• Nuclear Engineering and Technology
• /
• 제13권4호
• /
• pp.245-253
• /
• 1981

고분자피복재 중 polyethylene은 전기적 절연성 및 내방사선성이 좋으나 난연성이 결여되어 있으므로 이 단점을 개질하였다. 방사선을 이용하여 polyethylene에 여러 종류의 난연제를 고착시켰는데 grafting 방법과 blending후 crosslinking 방법을 사용하였다. 일반적으로 grafting시키는 경우 시료에 난연제가 고착되는 량은 방사선선량이 증가할수록 증가하였다. Grafting 방법으로 polyethylene에 난연제를 고착시킬 때 시료를 팽윤(swelling)시켜서 난연제를 grafting시켜야 한다. Blending 한 후 crosslinking시킨 경우 시료와 난연제의 량을 자유롭게 조절하여 blending하여 crosslinking시킬 수 있는 이질이 있다. 난연제를 고착시키는 2가지 방법중 blending후 crosslinking 시키는 방법이 가장 바람직하다.

• 한국염색가공학회지
• /
• 제10권4호
• /
• pp.1-6
• /
• 1998

It is important in the durable water and oil repellent finishing for wool fabric what kinds of water-repellent agents will be used. Water repellent agents and its concentration were aleady chosen in the previous paper, one of the crosslinking agents which has less damages(harsh handle or yellowing) to the treated fabrics was a low molecular weight urethane-based resins(eg. Elastron BN-11). In repellent finishing, fabrics were padded in a bath which contained aqueous solution of water-repellent agents, and crosslinking agents, and wetting agents, followed by drying and curing. The most suitable treating condition for excellent repellency and durability to dry-cleaning was as follows ： Fabrics are padded at liquor pick-up ratio of 50%, with aqueous solution which contained $30g/\ell$ of water-repellent agents, and $1g/\ell$ of crosslinking agents, and 40g/s of wetting agents. And the padded fabrics were dried at $110^\circ{C}$ for 1 minute, and cured at $160^\circ{C}$ for 1 minute. For the fabrics, water and oil repellencies and durability to repeated dry-cleanings were observed. For enhancing the durability to dry-cleaning, the role of crosslinking agents was important for they bonds water-repellent agents and fibers to 3-dimensional net structure. Therefore, the most suitable drying and curing conditions should be selected according to the kinds of crosslinking agents.

• 한국염색가공학회지
• /
• 제21권4호
• /
• pp.39-45
• /
• 2009

PVA films were crosslinked with dimethylol dihydroxy ethylene urea (DMDHEU) and three polycarboxylic acids of butanetetracarboxylic acid (BTCA), citric acid and malic acid Different factors influencing the crosslinking treatment with BTCA were investigated including BTCA and sodium hypophosphite (SHP) concentration, curing temperature and time. The cured films was extracted with boiling water and gel fraction was calculated based on weight change of the PVA films. The gel fraction of PVA films increased with increasing curing temperature and time. And the resistance to water and thermal stability of the crosslinked PVA films improved with the BTCA crosslinking treatment. While crosslinking with citric acid gave the highest gel fraction among the crosslinkers, crosslinking with malic acid showed the highest absorbancy in 0.9% saline solution, which was attributed to lower crosslink density and high number-average molecular weight between crosslinks. The superabsorbent PVA films could be prepared by adjusting the crosslinking condition of PVA with polycarboxilic acids.

• 접착 및 계면
• /
• 제17권2호
• /
• pp.56-61
• /
• 2016

본 연구에서는 아크릴 접착제의 물성에 대한 주 모노머의 영향을 비교하기 위하여 2-ethylhexyl acrylate 대신에 butyl acrylate를 사용하여 acrylic acid와 2-hydroxyethyl methacrylate의 공중합체를 합성하고 2종의 경화제를 이용하여 접착 물성을 연구하였다. 선형의 측쇄사슬을 가진 butyl acrylate계 점착제는 가지형태의 측쇄를 가진 2-ethylhexyl acrylate계 접착제에 비해 낮은 접착특성을 보였다. 경화제의 경우 가교점이 많고 가교반응을 통해 유연한 ether나 ester그룹을 생성하는 epoxy형 경화제에서 우수한 물성을 보였고 관능기인 산의 농도가 높을수록 접착특성이 향상되는 것을 관찰하였다.

• 반도체디스플레이기술학회지
• /
• 제15권1호
• /
• pp.12-16
• /
• 2016

Toluene-free pressure sensitive adhesives were synthesized by using butyl acrylate (BA), 2-hydroxy ethyl acrylate, methyl methacrylate, acrylic acid (AA) as monomers and ethyl acetate as a solvent. The polymerization recipes were designed by changing 1, 3, 5 part per hundreds monomer (phm) of AA content on the basis of 100 BA parts. Two crosslinking agents, ethyl glycol diglycidyl ether (EDGE) and isophorone diisocyanate (IPDI) were added to the synthesized polymers to increase adhesion due to crosslinking. In the measurement of properties, holding power, peel strength, and initial tackiness increased with AA content due to crosslinking between carboxyl group in AA and epoxy group in EDGE and isocyanate group in IPDI. In the comparison of two crosslinking agents, EDGE showed better in the three properties than IPDI by better reaction of epoxy group of EDGE to carboxyl group of AA.

• Elastomers and Composites
• /
• 제53권4호
• /
• pp.202-206
• /
• 2018

Five solution styrene butadiene rubber/neodymium butadiene rubber (SSBR/NdBR) composites were manufactured using different ratios of SSBR and NdBR. In this study, the composites were reinforced with NdBR and silica to confirm the physical properties of SSBR used for treads of automobile tires and the dispersibility with silica. The morphologies of the rubber composites were observed using field-emission scanning electron microscopy (FE-SEM). The crosslinking behaviors of the composites were tested using a rubber process analyzer (RPA), and the abrasion resistances were tested using a National Bureau of Standards (NBS) abrasion tester. The hardness values, tensile strengths, and cold resistances of the composites were also tested according to ASTM standards. Increased NdBR content yielded composites with excellent crosslinking properties, abrasion resistances, hardnesses, tensile strengths, and cold resistances. The crosslinking point increased due to the double bond in NdBR, thereby increasing the degree of crosslinking in the composites. The NdBR-reinforced composites exhibited excellent abrasion resistances, which is explained as follows. In SSBR, a breakage is permanent because a resonance structure between styrene and SSBR forms when the molecular backbone is broken during the abrasion process. However, NdBR forms an additional crosslink due to the breakdown of the molecular backbone and high reactivity of the radicals produced. In addition, the low glass transition temperature (Tg) of NdBR provided the rubber composites with excellent cold resistances.

• 공업화학
• /
• 제32권4호
• /
• pp.472-477
• /
• 2021

다면체 올리고머 실세스퀴옥산 (POSS) 중 케이지 형태 8개의 아크릴레이트 그룹을 포함하는 POSS가 에틸렌-프로필렌-디엔고무 (EPDM) 과산화물 가교에서의 가교 거동, 기계적 특성에 미치는 영향 및 열 안정성 등을 조사하였다. 고무 100 phr당 0~12 phr의 POSS를 함량 별로 혼합하고 과산화물 가교제를 첨가하여 EPDM/POSS 복합재료를 만들었다. 가교 특성 결과 POSS의 아크릴레이트 그룹이 과산화물에 의해 활성화 되었고, 과산화물 가교 효율을 향상시키는 것으로 나타났다. EPDM/POSS 복합재료에서 POSS의 분산안정성은 떨어졌지만, 복합재료의 파단 강도, 신장률 및 열 안정성은 향상되었다.

• 방사선산업학회지
• /
• 제6권2호
• /
• pp.171-176
• /
• 2012

In this study, a crosslinked poly(styrene-butadiene-styrene) [SBS] block copolymers were prepared by using gamma ray irradiation method. The effects of various radiation doses on the degree of crosslinking, thermo property, and morphology of crosslinked SBS block copolymer were investigated. The degree of crosslinking of crosslinked SBS block copolymers were measured by gel-fraction and FT-IR. It was found that the degree of crosslinking of crosslinked SBS block copolymers increases with increase of the irradiation dose while the TGA result shows that the initial degradation temperature of irradiated SBS block copolymer was shifted to lower temperature with increasing irradiation dose. These results indicate that degradation reaction also occurs when SBS block copolymer is exposed to gamma ray irradiation for crosslinking reaction. The SAXS and FE-SEM results indicate that the phase separation of the styrene block and butadiene block was reduced with increasing irradiation dose.

• 한국염색가공학회지
• /
• 제14권3호
• /
• pp.26-33
• /
• 2002

Dyeing properties and crosslinking effect of bifunctional reactive dyes on chitosan fiber were investigated to improve the stability of chitosan fiber against the mild acidic solution and the wet processing. Chitosan fibers were crosslinked with epichlorohydrin for comparing purpose, and dyed with C. I. Reactive Red 194, C. I. Reactive Blue 50, and the reactive dye having two $\alpha$-bromoacrylamide groups at various concentrations. The initial dyeing rates of reactive dyes are rapid and chitosan fibers absorb the relatively large amount of dyes. The chitosan fibers dyed with these dyes show the low degree of swelling and the low solubility in 1 % acetic acid solution and also represent the higher thermal stability The reactive dye with two $\alpha$-bromoacrylamide groups shows higher crosslinking effect than other dyes.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 춘계학술대회 논문집
• /
• pp.130-134
• /
• 1997

The structural defects, impurities, degree of crosslinking and shrinkage of 38 field-aged distribution cables have been analyzed. For the comparison of data, 9 new cables were also subjected to an analysis. It is observed that the structural defects and degree of crosslinking show a radial profile. The structural defects are different depending on the manufacturer. A large amount of impurities is present in the insulation shield, which hold true for the new cables manufactured recently. The degree of crosslinking near both shields is lower than that at the central region of the insulation layer. It was also found that, in some cal)toes, the ins난lation was not fully crosslinked. The shrinkage of field-aged cables is higher than that of new cables.