The aim of this study was to develop the noise and vibration damping wood-based composites by using viscoelastic polymer materials. Polyvinylchloride(PVC) was plasticized with 20-140 phr bis(2-ethylhexyl) phthalate(DOP) and the dynamic tensile mechanical properties were measured at 110Hz and approximate temperature range -100 to 150$^{\circ}$ using a Rheovibron Instrument. The PVC/DOP blends were shown to be compatible in all proportions, and both T(E”$_{max}$) and T(tan${\delta}_{max}$) shifted to the lower temperature side as the DOP content increased. The vibration damping properties of wood/polymer composites were measured using the Rheovibron instrument in a bending mode. The composite damping factor(tan ${\delta}_{c}$) of wood /PVC-DOP/wood sandwich structure correlated with the loss factor and that of the coated structure correlated with the loss modulus(E”) of the polymer layer. In addition, the sandwich structure was found to be more effective in damping than the coated structure. The logarithmic decrement (${\Delta}$c) curve of a sandwich structure, which was determined by the free-free flexural vibration method was similar in shape to the tan ${\delta}_{c}$ curve.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.2
• /
• pp.15-22
• /
• 1999

Polymeric meterials that are used for noise and vibration damper in wood/polymer/wood sandwich composites, must have a high loss factor(tan ${\delta}$), and at the same time the storage modulus(E) of $5{\times}10^7$ to $10^9$ dyne/$cm^2$ must withstand over a wide temperature and frequency ranges. In this study, the series of epoxy resinlpolyacrylate interpenetrating polymer networks(IPNs) were synthesized by simultaneous polymerization. Their dynamic tensile properties were measured at 110Hz using Rheovibron instrument. Composite damping factor(tan ${\delta}_c$) and dynamic bending modulus($E_c,\;E_^{\prime\prime}c$) of wood/polymer/wood sandwich composites were measured at 110Hz using a Rheovibron in bending mode of vibration. These dynamic tensile studies indicated that cured epoxy resin/polyacrylates IPNs were semicompatible in the sense that both the shifting of T($E^{\prime\prime}_{max}$) or T(tan ${\delta}_{max}$) and the broadening of glass transition temperature range were observed. Especially, the cured Epikote871/P(n-BMA) IPNs of composition 70/30 to 50/50 showed a relatively high tan a and appropriate E' value over a wide temperature range; consequently the tan a e curves of wood/IPNs/wood sandwich composites was broadened over a wide temperature range.