• Corrosion Science and Technology
• /
• 제6권3호
• /
• pp.103-111
• /
• 2007

The effect of stress factors on the growing process of stress corrosion cracking (SCC) of the sensitized 18-8 stainless steel in high temperature water was investigated using equations of crack growth rate derived from applying electric circuits to SCC corrosion paths. Three kinds of cross sections have to be considered when electric circuit is constructed using total current. The first is ion flow passage area, $S_{sol}$, of solution in crack, the second is total dissolving surface area, $S_{dis}$, of metal on electrode of crack tip and the third is dissolving cross section, $S_{met}$, of metal on grain boundary or in base metal or in welding metal. Stress may affect each area. $S_{sol}$ may depend on applied stress, $\sigma_{\infty}$, related with crack depth. $S_{dis}$ is expressed using a factor of $\varepsilon(K)$ and may depend on stress intensity factor, K only. SCC crack growth rate is ordinarily estimated using a variable of K only as stress factor. However it may be expected that SCC crack growth rate depends on both applied stress $\sigma_{\infty}$ and K or both crack depth and K from this consideration.$\varepsilon(K)$ is expressed as ${\varepsilon}(K)=h_2{\cdot}K^2+h_3{\cdot}K^3$ when $h_{2}$ and $h_{3}$ are coefficients. Also, relationships between SCC crack growth rate, da/dt and K were simulated and compared with the literature data of JBWR-VIP-04, NRC NUREG-0313 Rev.2 and SKIFS Draft. It was pointed out in CT test that the difference of distance between a point of application of force and the end of starter notch (starting point of fatigue crack) may be important to estimate SCC crack growth rate. An anode dissolution current density was quantitatively evaluated using a derived equation.

• Journal of Welding and Joining
• /
• 제33권4호
• /
• pp.1-6
• /
• 2015

Advances in laser technology have yielded a multitude of innovative processes and applications in various industries. Laser peening is a typical example invented in the mid-1990s as a surface technology, which converted residual stress from tension to compression by just irradiating successive laser pulses to metallic materials under aqueous environment without any surface preparation. The effects of laser peening have been experimentally studied on residual stress, stress corrosion cracking(SCC) susceptibility and fatigue properties with water-penetrable frequency-doubled Nd:YAG laser. In addition, laser peening has been widely used in aviation and aerospace industries, automobile manufacturing and nuclear plant. One of the most important causes to improve the above-mentioned properties is the deeper compressive residual stress induced by laser peening. Taking advantage of the process without reacting force against laser irradiation, a remote operating system was developed to apply laser peening to nuclear power reactors as a preventive maintenance measure against SCC.

• 한국안전학회지
• /
• 제25권6호
• /
• pp.1-8
• /
• 2010

P-PIE program is developed for evaluating failure probability of pipes in nuclear power plants based on the existing PRAISE program. In the program, crack growth due to fatigue loading and stress corrosion can be considered and the probability of fracture or leakage of pipes can be calculated. Crack growth simulation is performed based on stress intensity factor and a damage parameter and failure of a pipe is determined based on J integral or net section yielding. Using the developed program the failure probabilities of tubes in a domestic nuclear power is obtained and discussed.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.675-680
• /
• 2002

Cracking and bulging in welded and internally lined pressure vessels that work in thermal-mechanical cycling service have been well known problems in the petrochemical, power and nuclear industries. However, published literature and industry surveys show that similar problems have been occurring during the last 50 years. A better understanding of the causes of cracking and bulging causes is needed to improve the reliability of these pressure vessels. This study attempts to add information required for increasing the knowledge and fundamental understanding required. Typical examples of this problem are the coke drums in the delayed coking units refinery process. This case was selected for experimental work, field study and results comparison. Delayed coking units are among the refinery units that have higher economical yields. To shut down these units represents a high negative economical impact in refinery operations. Also, the maintenance costs associated with repairs are commonly very high. Cracking and bulging occurrences in the coke drums, most often at the weld areas, characterize the history of the operation of delayed coking units. To design and operate more robust coke drums with fewer problems, an improved metallurgical understanding of the cracking and bulging mechanisms is required. A methodology that is based field experience revision and metallurgical analyses for the screening of the most important variables, and subsequent finite element analyses to verify hypotheses and to rank the variables according to their impact on the coke drum lives has been developed. This indicated approach provides useful information for increasing coke drum reliability. The results of this work not only order the most important variables according to their impact in the life of the vessels, but also permit estimation of the life spans of coke drums. In conclusion, the current work shows that coke drums may fail as a combination of thermal fatigue and other degradation mechanisms such as: corrosion at high and low temperatures, detrimental metallurgical transformations and plastic deformation. It was also found that FEA is a very valuable tool for understanding cracking and bulging mechanisms in these services and for ranking the design, fabrication, operation and maintenance variables that affect coke drum reliability.

• 한국자동차공학회논문집
• /
• 제13권1호
• /
• pp.159-165
• /
• 2005

Shot peening can be defined as the process of work hardening of the surface of components by means of propelled stream of spherical shot. Benefits due to shot peening are increase in resistance to fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this study, the influence of shot peening on the corrosion was investigated on spring steel immersed in $3.5\%\;NaCl$. The immersion test was performed on the two kinds of specimens. Corrosion potential, polarization curve, residual stress and etc. were investigated from experimental results. From test results, the effect of shot peening on the corrosion was evaluated. The important results of the experimental study on the effects of shot peened spring steels on the environment corrosion are as follows; In case of corrosion potential, shot peened specimen shows more activated negative direction as compared with parent metal. Surface of specimen, which is treated with the shot peened, is placed as more activated state against inner base metal. It can cause the anti-corrosion effect on the base metal.

• 한국표면공학회지
• /
• 제44권3호
• /
• pp.105-116
• /
• 2011

Ships and offshore structures are exposed to harsh marine environments, and maintenance and repair are becoming increasingly important to the industry and the economy. The major corrosion phenomenons of metals and alloys in marine environment are pitting corrosion, stress corrosion cracking, crevice corrosion, fatigue corrosion, cavitation-erosion and etc. due to the effect of chloride ions and is quite serious. Methods of protection against corrosion can generally be divided into two groups: anodic protection and cathodic protection. Anodic protection is limited to the passivity characteristics of a material in its environment, while cathodic protection can apply methods such as sacrificial anode cathodic protection and impressed current cathodic protection. Sacrificial anode methods using Al and Zn alloys are widely used for marine structures and vessels intended for use in seawater. Impressed current cathodic protection methods are also widely used in marine environments, but tend to generate problems related to hydrogen embrittlement caused by hydrogen gas generation. Therefore, it is important to the proper maintenance and operation of the various corrosion protection systems for ship in the harsh marine environment.

• 한국압력기기공학회 논문집
• /
• 제13권2호
• /
• pp.19-30
• /
• 2017

Austenitic Stainless Steels (ASSs) are widely used as structural materials in the pressurized water reactors (PWRs) because of their superior mechanical properties and corrosion resistance. However, it is well known that ASSs are susceptible to the environmental assisted cracking (EAC) such as environmental assisted fatigue (EAF) during the long term operation. There have been extensive tests and researches to understand the extent and the mechanisms of environmental effects. In this paper, the world-wide EAF test results of ASSs are introduced including those of Korean test programs. The suggested EAF mechanisms of ASSs are also discussed. Finally, the areas of further research to resolve the issue of EAF are suggested.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.325-330
• /
• 2004

Recently, the request for the high strength of material is more and more increased in the area of industrial environment and machinery. To accomplish the high strength of materials, carbonizing treatment, nitrifying treatment, shot-peening method are representatively applied, however, shot-peening method is generally used among the surface processes. Shot peening is a cold working process used to impact Compressive residual stressed in the exposed surface layers. Benefits due to shot peening are increase in resistance to fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this study, the influence of shot peening on the corrosion was investigated on spring steel immersed in 3.5% NaCl. The immersion test as performed on the two kinds of specimens. Corrsion potential, polarization curve, residual stress and etc, were investigated from experiment results. From test result the effect of shot peening on the corrosion was evaluated. The important results of the experimental study on the effects of shot peened on the environment corrosion of spring steels are as follows; In case of corrosion potential, shot peened specimen shows more activated negative direction as compared with parent mental. Surface of specimen, which is treated with the shot peened is placed as more activated state against inner base metal. It can cause t도 anti-corrosion effect on the base metal.

• Nuclear Engineering and Technology
• /
• 제45권2호
• /
• pp.265-276
• /
• 2013

Pressure tubes made of Zr-2.5 wt% Nb alloy are important components consisting reactor coolant pressure boundary of a pressurized heavy water reactor, in which unanticipated through-wall cracks and rupture may occur due to a delayed hydride cracking (DHC). The Canadian Standards Association has provided deterministic and probabilistic structural integrity evaluation procedures to protect pressure tubes against DHC. However, intuitive understanding and subsequent assessment of flaw behaviors are still insufficient due to complex degradation mechanisms and diverse influential parameters of DHC compared with those of stress corrosion cracking and fatigue crack growth phenomena. In the present study, a deterministic flaw assessment program was developed and applied for systematic integrity assessment of the pressure tubes. Based on the examination results dealing with effects of flaw shapes, pressure tube dimensional changes, hydrogen concentrations of pressure tubes and plant operation scenarios, a simple and rough method for effective cooldown operation was proposed to minimize DHC risks. The developed deterministic assessment program for pressure tubes can be used to derive further technical bases for probabilistic damage frequency assessment.

• Journal of Advanced Marine Engineering and Technology
• /
• 제34권5호
• /
• pp.661-669
• /
• 2010

The effects of laser peening on metallic materials have been investigated with water-penetrable frequency-doubled Nd:YAG laser. Laser pulses of 200 mJ energy and 8 ns duration focused on samples underwater with 0.8 mm spot diameter. X-ray study showed that compressive residual stress was imparted on SKD61 from the surface to nearly 2 mm depth. Stress corrosion cracking (SCC) was prohibited for sensitized SUS304 even in a severely corrosive environment fatigue lives of SUS316L and SM490A welded samples were prolonged significantly in the high-cycle regime. Since 1999, laser peening has been applied to prevent SCC in operating nuclear power plants in Japan.