• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.353-358
• /
• 2002

The purpose of this paper was to estimate the cumulative damage of pavement concrete by split tension fatigue test. The split tension fatigue test of variable amplitude loading were performed in two and three stages. The results of the fatigue test by variable amplitude loading showed that the sums of damage were greater than 1 in the increasing sequence loading tests, and less than 1 in the decreasing sequence loading tests. The remaining life estimated by equivalent damage theory was almost similar to that of experimental results.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1161-1166
• /
• 2001

Fatigue behavior of reinforced concrete(RC) elements has been experimentally and analytical investigated. Fatigue behavior influenced by longitudinal reinforcement ratio, strength of concrete and load ratio $P_{u}$/ $P_{o}$. The purpose of these studies is to propose an empirical formula for fatigue behavior on basis of experimental results. Also an analytical method to predict the crack propagation of RC beams has been developed based on the relationships between bond stress and slip.

• Proceedings of the Earthquake Engineering Society of Korea Conference
• /
• 2001.04a
• /
• pp.443-452
• /
• 2001

Fatigue behavior of reinforced concrete(RC) and steel fiber reinforced concrete(SFRC) beams has been experimentally investigated. Fatigue behavior influenced by longitudinal reinforcement ratio, volume and type of steel fiber, strength of concrete and load ratio $P_{u}/P_{o}$. It can be observed from experimental results that addition of steel fiber to reinforced concrete beam reduces crack widths and increases stiffness, and thus enhances the behavior in serviceability limit states also for high cyclic fatigue loading.

• Proceedings of the Earthquake Engineering Society of Korea Conference
• /
• 2001.09a
• /
• pp.431-438
• /
• 2001

Fatigue behavior of reinforced concrete(RC) and steel fiber reinforced concrete(SFRC) elements has been experimentally investigated. Fatigue behavior influenced by longitudinal reinforcement ratio, volume and type of steel fiber, strength of concrete and load ratio $P_{u}$ $P_{o}$. It can be observed from experimental results that addition of steel fiber to reinforced concrete beam reduces crack widths and increases stiffness, and thus enhances the behavior in serviceability limit states also for high cyclic fatigue loadingngng

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05a
• /
• pp.38-41
• /
• 2006

Wheel load fatigue experiment is carried out on a FRP-concrete composite deck. In FRP-concrete composite deck, FRP plays a role of a main tensile member as well as a permanent formwork and concrete plays a role of a main compressive member. Wheel load fatigue experiment, which shows more realistic behavior than pulsating fatigue experiment, is selected as a fatigue performance evaluation method. Until 1,000,000 cycles of loadings, load resistant performance is maintained without any loss, while residual deflection is increased.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.311-314
• /
• 2003

Concrete structures such as bridge, pavement, airfield, and offshore structure are normally subjected to repeated load. This paper proposes a failure probability models of concrete subjected to split tension repeated-loads, based on experimental results. The fatigue tests were performed at the stress ratio of 0.1, the loading shape of sine, the frequency of 20Hz, and the stress levels of 90, 80 and 70%. The fatigue test specimen was 150mm in diameter and 75mm in thickness. The fatigue analysis did not include which exceeded 0.9 of statistical coefficient of determination values or did not failure at 2$\times$$10^6$ cycles. The graphical method, the moment method, and maximum likelihood estimation method were used to obtain Weibull distribution parameters. The goodness-of-fit test by Kolmogorov-Smirnov test was acceptable 5% level of significance. As a result, the proposed failure probability model based on the two-parameter($\alpha and \mu$) Weibull distribution was good enough to estimate accurately the fatigue life subjected to tension mode.

• Structural Engineering and Mechanics
• /
• v.78 no.3
• /
• pp.281-296
• /
• 2021

This article analyzed the modulus degradation of concrete subjected to multi-level compressive cyclic loading. The evolution of secant elastic modulus is investigated based on measurements from top loading platen and LVDT in the middle part of concrete. The difference value of the two secant elastic moduli is reduced when close to failure and could be used as a fatigue failure precursor. The fatigue hardening is observed for concrete during cyclic loading. When the maximum stress is smaller the fatigue hardening is more obvious. The slight increase of maximum stress will lead to the "periodic hardening". The tangent elastic modulus shows a specific "bowknot" shape during cyclic loading, which can characterize the hysteresis of stress-strain and is influenced by the cyclic loading stresses. The deterioration of secant elastic modulus acts a similar role with respect to the P-wave speed during cyclic loading, can both characterize the degradation of the concrete properties.

• Journal of the Korean Society of Safety
• /
• v.9 no.2
• /
• pp.18-25
• /
• 1994

In this thesis, the fatigue tests were performed on a series of reinforced concrete to Investigate the variation of strength and the safety of reinforced concrete structures under fatigue load. The specimens were of the same rectangular cross-section, of effective height 24cm and width 30cm and their span was 330cm. The three point loading system is used in the fatigue tests. In these tests, the fracture mode of reinforced concrete structures under fatigue load, relationship between the repeated loading cycles and the mid-span displacement of the specimens were observed. According to the test results, the following fatigue behavior of reinforced concrete specimens were observed. By increasing of the number of repeated loading cycles, the mid-span displacement became greater, however the Incremental amounts of the displacement were reduced. It could be also known that the inelastic strain energy of the doubly reinforced rectangular beams was larger than that of the singly reinforced rectangular beams as increasing the number of repeated loading cycles. Compliance of reinforced concrete structures tended to be reduced as increasing the repeated loading cycles, and the compliance of the doubly reinforced rectangular beams was generally smaller than that of the singly reinforced rectangular beams. Based on the above investigation, it could be concluded that the doubly reinforced rectangular beams under fatigue load were more efficient to resist the brittle fracture than the singly reinforced rectangular beams.

• Steel and Composite Structures
• /
• v.24 no.4
• /
• pp.455-465
• /
• 2017

This paper presents a series of ultimate and fatigue experimental investigation on concrete-filled rectangular hollow section (CRHS) X joints with Perfobond Leister rib (PBR) under tension. A total of 15 specimens were fabricated, in which 12 specimens were tested under ultimate tension and 3 specimens were investigated in fatigue test. Different parameters including PBR stiffening, brace-to-chord ratio (${\beta}$) and inclined angle (${\theta}$) were considered in the test. Each joint was tested to failure under tension load. Obtained from test result, PBR was found to improve the tension strength and fatigue durability of CRHS joint substantially. Concrete dowel consisted by PBR and concrete inside the chord stiffened the joint, which leaded to a combination failure mode of punching shear and chord plastification of CRHS joint under tension. Finite element analysis validated the compound failure mode. Stress concentration on typical spot of CRHS joint was mitigated by PBR which was observed from fatigue test. Initial fatigue crack presented in CRHS joint with PBR also differentiated with the counterpart without PBR.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.37-40
• /
• 2005

Reinforced dual concrete beam (RDC beam) is the reformed system that improves the overall structural properties of beam by partially applying high performance steel fiber reinforced concrete (HPSFRC) in the lower tension part of conventional reinforced concrete beam (RC beam). Fatigue test was done to prove the structural superiority of RDC beam. As a result of fatigue test, the deflection of RDC beam was decreased obviously and the slope of number of cycle-deflection relation curve of RDC beam was increased gently in comparison with RC beam.