and consolidation of a 20mm thick unidirectional glass/epoxy laminate were investigated using an experiment and a 3-dimentional numerical analysis considering the exothermic reaction. From the experimental and numerical results, it was found that the experimentally obtained temperature profile agreed well with the numerical one and the cure cycle recommended by the prepreg manufacturer should be modified to prevent a temperature overshoot and to obtain full consolidation.