The effects of annealing temperature and time on mechanical properties and microstructures were studied in cold drawn pearlitic steel wires containing 0.84wt% Si. Annealing was performed from $200^{\circ}C$ to $450^{\circ}C$ with different time of 30sec, 1min, 15min and 1hr. The increase of tensile strength at low temperature was related with strain ageing. The decrease of tensile strength at high annealing temperature was related with spherodization of cementite and the occurrence of recovery of the lamellar ferrite in the pearlite. The improvement of ductility was connected with spherodization of cementite plate in pearlite and recovery process by reduction of high dislocation density at short time annealing temperature of $400^{\circ}C$.

• 대한금속재료학회지
• /
• 제49권12호
• /
• pp.995-1000
• /
• 2011

The microstructure of Cu-24 wt.%Ag filamentary nanocomposite fabricated by a thermo-mechanical process has been investigated by transmission electron microscopy (TEM) observations. This study is focused on the stability of Ag filaments formed by cold drawing; the effects of thermal treatment on the precipitation behavior and distribution of Ag-rich precipitates were also investigated. The Ag filaments elongated along the <111> orientation were observed in Cu-rich ${\alpha}$ phase of the as-drawn specimen and the copper matrix and the silver filament have a cube on cube orientation relationship. Annealing at temperatures lower than $200^{\circ}C$ for the as-drawn specimen caused insignificant change of the fibrous morphology but squiggly interfaces or local breaking of the elongated Ag filaments were easily observed with annealing at $300^{\circ}C$. When samples were annealed at $400^{\circ}C$, discontinuous precipitation was observed in supersaturated Cu solid solution. Ag precipitates with a thickness of 7-20 nm were observed along the <112> direction and the orientation relationship between the copper matrix and the Ag precipitates maintained the same orientation relationship in the as-drawn specimen. The interface between the copper matrix and the Ag precipitates is parallel to {111} and micro-twins were observed in the Ag precipitates.

• 한국재료학회지
• /
• 제11권2호
• /
• pp.115-119
• /
• 2001

다발체형성 제조기술을 이용하여 심하게 인발가공된 Cu-Nb 미세복합재료 전선의 전기적 특성과 열처리에 따른 미세조직 변화와의 관계에 대하여 연구하였다. 다발체형성과 인발공정에 의해 제조된 전선에서 Nb필라멘트 단면방향의 형태는 직선이거나 약간 굽은 형태로 나타났다 Nb필라멘트 형태의 차이는 고온에서의 다발체형성 제조공정중의 Nb필라멘트의 파손과 실린더화에 의해 발생하였다. Cu-Nb 미세복합재료의 비저항은 Cu-Nb 계면에서의 전자 산란에 의해 주로 결정된다. $400^{\circ}C$의 어닐링온도 이하에서 전도도의 감소는 침상형태 석출물의 정합변형율과 관계된 산란의 기여가 증가하기 때문이다. 비저항의 비 ($\rho_{295K}$/$\rho_{75K}$)의 약간의 감소는 또한 Nb원자의 석출 때문이다. 50$0^{\circ}C$의 어닐링온도에서 Cu-Nb 미세복합재료의 전도도 중가는 Nb필라멘트의 조대화와 구형화때문이다