• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2002.05a
• /
• pp.39-39
• /
• 2002

In order to improve wear and fatigue resistance of the structural materials, especially cold work roller for 304 stainless steel, an eco-super-finishing and surface hardening treatment using ultrasonic vibration energy was developed and applied to the SKD-ll roller. The eco-super-finishing machine was designed and fabricated by DesignMecha Co, by its own technology. It was observed that the surface roughness, hardness and residual stress were changed from $Ra{\;}={\;}O.25\mu\textrm{m}$, Hv=710 and ${\sigma}$={\;}+400{\;}MPa{\;}to{\;}Ra{\;}={\;}0.165\mu\textrm{m}$, Hv = 1200 and ${\sigma}=-610$ MPa after 20 KHz micro-cold forging, which means almost equal to the 300 % improvement of life-time.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10b
• /
• pp.36-39
• /
• 2003

Due to the strength and biocompatibility requirement, the stainless steel SUS 316L is widely used for trauma internal fixation device. SUS 316L can be hardened and strengthened only by cold work. In this work, the material compression test is performed both in laboratory and computer simulation by a FEM analysis software DEFORM to correlate the hardness to strain. This data is then used for preform design and predict the hardness of the finish bone plate forging. Finally, we compared the hardness between the actual forging and computer analysis results. Although the predicted hardness from computer simulation. is 55HV higher than the final forging sample, we can get good compatibility on the hardening tendency of cold forging.

• International Journal of Precision Engineering and Manufacturing
• /
• v.1 no.1
• /
• pp.91-97
• /
• 2000

Anisotropic work hardening of cold rolled low carbon steel sheets is studied. The experiments consist of two stage tensile prestraining and tensile tests. At the first prestraining, steel sheets are streteched along the rolling direction by 3% and 6% tensile strains. The second prestrains are at 0${\cric}$, 30${\cric}$, 60${\cric}$to the rolling directions by varying degrees. Tensile tests are performed on the specimens cut from the sheets after the two stage prestraining. A theoretical framework on anisotropic hardening is proposed which includes Hill's quadratic yield function, ziegler's kinematic hardening rule, and Kim and Yin's assumption on the rotation of orthotropy axes. The predicted variations of R-values with second stage tensile strain are compared with the experimental data.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.317-320
• /
• 2005

The micro-alloying forging steels have been developed to save energy consumption during forging and subsequent heat treatment stages. The work hardening ability of micro-alloying forging steels is one of major hardening component while it gives severe die damage if the forging process design is poorly set up on the other hand. In the present study, it was tried to characterize three types of micro-alloying forging steels to understand the differences with the conventional low carbon steels used fur cold forging with a spherodizing heat treatment. After forging of a certain forging part with both micro-alloying forging steels and conventional low carbon steel, several mechanical tests were carried out.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.16 no.2
• /
• pp.58-67
• /
• 2020

This study presents cyclic stress-strain and tensile test results at room temperature (RT) and 316℃ using cold-worked TP304 stainless steel base and weld metals. By comparing the cyclic hardening/softening behavior and failure cycle of cold-worked materials with those of irradiated austenitic stainless steels, the feasibility of simulating the irradiation effect on cyclic deformation and failure behaviors of TP304 stainless steel base and weld metals was investigated. It was found that, in the absence of strain-induced martensite trasformation, cold-working could properly simulate the change in cyclic hardening/softening behavior of TP304 stainless steel base and weld metals due to neutron irradiation. It was also recognized that cold-working could adequately simulate the reduction in failure cycles of TP304 stainless steel base and weld metals due to neutron irradition in the low-cycle fatigue region.

• Journal of the Korean Society of Safety
• /
• v.12 no.1
• /
• pp.19-28
• /
• 1997

This study was made of the effect of cold working on the stress corrosion cracking(SCC) of austenitlc 304 stainless steel in boiling 42% $MgCl_2$ solution. For this experiment, specimens cold-worked of 0%, 10%, 20%, 30%, 40% were fabricated respectively, and then experiments of mechanical properties and stress corrosion cracking(SCC) of these specimens were carried out. The results of these experiments indicate that the maximum resistance to SCC showed at 20% of cold working degree and that the SCC susceptibility depended on the volume fraction of deformation-induced martensite by cold working and the work hardening of matrix. On the other hand, the fracture mode was changed. This phenomenon was considered that deformation-induced martensite was grown from transgranular fracture mode to intergranular fracture mode and caused by increased of dislocation density along the slip planes.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.4
• /
• pp.395-408
• /
• 2012

An experimental investigation with 2.8kW Nd:YAG laser system was carried out to study the effects of different laser process parameters on the microstructure and hardness of STD11. The optical lens with the elliptical profile are designed to obtain a wide surface hardening area with uniform hardness. The Laser beam is allowed to scan on the surface of the work piece varying the power (1600, 1800 and 1900kW) and traverse speed (200, 400, 600, 800 and 1000mm/min) at three different F-numbers of lens. After laser surface treatment three zones, In the microstructure have been observed : melted zone(decarburization), heat affected zone(martensite), and the substrate.

• Transactions of Materials Processing
• /
• v.19 no.2
• /
• pp.95-100
• /
• 2010

Drawing and normalizing are efficient means for controlling strength, fatigue and machinability of free machining steel. Normally strength and machinability are conflicting properties which need to be optimized. In this study, the effects of normalizing temperature and reduction of area on strength, fatigue and machinability were investigated. Fine grains were generated at lower normalizing temperature and fatigue life was increased with decreasing grain size. Matrix was work hardened and elongated with increasing reduction of area. Inclusions also were elongated and cross-sectional area of inclusions along drawing axis was decreased. The effects of work hardening and grain size on fatigue life were significant, but only work hardening affected machinability. Shape and distribution of inclusions after drawing had little effect on fatigue life and machinability.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.05a
• /
• pp.409-412
• /
• 2004

Microstructures and mechanical properties of microalloyed cold forging steel and cold forged prototype automobile part are characterized. The work hardening according to the increase of plastic strain plays a major role in increasing the tensile strength of microalloyed cold forging steel during cold forming. On the other hand, inhomogeneous distribution of plastic strain causes variations in microstructure and mechanical properties. The relation between inhomogeneous distribution of plastic strain and variations in microstructure and mechanical properties is discussed. The variation of mechanical property in cold forged automobile part is analyzed using quantitative evaluation of plastic strain from finite element method.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.326-329
• /
• 2005

Since the required strength of forged part is achieved by work hardening with the accumulation of plastic strain during the cold working, severe load can be exerted on die system. So, dies are liable to the early fracture for the non-heat treated steel forging in comparison with the conventional mild steels. Therefore, it is necessary to lower the flow stress of steels as much as possible during forging steps. Bauschinger effect can be utilized to lower flow stress during forging steps by giving the tensile prestrain on the forging billet during wire drawing step. In the present study, the prestrain effect on Bauschinger phenomenon is studied to avoid difficulties with application of non-heat treated cold forging steels in practice.