• Journal of Magnetics
• /
• 제13권4호
• /
• pp.170-172
• /
• 2008

Fe-6.5% Si alloys have good magnetic properties due to their high electrical resistivity, very low magneto-striction, and low crystalline anisotropy. Despite their strong potential, these alloys have seldom been used in magnetic applications because of the very poor ductility of Si-steel above 3.0 wt% Si [1-4]. It is difficult to achieve compressed Fe-6.5% Si powder cores with excellent properties because of the low density due to poor ductility. In compressed powder cores, high density is essential in order to obtain high magnetization and permeability. In this study, an attempt was made to produce Fe-3%Si powder cores because the Fe-3.0 wt% Si alloys have relatively good magnetic properties and room temperature ductility. Gas atomized Fe-3.0 wt% Si powder was compressed into toroid shape cores. By reducing the Si content to 3.0 wt%, the hysteresis loss could be greatly reduced and thus the total core loss could be minimized. The total core loss is 600 mW/$cm^3$ at 0.1 T and 50 kHz.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1183-1184
• /
• 2006

Core loss of soft magnetic powder cores have been focused on to achieve high efficiency of power supplies. In this study the effects of crystal grain size on core loss were investigated by changing heat treatment conditions. It was found that core loss is influenced by crystal grain size because eddy current loss decreased and hysteresis loss increased by making crystal grain size smaller, and it is also influenced by particle size.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2013년도 자성 및 자성재료 국제학술대회
• /
• pp.57-58
• /
• 2013

• 한국자기학회지
• /
• 제14권5호
• /
• pp.186-191
• /
• 2004

250～850 $\mu\textrm{m}$ 크기의 FeCuNbSiB 나노결정립 합금분말에 3wt%의 전기절연체(glass frits, 활석 또는 폴리아미드 분말)를 혼합한 뒤 압축성형하여 분말코아를 만들었을 때, 절연물질의 종류에 따른 자기적 특성의 변화를 조사하고 그 결과를 비교하였다. 세라믹 물질인 glass frits와 활석은 폴리아미드에 비해 수백 kHz이하의 주파수 범위에서 높은 투자율을 나타내나 1 MHz 이상의 주파수에서는 투자율이 빠르게 낮아지는 거동을 보였다 자심손실은 glass frits와 활석을 첨가한 자심 쪽이 더 크며, 품질계수는 폴리아미드를 첨가한 자심보다 더 낮은 주파수에서 피크를 나타내고 그 값도 더 작았다. 반면 폴리아미드로 절연처리한 자심의 경우 수 MHz에 이르기까지 투자율의 저하가 거의 나타나지 않았으며, 더 우수한 자심손실 및 품질계수 특성을 보여 주었다. 그리고 직류중첩특성 또한 폴리아미드를 첨가한 자심이 100 Oe이상의 큰 자장에 이르기까지 더 우수하였다. 폴리아미드를 절연체로 사용한 경우 그 밀도가 낮음으로 인해 결국 더 많은 체적비로 혼합되므로 자성 입자 사이의 전기적 절연을 보다 더 충분히 해주고 있는 것으로 판단되었으며, 세라믹 물질을 절연체로 사용했을 때와의 이상과 같은 자기적 특성의 차이는 이 사실에 주로 의존하고 있는 것으로 평가되었다.

• 한국자기학회지
• /
• 제20권1호
• /
• pp.13-17
• /
• 2010

연자기 특성이 우수한 것으로 잘 알려진 Fe-6.5 % Si 합금을 분말로 제작하여 성형한 Fe-6.5 % Si 압분코어에서도 좋은 특성을 얻을 수 있는 지를 확인하기 위해 Fe-3, 4.2 그리고 6.8 % Si 압분코어를 각각 제작하여 교류와 직류 자기특성, 미소경도 등을 분석하였다. 실리콘 함량이 증가할수록 와전류손실은 감소하나 이력손실은 증가하여 Fe-6.8 % Si에서 최소손실을 얻을 수 없었다. 또한 실리콘함량이 증가할수록 코어의 전기비저항과 분말입자의 미소경도는 지속적으로 증가하였으며 이 때문에 충진율은 감소하였다. B2와 $DO_3$상이 Fe-6.8 % Si 분말에서만 생성된 것을 확인할 수 있었으며, 6.8 % Si보다 낮은 실리콘 함량에서 코어손실이 더 낮은 것을 절연체와 분말입자의 비저항 비율, 미소경도변화에 따른 충진율 저하와 반자장 효과 등으로 설명할 수 있었다.

• Journal of Magnetics
• /
• 제11권3호
• /
• pp.126-129
• /
• 2006

The phosphate coating on the $(Fe_{0.97}Cr_{0.03})_{76}(Si_{0.5}B_{0.5})_{22}C_2$ amorphous powders with an average size of 10 ${\mu}m$ in diameter has been carried out in aqueous 1.0-2.0 wt% $H_3PO_4$ solutions, and the consolidation behavior and magnetic properties of their compressed powder cores has been investigated. The phosphate coating could provide efficient electrical insulation between amorphous powders and improved consolidation ability at room temperature. Especially when the powders were treated in more concentrated phosphoric acid solution, enhanced phosphate covering and higher frequency/dc-bias stability were achieved. The powder cores phosphate-coated in 2.0 wt% $H_3PO_4$ solution exhibited constant permeability of 21 up to 10 MHz, 110 of the quality factor at 0.9 MHz, 610 mW/cm3 core loss at 100 kHz/0.1 T and 89 of percent permeability at 100 kHz.

• 한국자기학회지
• /
• 제15권5호
• /
• pp.270-275
• /
• 2005

가스분무법으로 제조한 $35\~180\;{\mu}m$ 크기의 $Fe-6.0wt\%Si$ 합금분말에 대하여 인산염계 절연물질을 피막처리하고 $600\~900^{\circ}C$에서 1시간 동안 열처리한 후 압축성형한 압분자심(분말코아)의 자기적 성질 및 기계적 특성을 조사하였다. 대체적으로 열처리온도가 증가할수록 압축강도가 감소하였으며, 자심손실 또한 낮아졌다. $800^{\circ}C$에서 열처리한 경우 압축성형강도가 15 kgf, 100 kHz에서 실효투자율은 74, 품질계수는 26, 50 Oe의 직류자장 하에서 퍼센트투자율은 78 정도의 값을 나타내었으며, 50 kHz-0.1 T에서 자심손실은 $750\;mW/cm^3$였다. 그리고 투자율-주파수 곡선 상에서의 cut-off 주파수는 거의 200 kHz 이상에 이르는 것으로 나타났다. $Fe-6.0wt\%Si$ 합금 압분자심의 이러한 제반 특성은 인산염 피막의 양호한 전기절연효과와, 고규소농도에 따른 합금의 결정자기이방성 및 포화자기변형의 감소, 전기비저항의 증대 등 기초 물성의 변화에 기인하는 것으로 사료되었다.

• 한국자기학회지
• /
• 제12권6호
• /
• pp.218-223
• /
• 2002

가슨 분무법으로 제조한 High-Flux형 $Ni_{x}Fe_{100-x}$(x=40~50, wt.%) 퍼멀로이 분말 및 압분 코아의 자기적 특성을 조사하였다. 포화자화는 45%Ni조성에서 최대 값을 보이며 이보다 보 함량이 낮아지면 인바 효과의 작용에 의해 급격하게 감소하였다. 압분 코아의 투자율은 Ni 농도가 낮아지면 현저히 증가하는 바 이는 자기변형의 감소에 기인하는 것으로 사료되었으며, 자심손실은 Ni=45%에서 가장 낮은 값을 나타내었다. Ni농도가 50%에서 45%로 낮아짐에 따라 자심손실이 감소하는 주원인은 전기 비저항의 증대에 따른 와전류 손실의 감소에 있는 것으로 생각되었다. Ni=45% 분말 합금으로 만든 압분 코아는 Ni=50%의 경우보다 더 우수한 투자율의 주파수 의존성, 큰 Q 값, 그리고 더 나은 직류 바이어스 특성을 나타내어 상용 High-Flux 코아(50%Ni-50%Fe)에 비해 더 좋은 압분 자심 재료가 될 수 있음을 확인하였다.

• 한국자기학회지
• /
• 제14권1호
• /
• pp.7-12
• /
• 2004

F $e_{73.5}$C $u_1$N $b_3$S $i_{15.5}$ $B_{7}$ 비정질 리본 합금을 490∼61$0^{\circ}C$의 온도 범위에서 열처리하고 이를 볼 밀링 하여 얻은 250∼850$\mu\textrm{m}$크기의 자성분말과 5wt%의 세라믹 절연체로 구성된 분말 코아의 자기적 특성에 열처리 온도가 미치는 영향을 조사하였다. 5$50^{\circ}C$에서 1 h동안 열처리하여 직경 11 nm의 $\alpha$-Fe상 나노 결정립 구조로 되었을 때(전기비저항은 110$\mu$Ω$.$cm)가장 높은 실효투자율 및 품질계수를 나타내었으며 그 값은 각각 125와 53이었고, 실효투자율의 경우 약 500 KHz에 이르기까지 일정한 크기를 유지하였다. 그리고 이 열처리 조건에서 230 mW/㎤(f=50 KHz, $B_{m}$ =0.1 T)의 대단히 낮은 자심손실을 나타내었다. 그러나 이 합금의 분말 코아는 종래의 분말 코아 재료(MPP,센더스트 등)에 비해 그리 우수하지 못한 직류 바이어스 특성 특히 저 자장 하에서의 낮은 퍼센트 투자율을 나타내었는데, 이는 종래의 소재와 유사한 투자율을 얻는데 너무 큰 입도의 분말이 필요한 것에 그 원인이 있는 것으로 이해되었다.