• Journal of Welding and Joining
• /
• 제3권1호
• /
• pp.22-31
• /
• 1985

Hot straining embrittlement is one of the most important factors which cause the brittle fracture initiation even in the service temperature in the case of mild steel and high tensile steel. Therefore it is necessary to analyze thoroughly the hot straining embrittlement occurred in weld HAZ of the structural steels. The behaviors of plastic deformation and fracture toughness at the notch tip of the hot strained weld HAZ in structural steels (SB 41 KS, SA 588-Grade A ASTM) have been studied by the recrystallization technique and crack opening displacement (COD) test method. The obtained results are summarized as follows; 1. The plastic zone is formed at the notch tip of weld HAZ owing to nomotonic and cyclic hot stran, and the maximum plastic strain increases with the accumulated hot straining amounts. 2. The distribution of the effective strain at the plastic deformed zone in HAZ can be determined as follows; (.epsilon. over bar $_{p}$ )$_{\chi}$=.epsilon. over bar $_{cr}$ ( $R_{/chi}$/.chi.)$^{m}$ where, .epsilon. over bar $_{cr}$ : (SB 41; .epsilon. over bar $_{cr}$ = 0.2, SA 588; .epsilon. over bar $_{cr}$ = 0.1) 3. The embrittlement of weld HAZ in SB 41 and SA 588 is influenced by hot strain, and the degree of embrittlement becomes deeper with hot straining amounts. 4. The embrittlement of weld HAZ of SB 41 is not influenced by the hot straining amounts until .epsilon. over bar $_{max}$ = 0.36, $R_{\chi}$ = 0.065mm, however the embrittlement of structure in SA 588 is considerably influenced even by a small quantity of the hot straining amounts.s.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.61-61
• /
• 2009

This paper has been performed in order to figure out the reason of failure in T23 weldments used for boiler tube at 550 $^{\circ}C$. Defects such as cracks and cavities occurred in CGHAZ (coarse grain heat-affected-zone) and multi pass of weld metal, and these crack propagated along grain boundary. Microstructure evolution such as grain growth and carbide precipitation was investigated by optical microscope (OM), transmission electron microscope(TEM). Moreover, Auger electron spectroscope (AES) was employed in order to examine segregation along the grain boundaries. There is significant difference in grain size and precipitation distribution in the region where cracking took place. In addition, sulfur segregation was observed. Based on the results of this investigation, it has been possible to establish that this type of cracks were consistent with reheat cracking and creep damage. Selection of optimal filler metal, heat input, and PWHT temperature is required for prevention in order to avoid this type of cracking.

• Structural Engineering and Mechanics
• /
• 제5권6호
• /
• pp.803-815
• /
• 1997

It is well understood that concentrated forces applied in the plane of a beam or panel (such as a wall or slab) lead to splitting forces developing within a disturbed region forming beyond the bearing zone. In a linearly elastic material the length of the disturbed region is approximately equal to the depth of the member. In concrete structures, however, the length of the disturbed region is a function of the orthotropic properties of the concrete-steel composite. In the detailing of steel reinforcement within the disturbed regions two limit states must be satisfied; strength and serviceability (in this case the serviceability requirement being acceptable crack widths). If the design requires large redistribution of stresses, the member may perform poorly at service and/or overload. In this paper the results of a plane stress finite element investigation of concentrated loads on reinforced concrete panels are presented. Two cases are examined (i) panels loaded concentrically, and (ii) panels loaded eccentrically. The numerical investigation suggests that the bursting force distribution is substantially different from that calculated using elastic design methods currently used in some codes of practice. The optimum solution for a uniformly reinforced bursting region was found to be with the reinforcement distributed from approximately 0.2 times the effective depth of the member ($0.2D_e$) to between $1.2D_e$ and $1.6D_e$. Strut and tie models based on the finite element analyses are proposed herein.

• Computers and Concrete
• /
• 제24권5호
• /
• pp.413-422
• /
• 2019

In this study, 3D Meso-scale finite-element model is presented to study the mechanical behavior of steel microfiber-reinforced polymer concrete considering the random distribution of fibers in the matrix. The composite comprises two separate parts which are the polymer composite and steel microfibers. The polymer composite is assumed to be homogeneous, which its mechanical properties are measured by performing experimental tests. The steel microfiber-polymer bonding is simulated with the Cohesive Zone Model (CZM) to offer more-realistic assumptions. The CZM parameters are obtained by calibrating the numerical model using the results of the experimental pullout tests on an individual microfiber. The accuracy of the results is validated by comparing the obtained results with the corresponding values attained from testing the steel microfiber-reinforced polymer concrete incorporating 0, 1 and 2% by volume of microfibers, which indicates the excellent accuracy of the current proposed model. The results show that the microfiber aspect ratio has a considerable effect on the mechanical properties of the reinforced polymer concrete. Applying microfibers with a higher aspect ratio improves the mechanical properties of the composite considerably especially when the first crack appears in the polymer concrete specimens.

• Earthquakes and Structures
• /
• 제17권5호
• /
• pp.435-445
• /
• 2019

The collapses of curved bridges are mainly caused by the damaged columns, subjected to the combined loadings of axial load, shear force, flexural moment and torsional moment, under earthquakes. However, these combined loadings have not been fully investigated. This paper firstly investigated the mechanical characteristics of the bending-torsion coupling effects, based on the seismic response spectrum analysis of 24 curved bridge models. And then 9 reinforced concrete (RC) and circular column specimens were tested, by changing the bending-tortion ratio (M/T), axial compression ratio, longitudinal reinforcement ratio and spiral reinforcement ratio, respectively. The results show that the bending-torsion coupling effects of piers are more significant, along with the decrease of girder curvature and the increase of pier height. The M/T ratio ranges from 6 to 15 for common cases, and influences the crack distribution, plastic zone and hysteretic curve of piers. And these seismic characteristics are also influenced by the compression ratio, longitudinal reinforcement ratio and spiral reinforcement ratios of piers.

• 콘크리트학회논문집
• /
• 제19권3호
• /
• pp.359-366
• /
• 2007

최근들어 내구성에 대한 사회적, 공학적 중요성이 부각됨에 따라, 염해 및 탄산화에 대한 연구가 집중되고 있다. 일반적으로 침지된 구조물의 경우를 제외하고는 염해와 탄산화는 동시에 발생하게 되는데, 탄산화 영역에서는 염화물 거동이 일반콘크리트에서의 염화물 거동과 다르게 평가된다. 그리고 콘크리트 구조에 발생된 균열은 단일열화 뿐 아니라 복합열화의 진전에도 큰 영향을 미치게 된다. 본 연구의 목적은 염화물 확산과 침투 그리고 이산화탄소 유입에 따른 탄산화 거동을 고려하여, 복합열화에 노출된 건전부 및 균열부 콘크리트 구조물의 열화 해석을 수행하는데 있다. 먼저 초기재령 콘크리트의 다상 수화 발열 모델 및 공극 구조 형성 모델을 도입한 염화물 확산 및 침투를 고려한 염화물 이동 모델을 이용하였다. 이후 탄산화 해석을 통하여 탄산화 영역 진전에 따라 변화하는 공극 분포, 포화도 및 고정화 염화물의 해리를 모델링하여 복합 열화 모델을 개발하였으며 개발된 모델은 기존의 실태 조사 결과 및 실험 결과와 비교하여 그 적용성을 검증하였다. 한편 선행된 연구 결과인 균열부의 염화물 및 탄산화 거동을 고려하여, 보통포틀랜트시멘트 (OPC; ordinary portland cement) 및 혼화재 (슬래그)를 사용한 콘크리트에 대한 복합열화 거동을 시뮬레이션 하였다. 그 결과 건전부 및 균열부에 대하여 복합열화 저항성을 평가할 수 있는 복합열화 천이 영역 (CCTZ)를 제안하였으며, 혼화재를 사용한 콘크리트가 OPC를 사용한 콘크리트에 비하여 복합열화 저항성이 우수함을 해석적으로 구명하였다.

• 콘크리트학회논문집
• /
• 제16권4호
• /
• pp.467-476
• /
• 2004

철근콘크리트(RC)의 경우 철근과 콘크리트의 부착특성에 의한 균열의 제어로 균열 후의 재료모델은 무근콘크리트(PL)와 다르다. 수평력을 받는 RC 기둥의 비선형 거동특성을 기둥의 단면을 영역화(RC영역과 PL영역)하여 각기 다른 재료모델을 적용하여 3차원 해석으로 모사였다. 파괴시 면외방향으로의 전단변형률은 비균일성을 나타내면서 진전되고 이러한 경향은 면외방향으로의 두께가 클수록 강하게 나타났다. 이러한 변형률의 분포특성을 고려하지 않는다면 2차원 해석에서는 기둥의 내하력과 변위성능을 과다하게 예측하게 된다. 인장과 전단모델에서 적절한 등가 경화계수를 도입함으로써 2차원 해석에서도 3차원 해석과 유사한 결과를 얻을 수 있음을 확인하였다.

• Journal of Welding and Joining
• /
• 제27권2호
• /
• pp.69-75
• /
• 2009

The effects of welding speed were investigated on penetration characteristics, defects and mechanical properties including formability test in Nd:YAG laser welded 1000MPa grade DP steels. A shielding gas was not used and bead-on-plate welding was performed with various welding speeds at 3.5kW laser power. Defects of surface and inner beads were not observed in all welding speeds. As the welding speed increased, the weld cross-section varied from the trapezoid having wider bottom bead, through X type, finally to V type in partial penetration range of welding speeds. The characteristic of hardness distribution was also investigated. The center of HAZ had maximum hardness, followed by a slight decrease of hardness as approaching to FZ. Significant softening occurred at the HAZ near BM. Regardless of the welding speed, the weld showed approximately the same hardness distribution. In the perpendicular tensile test with respect to the weld direction, all specimens were fractured at the softening zone. In the parallel tensile test to the weld direction, the first crack occurred at weld center and then propagated into the weld. Good formability over 80% was taken for all welding conditions.

• 대한토목학회논문집
• /
• 제4권3호
• /
• pp.19-25
• /
• 1984

용접구조에 있어서 가장 위험한 단면은 용접부이며 대부분의 파괴가 용접부로부터 발생하였다. 따라서 용접부의 파괴거동을 확인하는 것은 파괴방지를 위하여 중요한 요소라 할 수 있다. 본 연구는 용접부의 파괴거동에 관한 기초적인 연구로서 용접부의 국부적인 인성분포와 다층용접의 효과 및 잔류응력제거풀림의 효과를 조사하였다. 연구에 사용된 기본소재로서는 피로이력을 갖고 있는 강재와 피로이력이 없는 강재를 선택하였다. 용접부에서 미사용강재(피로이력이 없는 강재)모재, 열영향부 용착금속의 파괴인성이 각각 차이가 있었고 용착금속은 균열저지능력으로서 파괴인성이 가장 작아서 파괴발생원이 될수 있음을 확인하였다. 특히 본연구의 대상강재인 기사용강재(피로이력을 갖고 있는 강재)는 파괴인성이 용착금속 보다 작아서 균열이 존재하는 경우 가장 취약한 단면이 될수 있다는 것을 확인하였다. 다충용접은 용접부에 결합이 존재하지 않는다면 안정개선에 효과가 있음을 확인하였고 또한 잔류응력제거 풀림은 본연구에 관한 한은 효과가 없는 것으로 밝혀졌다.

• 비파괴검사학회지
• /
• 제16권1호
• /
• pp.10-18
• /
• 1996

본 연구에서는 SS41 불림재와 M.E.F. 복합 조직강에 대해서 파괴 역학 파라미터와 X-선 파라미터 사이의 관계를 규명하였다. 피로 균열 진전 실험이 수행되었고, X-선 회절 방법이 피로 파단면에 적용되었다. 피로 파단면을 순차적으로 전해 연마하면서 깊이에 따른 X-선 파라미터(잔류응력, 반가폭)의 변화를 관찰하였다. 최대 소성역 깊이 $w_y$는 SS41 불림재에서는 반가폭의 분포로, M.E.F. 복합 조직강에 대해서는 잔류 응력의 분포로 결정할 수 있었다. 피로 파단면의 깊이 방향에 따른 X-선 파라미터의 분포로부터 $K_{max}$과 $w_y$의 관계식이 실험 데이타로부터 얻어지고, 이 식들으로부터 $K_{max}$은 $w_y$의 측정에 의하여 추정되어질 수 있다.