• 소성∙가공
• /
• 제20권2호
• /
• pp.99-103
• /
• 2011

Many parameters influence the frictional behavior of steel sheet during stamping. The contact pressure between a die and a sheet during stamping is one of them. Thus, this parameter is investigated for high strength steel (HSS) sheets, which are widely used for auto body panels due to their potential for weight reduction. Since HSS extend the limits of contact pressure for mild steel, the effect of this parameter on friction cannot be ignored. To investigate the influence of contact pressure on the frictional behavior of steel sheets, a flat type of friction test was conducted on three different steel sheets under various contact pressures. For bare steel sheets, the curve representing the relationship between contact pressure and friction coefficient exhibits a U shape. Coated steel sheets show a similar tendency except at low contact pressure. For these materials, when the contact pressure is very low, the friction coefficient slightly increases with pressure before it starts to decrease. The test results show that the effect of contact pressure on frictional behavior of steel sheet is not negligible even for contact pressures that are lower than the strength of HSS sheet.

• 펄프종이기술
• /
• 제33권2호
• /
• pp.49-57
• /
• 2001

This study was performed to identify the effect of calendering variables on the properties of coated paper such as sheet gloss, surface roughness, opacity, etc. The effect of calendering variables including the number of nips, pressure, machine speed and moisture content on the properties of coated paper was investigated. The calender was installed with two steel rolls and one cotton-made roll. With this calender, the coated sheets were passed through the calender from 1 to 4 times, applying the linear pressure on calender rolls, 5 through 100kg/cm and operating the machine speed 3 to 12m/min. Also, the moisture content of coated sheet was varied about 5 and 10%. It was found that sheet gloss and surface roughness of coated paper was increased with increasing the number of passing nips, linear roll pressure and the moisture content of coated paper. But it was shown that the opacity and brightness of coated paper were decreased under the above conditions due to the blackening. It was also suggested that the soft nip possibly increased the thermoplasticity of coating layer with the heat of steel roll, resulting in the reinforcement of surface properties positively. The sheet gloss and surface roughness of coated paper could be improved by the longer dwell time over the rolls.

• Journal of Welding and Joining
• /
• 제16권1호
• /
• pp.52-62
• /
• 1998

Laser beam welding of zinc-coated steel, especially lap joints, has a problem of zinc vapor produced during welding which has a low vaporization temperature of 906.deg. C. It is lower than the melting temperature of steel (1500.deg. C). The high pressure formed by vaporization of zinc during laser welding splatters the molten pool and creates porosities in weld. During laser lap welds of zinc-coated steel sheets with CW CO$_{2}$ laser the gap size has been analyzed and simulated using a FEM. The simulation has been carried out in the range of gap aetween 0 and 0.16 mm. The vaporized zinc gas has effected to prevent heat from conducting toward the bottom of sheets. In vaporized zinc gas has effected to prevent heat from conducting toward the bottom of sheets. In the case of too small gap size, zinc gas has not ejected and existed between two sheets. Therefore heat was difficult to conduct from the upper sheet to lower sheet and the upper sheet could over-melted. In the case of large gap size the zinc gas has been prefectly ejected but only a part of lower sheet has melted. The optimum range of gap size in the lap welds of zinc-coated steel sheets has been calculated to be between 0.08 and 0.12 mm. According to the comparison of experiment, the simulation is proved to be acceptable and applicable to laser lap welds.

• 한국물환경학회지
• /
• 제20권2호
• /
• pp.163-169
• /
• 2004

Feasibility of using PE sheet laminated CSP(Corrugated steel pipe) to sewers were tested via corrosion and abrasion tests for PE sheet laminated CSP; 1) corrosion test for PE film and PE coated plate, 2) corrosion test for joint of PE sheet laminated CSP, 3) corrosion test for outside of PE sheet laminated CSP, and 4) abrasion test for inside of PE sheet laminated CSP. The results for the corrosion and abrasion tests are as follows. 1. Results for corrosion tests on PE films and zinc coated steel plates that were coated with PE films show that the surfaces of both PE were not changed compared to those of original PE samples. Furthermore, PE films maintained strong adhesion on the steel plates even though they were exposed to sewage and seawater provided cutting planes of the steel plates were treated with molding. But, results for corrosion tests on the spots that were previously cut off by a knife and a cutting planes of the steel plates were treated without molding show that steel plates have been corroded if they were exposed to sewage and seawater. 2. Results for corrosion tests on joints of PE sheet laminated corrugated steel using sewage show that gathering rust was observed at cutting plane of PE sheet laminated corrugated steel after 180 days, but PE film was not flaked off. However, PE film at cutting plane was flaked off when PE sheet laminated corrugated steel was exposed to seawater. Furthermore, flaking process was severely progressed at lockseam points of which the surfaces were not smooth. 3. Results for laying PE sheet laminated corrugated steel under the ground show that the surface of untouched PE film was almost identical to that of original PE film. However, the spots that were previously cut off by a knife and a cutting plane of PE sheet laminated corrugated steel have flaked off. 4. As a result of abrasion tests conducted with PE sheet laminated corrugated steel and sand, brilliance and thickness of PE was not greatly changed under the severe abrasion conditions. Therefore, the durability of PE sheet laminated corrugated steel for abrasion was determined to be good.

• 소성∙가공
• /
• 제31권1호
• /
• pp.17-22
• /
• 2022

Hot stamping is widely used to manufacture structural parts to satisfy requirements of eco-friendly vehicles. Recently, hot forming technology using uncoated steel sheet is being studied to reduce cost and solve patent problems. In particular, research is focused on process technology capable of suppressing the generation of an oxide layer. To evaluate the oxide layer in the hot stamping process, Gleeble testing machine can be used to evaluate the oxide layer by controlling the temperature history and the atmosphere condition. At this time, since cooling by gas injection is impossible to protect the oxide layer on the surface of a specimen, research on a method for securing a quenching speed through natural cooling is required. This paper proposes a specimen shape design method to secure a target quenching speed through natural cooling when evaluating the oxide layer of an un-coated boron steel sheet by Gleeble test. For the evaluation of the oxide layer of the un-coated steel sheet through the Gleeble test, dog-bone and rectangular type specimens were used. In consideration of the hot stamping process, the temperature control conditions for the Gleeble test were set and the quenching speed according to the specimen shape design was measured. Finally, the quenching speed sensitivity according to shape parameter was analyzed through regression analysis. A quenching speed prediction equation was then constructed according to the shape of the specimen. The constructed quenching speed prediction equation can be used as a specimen design guideline to secure a target quenching speed when evaluating the oxide layer of an un-coated boron steel sheet by the Gleeble test.

• Journal of Welding and Joining
• /
• 제31권4호
• /
• pp.7-12
• /
• 2013

The dissimilar welding between magnesium alloy and steel sheet was required in automobile industry to increase the strength of the dissimilar joints. Laser brazing is one of the good joining processes for Mgsteel dissimilar joint. In this study, the effect of coating materials was evaluated on the laser brazing for the dissimilar joint between AZ31 and coated steels such as Zn, Sn and Ni. Diode direct laser was used to braze the lap-edge joint with Mg600 filler wire and Superior #21 flux. The wettability was best on Zn coated steel. The interlayer was formed at the interface between brazement and steel for all coating materials. The strengths of brazed specimen were 146.5N/mm, 204.6N/mm and 101.6N/mm for Zn, Sn and Ni coated steel respectively.

• 한국기계가공학회지
• /
• 제1권1호
• /
• pp.71-78
• /
• 2002

Since the early 1980's the use of zinc-aluminum alloy-coated steel sheet(Galvalume) for vehicular corrosion protection has increased drastically. It is consisting of 55%Al-43.4% Zn-1.6%Si. Galvalume has a good corrosion resistance, heat reflectivity and shiny appearance, which has a dendritic structure of alloy layer. It has a good corrosion resistance due to dendritic structure. But, this also has a weak point against moisture during long period of transportation as sheeted and or coiled without any relation of chromating on the surface of steel sheet or not because of high humidity and temperature. Here, We studied the corrosion mechanism by the moisture.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2006년도 추계학술대회 논문집
• /
• pp.397-398
• /
• 2006

• Journal of Welding and Joining
• /
• 제18권1호
• /
• pp.91-96
• /
• 2000

Characteristics of the weld defect, such as a blowhole and a pit in lap-jointed fillet Co₂ welds of Zn-coated steel sheet were studied in order to make clear the sequence of the blowhole formation during welding. Main conclusions obtained are as follows: 1) Blowhole, wormhole and pit were found in fillet welds, although the optimum welding condition of 200A-23V-100cm/min was applied. 2) Zn was only detected at the solidification boundary at the early stage of the blowhole formation. 3) Most of the blowholes was started to form at lap-joint by the Zn vapor. With increasing of the Zn vapor and its pressure, the blowhole was develope to th bed surface until the completion of weld solidification. 4) The behavior of the blowhole in growth was similar to that of the columnar dendrite during welding.

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.191-191
• /
• 2000

The mechanism of the blowhole and the pit formation in lap-jointed fillet CO₂ arc welds of Zn-coated steel sheet was established by the direct observation of the gas behavior in the molten pool with the high speed camera system. Main conclusions obtained are as follows1) Some blowholes were formed by incomplete back-filling to the pits at the last stage of the solidification. This type of blowhole was formed through four stages of gas in the molten pool, incubation, explosion, back-filling and completion of back-filling stage.2) Most of the pits was back-filled at the last stage of their formation. (Received September 27, 1999)