• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.5
• /
• pp.772-778
• /
• 2001

In this study, corrosion fatigue characteristics of 12Cr alloy steel were investigated in 3.5wt.% NaCl solution of 150$^{\circ}C$ and 4.5bar. Behavior of corrosion fatigue cracks was measured by the indirect compliance method and compared with the results in distilled water and in air. 1) 12Cr alloy steel was susceptible to temperature. Its susceptibility was increased as the temperature was increased. 2) The crack growth characteristics of 12Cr alloy steel in distilled water were similar to 3.5wt.% NaCl solution. 3) The temperature of solution affects to the crack growth characteristics of 12Cr alloy steel. In corrosion solutions of 4.5bar, 150$^{\circ}C$, fracture surfaces of corrosion fatigue crack growth at a/W=0.3 was showed the trans-granular fracture suface. As the crack grew up, it was changed to inter-granular type. In condition of high temperature, The crack growth behaviors of 12Cr alloy steel were remarkable.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1999.05a
• /
• pp.263-268
• /
• 1999

With HAZ of A 106 Gr B steel weldment, fatigue test in air, electrochemical polarization test and corrosion fatigue test in 3.5wt.% NaCl solution were performed changing load ratio. Obtained results are as follows. 1) K$\sub$op/ was independent of K$\sub$max/ and load ratio in fatigue crack growth. 2) In variation of load ratio, the scatter band of crack growth curve was reduced by half considering crack closure 3) In the result of electrochemical polarization test, current density was increased abruptly when potential was larger than corrosion potential. 4) Fatigue crack growth rate in corrosive environment was markly higher than the rate in air because of corrosion characteristics of the material and anodization of inner surface crack.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.62-69
• /
• 1995

In order to investigate the effect of TiN coating on corrosion fatigue behavior of metal, the rotary bending corrosion fatigue tests were carried out in 3% NaCl solution by using the round bar specimens of high-speed steel, SKH-9, coated with TiN by PVD method. From the experimental results, fatigue strength of TiN coating steel in air was obvious improvement as compared with that of the substrate because of the restriction of dislocation movement in near surface of the substrate by hard thin film. In 3% NaCl solution, corrosion fatigue life of TiN coating specimen in high stress level was improvement same as in air. But in low stress level, corrosion fatigue life of TiN coating one was equivalent to that without coating, due to much crack initiated from corrosion pits formed at the substrate by failure of coating layer.

• Journal of Ocean Engineering and Technology
• /
• v.6 no.2
• /
• pp.85-93
• /
• 1992

The only hardness of 2nd phase of martensite in dual phase steel which was composed of the martensite and ferrite was changed. Fatigue test was conducted by cantilever type of self-made rotated bending fatigue testing machine. The corrosion fatigue fracture behaviors of dual phase steel were investigated in 3% NaCl solution at $N_f$ = $1.5\times$$10^5$ $N_f$=1.0 $\times$ $10^6$ cycles. The fatigue strength was increased with increasing the hardness of 2nd phase. The size and number of corrsion pits were influenced by the 2nd phase hardness and pits remain constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of $\Delta$K and da/dn has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the higher the corrosion fatigue life becomes. Corrosion fatigue fracture behavior was effected by mechanics in case of $N_f$=1.5$\times$10$^5$$N_f$=1.5$\times$10$^6$ cycles.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.2 no.4
• /
• pp.53-60
• /
• 2003

Large sized marine structures are used under corrosion environment of seawater and applied by severe service loading such as an ocean current, a billow and a tempest. Marine structures are usually constructed by lots of thick wall steel pipes joining welded joints. The thickness of such as steel pipes is usually more than 40mm. The such as steels are called "Thermo-Mechanical Control Process steel (TMCP steel)" strengthened by a heat treatment in process of steel manufactures. The failure, especially crack initiation, of marine structures was starting at weld joints under service condition. Then they should be designed by basis of the fatigue strength under seawater corrosion environment of weld joints. To clarity the fatigue crack initiation behavior is important more than to clarify the crack propagation behavior on the strength design of marine structures, because it is very difficult to find out the crack initiation and propagation phenomena and then even if it will be able to find out, it is considered that the refit of the damaged parts of welded joints have a technical difficulty under the sea. Therefore, it is most important to clarify the corrosion fatigue crack initiation behavior under the seawater condition. But, there is one big difficulty to make a test for thick plate specimen, for example thicker than 40mm. Because, it is need large capacity loading apparatus to test such as thick plate specimen. In this research, the new configuration specimen for fatigue crack initiation tests was proposed. Using this new specimen, it is easy to carry out the fatigue clack initiation tests with relatively low cyclic loading and to observe a fatigue crack initiation behavior.

• Corrosion Science and Technology
• /
• v.2 no.2
• /
• pp.93-97
• /
• 2003

Fatigue crack growth test or low alloy steel was performed in high temperature water. Test parameters were dissolved oxygen content. loading frequency and R-ratio ($P_{min}/P_{max}$). Since the sulfur content or the steel was low, there were no environmentally assisted cracks (EAC) in low dissolved oxygen(DO) water. At high DO, the crack growth rate at R = 0.5 tests was much increased due to environmental effects and the crack growth rate depended on loading frequency and maximized at a critical frequency. On the other hand, R = 0.7 test results showed an anomalous decrease of the crack growth rate as much different behavior from the R = 0.5. The main reason of the decrease may be related to the crack tip closure effect. All the data could be qualitatively understood by effects of oxide rupture and anion activity at crack tip.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.113-122
• /
• 1987

Ships and offshore strrctures are exposed to the corrosive surroundings, and the extablishment of the design criteria and the elucidation on the influence by this environment are requested to maintain the safety and to demonstrate the function of the structure. In this paper, the fatigue-crack-growth behavior on the compact tension specimens of quenched, tempered HT80 grade steels and RA36 high tensile steels having a single edge fatigue cracked notch respectively, were investigated under the repeated tensile stress with constant stroke in sea water for the welded parts by shielded metal arc welding. Main results obtained are summerized as follows; 1. The fatigue-crack-growth rates da/dN in sea water appeared to be greater behavior than those in air environment at the same stress intensisy factor range $\DeltaK$. 2. The correlation data of da/dN$\DeltaK$ of the two kinds of high tensile steels in sea water showed no great difference, however, the correlation data of da/dN$\DeltaK/\sigma_y$($\sigma_y$ stands for yield strength of the material) showed that the fatigue-crack-growth behavior of RA36 plate is affected by active path corrosion(APC) mechanism, while that of HT80 grade plate is mainly affected by hydrogen embrittlement mechanism.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.35 no.1
• /
• pp.46-51
• /
• 2007

In this study, test results for fatigue crack propagation of Al-2024-T3511 are presented considering corrosion effects, and fatigue lifes are compared for the cases of corrosion and non-corrosion. Higher corrosion environments show lower fatigue life and faster crack growth. To predict the corrosion fatigue life, a corrosion factor concept is newly introduced and applied in Paris' law. The predicted results show good agreement with experimental data and this corrosion fatigue model can be successfully used for the prediction of fatigue life of aluminum structure with corrosion effects.

• Journal of Welding and Joining
• /
• v.11 no.2
• /
• pp.42-52
• /
• 1993

The corrosion fatigue fracture behaviour of dual phase steel was investigated in 3% NaCl solution at 302MPa and 137MPa. Fatigue test was conducted by cantilever type of self-made rotary bending fatigue testing machine. The fatigue strength increased with increasing the hardness of 2nd phase. Corrosion pit originated at the boundary of the 2nd phase. The size and number of corrosion pits were influenced by the 2nd phase hardness, and pits remained constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of .DELTA. K and da/dN has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the greater the corrosion fatigue life becomes. Corrosion fatigue fracture behaviour was primarily effected by mechanical factor in case of high stress(302MPa), but by electro-chemical reaction in a lower stress(137MPa). As stress level got lower and hardness of the 2nd phase got higher, the roughness of fracture surface increased.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.409-412
• /
• 2003

Fatigue strength. especially crack initiation behavior of high strength steel under marine water environment was investigated. Marine structures were usually constructed by lot of weld joints and were designed by basis of the fatigue strength of weld joints. This study was carried out to mini. The fatigue initiation behavior is more important rather than crack propagation behavior under the design of marine structures, because it is very difficult to find out the crack propagation phenomena and repair the damaged part of welded joints in sea water Then, the new configuration specimen for fatigue crack initiation tests was proposed. Using this new specimen, it is easy to carry out the crack initiation tests with relatively low cycling loading and clearly find out a crack initiation fatigue life.