• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.227-234
• /
• 2022

In this study, the rheological properties of cement paste composites applied with carbon-based nano-materials were experimental analyzed. Flow table and rheological properties, compressive strength were measured in the cement paste using graphene oxide asqueous solution and carbon nanotube aqueous solution. When carbon nano-materials was mixed in an aqueous solution, flow decreased and plastic viscosity and shear stress were increased. In particular, graphene oxide rapidly increased the plastic viscosity and shear stress. In the case of carbon nanotube aqueous solution, when less than 0.2 % was mixed, the increase rate was low compared to graphene oxide. This is because the specific surface area of graphene, which is in the form of a plate, is large. The compressive strength showed a small amount in strength increase when graphene mix, and CNT had a strength about 112 % of OPC. Carbon-based nanomaterials, is considered that CNT are suitable more to be used construction materials. However, extra studies on the surfactant to be used for mixing proportion and dispersion will be needed.

• Food Engineering Progress
• /
• v.22 no.4
• /
• pp.381-385
• /
• 2018

Various rheological methods to measure the hardness of instant cooked rice by a texture analyzer were investigated and compared. Specifically, instant white rice samples with a wide range of hardness were subjected to four different rheological tests with disk, cylinder, rod, and cone probe whose results were inter-correlated. All the measurements demonstrated that the hardness of instant rice was reduced with increasing moisture content and showed negatively linear relationships. Out of the four tests applied in this study, the highest coefficient of correlation ($R^2=0.9268$) was observed distinctly in the cone probe test, where both compressive and shear forces can be applied to deform individual rice grains. However, the cylinder probe test had the lowest coefficient of correlation ($R^2=0.7247$) because it may be ineffective in causing direct deformation of individual rice grains. Furthermore, when the hardness values (N) were converted to stress (Pa), highly linear correlations ($R^2{\approx}0.99$) were observed between the tests with similar probe geometry and force application.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.127-136
• /
• 2015

To evaluate the effects of limestone powder and silica fume on the properties of high-strength high-volume ground granulated blast-furnace slag (GGBFS) blended cement concrete, this study investigated the rheology, strength development, hydration and pozzolanic reaction characteristics, porosity and pore size distribution of high-strength mortars with the water-to-binder ratio of 20, 50 to 80% GGBFS, up to 20% limestone powder, and up to 10% silica fume. According to test results, compared with the Portland cement mixture, the high-volume GGBFS mixture had much higher flow due to the low surface friction of GGBFS particles and higher strength in the early age due to the accelerated cement hydration by increase of free water; however, because of too low water-to-binder ratio and cement content, and lack of calcium hydroxide content, the pozzolanic reactio cannot be activated and the long-term strength development was limited. Limestone powder did not affect the flowability, and also accelerate the early cement hydration. However, because its effect on the acceleration of cement hydration is not greater than that of GGBFS, and it does not have hydraulic reactivity unlikely to GGBFS, compressive strength was reduced proportional to the replacement ratio of limestone powder. Also, silica fume and very fine GGBFS lowered flow and strength by absorbing more free water required for cement hydration. Capillary porosities of GGBFS blended mortars were smaller than that of OPC mortar, but the effect of limestone powder on porosity was not noticeable, and silica fume increased porosity due to low degree of hydration. Nevertheless, it is confirmed that the addition of GGBFS and silica fume increases fine pores.