• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.297-298
• /
• 2006

Free-machining agent 'KSX' contains complex calcium oxide is developed. The effect of admix ratio of KSX on mechanical properties and machinability with two different cutting speeds is reported. KSX displays improved machinability without deterioration of mechanical properties up to 0.3mass% addition. It was observed that KSX is effective with a small addition of 0.1mass% at slower cutting speed, and increased of admix ratio is effective at faster cutting speed.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.654-655
• /
• 2006

This is about the effects deoxidization, carbonization and alloying preparation on fine grain W, WC, and grade YG8 powder reduced by "yellow tungsten oxide" and "blue tungsten oxide". The result indicates that yellow tungsten has single composition and blue tungsten oxide has complex composition. With this feature, yellow tungsten oxide got better uniformity and concentration distribution on fine particle size W and WC powder than blue tungsten oxide's. The grade alloy YG8 that made of this W or WC powder has uniform alloy construction, concentrated WC grain distribution and better alloy properties.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2002년도 추계학술강연 및 발표대회
• /
• pp.76-77
• /
• 2002

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2003년도 international symposium on advanced powder metallurgy
• /
• pp.80-81
• /
• 2003

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 추계학술발표강연 및 논문개요집
• /
• pp.32-32
• /
• 2002

• 한국세라믹학회지
• /
• 제32권11호
• /
• pp.1233-1240
• /
• 1995

LAS system, which is difficult to be sintered, was densified by using the powder synthesized from metal alkoxides. Sinterability, thermal and mechanical properties were improved through synthesizing the complex oxide powder from the addition of Ge as an alkoxide. As a result, the synthesizing and sintering temperature of the LAS system lowered by about 10$0^{\circ}C$ and its modulus of rupture (MOR) increased twice higher compared to the sample from the oxide by the direct method.

• 자원리싸이클링
• /
• 제9권4호
• /
• pp.16-27
• /
• 2000

본 연구에서는 기능성 자성재료의 원료분말을 분무배소법에 의해 제조하기 위하여 원료 용액을 효율적으로 미립화시킨 후 반응로 내로 분무시킬 수 있으며, 반응로 내부는 균일한 열분포를 이루어 열분해반응이 완전하게 진행 될 뿐만 아니라, 생성된 분말을 cyclone 및 bag filter 등의 포짐장치에서 효율적으로 포집할 수 있으며, 유해 생성가스를 청정시킬 수 있는 장치까지 포함하는 개선된 분무배소로 system을 제작하였다. 또한 본 연구에서는 불순물들을 다량 함유하고 있는 mill scale 및 ferro-Mirr을 산용액에 용해 시킨 복합 산용액의 pH를 4정도로 조절하여 용액 내에 존재하는 $SiO_2$, P 및 Al 등의 불순물들을 약 20ppm 이하로 감소시킴으로써 mill scale 및 ferro-Mn의 분무열분해를 위한 원료로의 재활용 가능성을 확인하였다. 원료용액인 정제된 복합 산용액을 nozzle을 통하여 분무배소로 내부로분무시킴으로써 Fe-Mn 계의 복합 산화물 분말을 제조하였으며, 반응온도, 원료용액 및 공기의 유입속도, nozzle tip 크기 및 원료용액의 농도 등의 주요 반응조건의 변화에 따른 생성분말의 특성 변화를 파악하였다. 생성된 분말들의 형상은 대부분의 반응조건에서 구형을 나타내고 있었으며, 조성 및 입도분포가 매우 균일하게 혼합된 형태로 나타남으로써 본 연구에 의해 제작된 분무배소로 system의 우수성을 확인할 수 있었다. 한편 본 반응조건 하에서 생성된 분말들의 결정입도가 대부분 약 100nm 이하으 초미립상태이면서 형상 및 입도분포가 매우 균일하다는 사실은 본 연구에서 제작한 분무배소, system을 이용함에 의해 Fe, Mn, Ni, Cu 및 회토류계 염화물로부터 초미립의 산화를 분말을 제조할 수 있을 뿐만 아니라, 반응분위기의 변화에 따라 초미립 순금속분말의 제조도 충분히 가능할 것으로 사료된다.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 2000년도 Proceedings of 2000 International Nano Crystals/Ceramics Forum and International Symposium on Intermaterials
• /
• pp.151-163
• /
• 2000

A polymerized organic-inorganic complexation route is introduced for the synthesis of oxide ceramic powders. Polyvinyl alcohol was used as the organic carrier for precursor ceramic gel. Porous and soft powders, which have a high specific surface area, were obtained after calcinating the aerated precursors. The PVA content and its degree of polymerization had a significant influence on the homogeneity of the final powder. In particular, attrition milling process with the porous powder resulted in ultra-fine particles. In the case of the preparation of cordierite powder, nano-size powder, which has a high specific surface area of 181 ㎡/g, was obtained by the milling process. The complexation route was also applied to the synthesis of unstable phase in room temperature like beta-cristobalite, high temperature form of silica.

• 자원리싸이클링
• /
• 제8권4호
• /
• pp.45-56
• /
• 1999

본 연구의 목적은 불순물들을 다량 함유한 mill scale과 ferro-Mn을 정제과정을 거쳐 불순물들의 함량을 100 ppm 이하로 감소시킨 후 이들을 원료로 사용하여 Mn-Zn ferrite 원료분말을 기존의 고상반응법이 아닌 분무배소 방법에 의해 제조하는데 있다. 이를 위하여 본 연구에서는 정제된 원료용액을 분무배소시킴으로써 고상의 미세한 복합산화물 분말을 형성시키며, 생성된 분말을 효율적으로 포집할 수 있을 뿐 아니라 유해 생성기체를 중화시킬 수 있는 분무배소로 system을 개발하였다. 또한 정제된 원료 용액을 본 연구에서 개발된 분무배소로 내로 투입시킴으로써 Mn-ferrite 및 $Fe_{2}O_{3}$와 $Mn_{2}O_{3}$의 복합산화물 분말을 제조하였으며, 이때 각각의 조건 하에서 생성된 분말들에 대해 조성, 비표면적 및 입도 분포 등의 물리적, 화학적 특성을 조사하였다. 분무 배소법에 의해 생성된 원료분말에 ZnO 및 기타 첨가제를 정해진 조성으로 혼합시킨 후 성형 및 엄격하게 제어된 소결과정에 의해 Mn-Zn ferrite core를 제조하였다. 또한 제조된 core에 대하여 손실값, 초투자율, 잔류자속밀도, 항자력 및 포화자속밀도의 자기적 특성을 측정하였으며, 이 결과들을 바탕으로 Mn-Zn ferrite 원료 분말을 제조하기 위한 분무배소방법의 타당성을 확인하였다.

• Archives of Metallurgy and Materials
• /
• 제64권3호
• /
• pp.921-924
• /
• 2019

In this study, ODS ferritic stainless steels were fabricated using a commercial alloy powder, and their microstructures and mechanical properties were studied to develop the advanced structural materials for high temperature service applications. Mechanical alloying and uniaxial hot pressing processes were employed to produce the ODS ferritic stainless steels. It was revealed that oxide particles in the ODS stainless steels were composed of Y-Si-O, Y-Ti-Si-O, and Y-Hf-Si-O complex oxides were observed depending on minor alloying elements, Ti and Hf. The ODS ferritic stainless steel with a Hf addition presented ultra-fine grains with uniform distributions of fine complex oxide particles which located in grains and on the grain boundaries. These favorable microstructures led to superior tensile properties than commercial stainless steel and ODS ferritic steel with Ti addition at elevated temperature.