• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.141-146
• /
• 2000

Crack closure and growth behavior of physically short fatigue cracks under random loading are investigated by performing narrow- and wide-band random loading tests for various stress ratios. The importance of the crack closure phenomenon is examined by predicting the growth lives of short cracks using obtained crack opening behavior. Artificially prepared two-dimensional, short through-thickness cracks are used. The crack opening load of short cracks is much lower under random loading than under constant-amplitude loading corresponding to the largest load cycle in a random load history. This result indicates that the largest load cycle in a random load history has an effect to enhance crack opening of short cracks. Most of the life prediction ratios are within the factor of 2 scatter band except several data at very short crack sizes, indicating that crack growth predictions based on the measured crack opening data are excellent. From the results obtained in this study, it can be concluded that crack closure is the primary factor governing fatigue crack growth of short cracks under random loading as well as under constant-amplitude loading.

• Journal of the Korean Ceramic Society
• /
• v.46 no.2
• /
• pp.211-218
• /
• 2009

For the Y5V characteristic MLCC which is very prone to crack, it is important to to find out the basic cause of the crack. After finding out the crack origin, the materials and processes should be developed to remove the crack. The microstructures of the cracks were investigated using the fractographic method for the various types of cracks such as an exterior crack, a cyclic thermal shock crack, and an piezo-electric crack. It was found out that the crack origin was the pore at the end of the Ni inner electrode after bake-out. Even though the three dimensional crack shapes were different, the crack origins were seemed to be similar. The exterior crack could grow from the origin with the aids of residual and applied stress. FEM (finite element method) analysis was used to calculate the stress distribution of residual and applied stress. And the concept of fracture mechanics was applied for the explanation of the crack initiation and propagation from the stresses concentration.

• Carbon letters
• /
• v.7 no.1
• /
• pp.19-26
• /
• 2006

Three point bending tests of single edge notched beam (SENB) specimens were carried out to evaluate the fracture behavior of the fine-grain isotropic nuclear grade graphite, IG-11. To measure the crack initiation point and the subsequent crack growth, the direct current potential drop (DCPD) method and a traveling microscope were used. The effects of test variables like initial crack length, specimen thickness, notch type and loading rate on the measured fracture toughness, $K_Q$, were investigated. Based on the test results, the ranges of the test variables to measure the reliable fracture toughness value were proposed. During the crack growth, the rising R-curve behavior was observed in IG-11 graphite when the superficial crack length measured on the specimen surface was used. The increase of crack growth resistance was discussed in terms of crack bridging, crack meandering, crack branching, microcracking and crack deflection, which increase the surface energy and friction force.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.6
• /
• pp.82-88
• /
• 2000

The effect of the welding for the offshore structure in the TMCP steel on the fatigue crack propagation rate and crack opening-and-closure behavior was examined. The welding anisotropy of the TMCP steel and crack propagation characteristics of the excessive loading were reviewed. (1) It seemed that a heat which was generated by the welding made a compressive residual stress over the base metal, so fatigue crack propagation rate was placed lower than in case of the base metal. (20 In the base metal, an effect of the anisotropy which has an effect of fatigue crack propagation rate of the excessive load and the constant amplitude laos was not found but in the welding material case, fatigue crack propagation rate of the excessive load in the specimen of the width direction was located in the retard side as compared with a specimen rolling direction. (3) A crack opening ratio of the used TMCP stel in this study was not changed after excessive loading but a retard phenomenon of crack propagation was observed. Consequently, it was thought that all of the retard phenomenon of crack propagation did not only a cause of the crack opening-and-closure phenomenon.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.4
• /
• pp.432-440
• /
• 2007

In this study, we have investigated the closure behavior of fatigue cracks in SAPH440 steel plates under a mixed-mode I+II loading. A crack image capturing system as a direct measuring method was used to measure the closure levels at a crack tip. The crack closure levels in the fluctuation and stable sections were increased with the increase of the mode mixture ratio. The mode mixture ratio independent fatigue crack propagation rates equation was calculated by considering mixed-mode crack closure levels. The equation was examined according to the application method of crack opening ratio. The fracture surface analysis by C-scan method was also performed in order to investigate the closure mechanism and propagation mode of crack under the mixed-mode I+II loading. The crack closure under the mixed mode I+II is confirmed as a surface roughness closure by the quantitative analysis of fracture surface using the proposed surface roughness parameter.

• International Journal of Highway Engineering
• /
• v.18 no.2
• /
• pp.43-49
• /
• 2016

PURPOSES : The field application and performance of continuously reinforced concrete pavement (CRCP), constructed by using the mechanical tube-feeding method, are evaluated in this study. METHODS: The location of the rebar was evaluated by using the MIRA system. The early-age CRCP performance was evaluated via visual survey, in which the crack spacing and crack width were examined. RESULTS: The location of longitudinal reinforcing bars was evaluated via MIRA testing and the results showed that the longitudinal rebars all lie within a given tolerance limit (${\pm}2.5cm$) of the target elevation. In addition, owing to the low temperature when the concrete was pured, the crack spacing in the Dae-Gu direction is slightly wider than that of the Gwang-Ju direction. Almost all of the crack spacings lay within the range of 1.0 m~3.0 m. A crack width of <0.3 mm was measured at the pavement surface. However, as revealed by the field survey, the crack spacing was not correlated with the crack width. CONCLUSIONS : In CRCP constructed by using the mechanical tube-feeding method, almost all of the longitudinal reinforcing bars lay within the tolerance limit (2.5 cm) of the target elevation. The concrete-placing temperature affects the crack spacing, owing to variations in the zero-stress temperature. Crack survey results show that there is no correlation between the crack spacing and crack width in CRCP.

• Computers and Concrete
• /
• v.7 no.6
• /
• pp.483-496
• /
• 2010

This work deals with the determination of crack openings in 2D reinforced concrete structures using the Finite Element Method with a smeared rotating crack model or an embedded crack model. In the smeared crack model, the strong discontinuity associated with the crack is spread throughout the finite element. As is well known, the continuity of the displacement field assumed for these models is incompatible with the actual discontinuity. However, this type of model has been used extensively due to the relative computational simplicity it provides by treating cracks in a continuum framework, as well as the reportedly good predictions of reinforced concrete members' structural behavior. On the other hand, by enriching the displacement field within each finite element crossed by the crack path, the embedded crack model is able to describe the effects of actual discontinuities (cracks). This paper presents a comparative study of the abilities of these 2D models in predicting the mechanical behavior of reinforced concrete structures. Structural responses are compared with experimental results from the literature, including crack patterns, crack openings and rebar stresses predicted by both models.

• Structural Engineering and Mechanics
• /
• v.63 no.3
• /
• pp.329-345
• /
• 2017

This paper devoted to study dynamic interaction between crack and inclusion or void by developing the eXtended Finite Element Methods (XFEM). A novel XFEM approximation is presented for these structures containing multi discontinuities (void, inclusion, and crack). The level set methods are used so that elements that include a crack segment, the boundary of a void, or the boundary of an inclusion are not required to conform to discontinuous edges. The investigation covers the effects of a single circular or elliptical void / stiff inclusion, and multi stiff inclusions on the crack propagation path under dynamic loads. Both the void and the inclusion have a significant effect on the dynamic crack propagation path. The crack initially curves towards into the void, then, the crack moves round the void and propagates away the void. If a large void lies in front of crack tip, the crack may propagate into the void. If an enough small void lies in front of crack tip, the void may have a slight or no influence on the crack propagation path. For a stiff inclusion, the crack initially propagates away the inclusion, then, after the crack moves round the inclusion, it starts to propagate along its original path. As ${\delta}$ (the ratio of the elastic modulus of the inclusion to that of the matrix) increases, a larger curvature of the crack path deflection can be observed. However, as ${\delta}$ increases from 2 to 10, the curvature has an evident increase. By comparison, the curvature has a slight increase, as ${\delta}$ increases from 10 to 1000.

• Journal of the Society of Naval Architects of Korea
• /
• v.44 no.4
• /
• pp.417-424
• /
• 2007

With regard to corrosion fatigue crack initiation life (Nc), it has been treated ambiguously for the member which doesn't have stress concentration area. In this research, in order to clarify the corrosion fatigue crack initiation life (Nc), corrosion fatigue tests were carried out. Reasonable and universal corrosion fatigue crack initiation life (Nc) was defined and corrosion fatigue crack initiation/propagation model was suggested also. As the fatigue crack which emanates from the pit is usually small, accordingly it is treated as a small crack. In addition, the observation of the corrosion fatigue fracture surfaces using SEM was conducted. And the fracture mechanics analysis using an intrinsic crack model was conducted for the treatment of the small crack. Finally, the followings were obtained. When there is no clear stress concentration point which seems to fall into a corrosion fatigue crack initiation life, the significance of the definition and suggestion of the moment of the reasonable and universal corrosion fatigue crack initiation life (Nc), at which the fatigue crack propagation rate becomes faster than the corrosion pit growth rate so that the fatigue crack initiates from the pit and propagates in earnest, has been clarified.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.813-819
• /
• 1999

Inner crack-like pores with controlled amount of Ca impurity level in the high purity alumina single crystal sapphire had been created by micro-fabrication technique which includes ion implantation photo-lithography Ar ion milling and hot press technique. The morphological change and the healing of crack-like pore in the Ca doped high purity single crystal alumina during high temperature heat treatment in vacuum were observed using optical microscopy. The hexagonal bridging ligaments were developed and the size of hexagonal bridging ligaments had been increased with temperature and Ca amount and had grown to their corner rounded. It appeared that the hexagonal bridging ligaments would have an equilbrium size with temperature and the amount of Ca addition. Three kinds of crack-like pore healing type were observed. Edge regression and ligament growth were observed from relatively low temperature in the crack-like pore. Edge regression were found in almost all of the crack-like pore but the ligament growth were found only in the several crack-like pores accelerating heating very fast. Flow type healing was observed above $1800^{\circ}C$ and It healed the crack-like pore very slowly.