• Journal of the Korea Concrete Institute
• /
• v.22 no.4
• /
• pp.575-583
• /
• 2010

This research investigated the influence of the number of twist on single fiber pullout behavior of Twisted steel (T-) fiber and tensile behavior of high performance cementitious composites reinforced with the (T-) fibers (HPFRCC). Micromechanical pullout model for T- fibers has been applied to analytically investigate the influence of various fiber parameters including the number of twist on single fiber pullout behavior; and, to optimize the number of twist to generate larger pullout energy during fiber pullout without fiber breakage. In addition, an experimental program including single fiber pullout and tensile tests has been performed to investigate the influence of twist ratio experimentally. Two types of T- fiber with different twisted ratios, T(L)- fiber (6ribs/30 mm) and T(H)- fiber (18ribs/30 mm), were tested. T(L)- fiber produced higher equivalent bond strength (larger pullout energy) although T(H)- fiber produced higher pullout stress during pullout since T(H)- fiber showed fiber breakage during pullout. Tensile test results confirmed that T(L)- fiber in high strength mortar generates better tensile performance of HPFRCC, e.g., load carrying capacity, strain capacity and multiple micro-cracking behavior.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.5
• /
• pp.131-139
• /
• 1994

The min aim of thls study was to evaluate the effect of particle slze of the fly ash as a cement additive. Experimental work was carried out with three different sizes of fly ash. 18.58, 8.95 and 4.02{$mu}m$ in average radius. Namely, the effect of particle size variation of fly ash on the physical properties of cement paste was investigated. The jluidity was decreased with increasing the addition of fly ash to cement paste regardless of the particle size variation. The decrement of the fluidity of the pulverized fly ash was higher than that of the spherical fly ash. On the other hand, the pozzolan reactivity increased with lowering particle size. In the case of specimens with 5% up to 10% addition of fly ash having a particle size of 4.02{$mu}m$. the compressive strength was increased as compared with the plain specimens before curing for 28 days and showed higher value above 800kg /$cm^2$ when cured for 60 days.This increased compressive strength was ascribed to both the closer packlng of fine particles and the pozzolan reactivity of fly ash. These results were comfirmed by measuring both the porosity of the specimens and Ca(OH ), contents remained in specimens. This work showed that could be effectively ut~lized as a blending material without any de crease in the strength of early hydration stage if we can control the particle size of fly ashes by sizing or pulverizing.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.1
• /
• pp.1-7
• /
• 2016

In this research, it used cement powder and reduction slag, which generates high hydration heat in hydration reaction without heat cure below $-5^{\circ}C$ degree. Purpose of final research is preventing freezing and thawing by making the compressive strength 5MPa in 3days below zero temperature due to own heat of concrete. and it is the result of physical characteristic and thermal property evaluation of reduction slag. Because reduction slag generates high hydration heat, compressive strength development is excellent. By generating highly hydration heat by $C_{12}A_7$ and $C_3A$ in reduction slag, compressive strength is developed in low temperature. In case of displacing only reduction slag without $SO_3$, it is indicated that quick-setting occurs by shortage of $SO_3$. For preventing quick-setting, gypsum is used essentially. According to this research result, in case of using reduction slag and gypsum as a ternary system, compressive strength developed 5MPa in 3 days below zero temperature. It is identified to prevent early frost damage of concrete below zero temperature.

• Journal of the Korea Concrete Institute
• /
• v.28 no.1
• /
• pp.59-65
• /
• 2016

Commercial synthetic resins with great amount of hydrogen atoms were investigated for neutron shielding aggregates. Total three types of resins were considered in this study: high density polyethylene (HDPE), polypropylene (PP), and ultra molecular weight polyethylene (UPE). When these resins replaced 20, 40, 60 vol% of fine aggregates, mechanical properties were first evaluated including compressive and tensile strengths, and then image/microstructure analyses such as cross-section analysis, SEM, and X-ray CT were performed. The results showed that the compressive and tensile strengths decreased with the increase of replacement ratio of HDPE and PP, which was found through image analysis that it was closely related to the distribution of resins at the failure surface of test specimens. The strength reduction of UPE was quite small compared to HDPE and PP but it abruptly increased when the replacement level exceeded 60 vol%. The results of microstructure analyses indicated that the replacement level significantly affected the amount of air void so that it is critical to determine the reasonable amount of UPE to make cementitous materials for neutron shielding.

• Journal of the Korea Concrete Institute
• /
• v.27 no.1
• /
• pp.3-9
• /
• 2015

In this study, hydration properties of ordinary Portland cement were examined, shown from a limestone and blast furnace slag alone or their mixture up to 10% as a minor mineral additives. As of setting time, it was identified that final setting became faster as the amount of limestone mixture increased, which showed limestone accelerated early hydration faster than blast furnace slag. This is because limestone did accelerate the hydration of alite. At the age of 3 days, limestone 5%-blast furnace slag 5% mixture had the highest compressive strength of mortar. It is because hydration acceleration of alite by limestone, and $Ca(OH)_2$ that was additionally formed by hydration acceleration of alite reacted with blast furnace slag, and as a result, additionally created C-S-H hydrate. Regarding the hydration properties by the age of 7 and 28 days, limestone 3%-blast furnace slag 7% of composited mixture showed the largest compressive strength, and in comparison with the 3 days in curing age. This period is when hydration reaction of blast furnace slag is active and the amount of hydrate depends on the amount of blast furnace slag mixture more than that of the limestone mixture. And in order to vitalize hydration reaction of blast furnace slag the amount of $Ca(OH)_2$ created has to increase, and thus, a small amount of limestone is necessary that can accelerate the hydration of alite. Therefore, after the age of 7 days, the fact that there were a large amount of blast furnace slag mixture and small amount of limestone mixture was effective to the strength development of ordinary Portland cement.

• Journal of the Korea Concrete Institute
• /
• v.15 no.2
• /
• pp.273-279
• /
• 2003

The purpose of this study is to clarify the effect of the monomer ratio on properties of the polymer-modified mortars using methylmethacrylate-butyl acrylate(MMA/BA) latexes, and to obtain basic data necessary to develop appropriate latexes for cement modifiers. From the test results, we knew that the pore volume of polymer-modified mortars using MMA/BA latexes at bound MMA contents of 60 and 70 percent is 7.5∼75nm and the fine pore volume is increased with an increase in the polymer-cement ratio. The total pore volume of polymer-modified mortars using MMA/BA latexes is linearly reduced with an increase in the bound MMA content and increased in the polymer-cement ratio. In general, the superior compressive strength of polymer-modified mortars using MMA/BA latexes is obtained at a bound MMA content of 70 percent and a polymer-cement ratio of 15%. And, the water absorption and chloride ion penetration depth are greatly affected by the polymer-cement ratio rather than the bound MMA content. The important factors affecting the properties of polymer-modified mortars using MMA/BA latexes polymerized with various monomer ratios are the variations of the pore size distribution with changing bound MMA content and the polymer-cement ratio.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.617-624
• /
• 2010

This paper reports on a comprehensive study on the mechanical properties of expansive fiber-reinforced strainhardening cement composite (SHCC) materials containing various replacement levels (0, 8, 10, 12 and 14%) of an expansive admixture and 1.5% polyethylene (PE) fibers volume fraction. A number of experimental tests were conducted to investigate shrinkage, compressive strength, flexural strength, and direct tension behavior. Test results show that as expected, the different replacement levels of an expansive admixture have an important effect on the evolution of the free shrinkage of SHCC with a rich mixture. At the volume fraction of 1.5%, PE fibers in normal SHCC reduce free shrinkage deformation by about 30% in comparison to plain mortar. The replacement of an expansive admixture in SHCC material has led the SHCC to a better initial cracking behavior. Enhanced cracking tendency improved mechanical properties of SHCC materials with rich mixtures. Note that an increase in the replacement of expansive admixture from 10% to 14% does not lead to a significant improvement for mechanical properties; this implies that the replacement of 10% expansive admixture is sufficient.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.137-145
• /
• 2015

The slab-type precast modular bridge consists of the precast slab bridge modules which are connected in the transverse direction. The longitudinal joints between the precast slab bridge modules are filled with cast-in-place mortar. The construction of the slab-type precast modular bridge is completed by applying the prestressing force on the longitudinal joints. In this study, 4-points bending tests and 3-points bending tests were conducted to examine the effects of the prestressing force and the shape of joint on the flexural strength and crack serviceability of longitudinal joint. The results of 4-points bending tests showed that the flexural strength is affected by the prestressing force but not by the shape of join. From the results of 3-points bending tests by which the bending moment and the shear force are simultaneously applied on the joints of the specimens, it is observed that the shape of joint affects on the flexural strength and the crack behavior. The results of two types of bending tests confirmed that the prestressing force according to the design code is appropriate and the joint with two shear keys gives the better performances against the crack of joint.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.4
• /
• pp.307-312
• /
• 2015

This paper addresses mechanical properties and length change performance of the recycled aggregate concretes(RAC) in which natural coarse was replaced by recycled coarse aggregate(RCA) by compressive strength levels(20, 35, 50 MPa). A total of 9 RAC were produced and classified into three series, each of which included three mixes designed with three compressive strength levels of 20 MPa, 35 MPa and 50 MPa and three RCA replacement ratios of 0, 50 and 100%. Physical/Mechanical properties of RAC were tested for slump test, compressive strength, and length change. The test results indicated that the workability of RC could be improved or same by RCA replacement ratios, when compared with that containing no RCA. This is probably because of the RCA shape improving the workability of RAC. Also, the test results showed that the compressive strength was decreased by 9~10% as the RCA replacement ratios increase. However, the length change ratio by the RCA replacement ratios increased regardless of compressive strength levels. At 20 MPa level, the length change ratio was 8~40% which was much higher than that of 4~17% at both 35 and 50 MPa levels. Therefore, it was considered that such admixture addition preventing dry shrinkage is required in order to improve the properties of the RAC at 20 MPa level.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.15 no.5
• /
• pp.455-468
• /
• 2013

In recent, various types of steel pipe-roof methods, which is reinforced by mortar after propulsion of steel pipe into the ground, have been used for the construction of trenchless underpass. Integrated steel pipe-roof has flexural stiffness and can resist against overburden load and reduce the stress acting on the concrete underpass structures. Due to arching effect, vertical and horizontal stress distribution around the steel pipe-roof is changing. In this study, therefore, the characteristic of stress distribution around the underpass induced by the construction of integrated steel pipe-roof is investigated by using numerical method. To examine the soil-structure interaction, interface element is introduced. Results show that vertical stress acting on the concrete structure placing inside the steel pipe-roof is significantly reduced due to arching effect and flexural stiffness of integrated steel pipe-roof. Design load can be reduced and effective design of underpass will be available if the earth pressure reduction due to arching effect is considered in the design stage.