• Resources Recycling
• /
• v.17 no.6
• /
• pp.10-16
• /
• 2008

In this study, the crystallization of cerium carbonate from cerium chloride solution by addition of ammonium bicarbonate was investigated. The concentration of reactants such as cerium chloride(0.5-2M) and ammonium bicarbonate, and reaction temperature($20-60^{\circ}C$) have a great effect on the crystal types of cerium carbonate such as lanthanite-type cerium carbonate[$Ce_2(CO_3)_3{\cdot}8H_2O$] and tengerite-type cerium carbonate[$Ce_2(CO_3)_3{\cdot}2.5H_2O$]. The crystallinity of cerium carbonate changed from lanthanite to tengerite as the concentration of reactants and reaction temperature increased. Transformation of cerium carbonate hydrate was transformed to cerium hydroxy carbonate depended on the drying conditions. Cerium carbonate of lanthanite and tengerite has the shape of aggregates with plate type crystal, and the size of lanthanite and tengerite crystal was $3{\mu}m$ and $5{\mu}m$, respectively. Cerium hydroxy carbonate has the shape of aggregates with needle type crystal, and the crystal size was about $7{\mu}m$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.2
• /
• pp.101-107
• /
• 2013

Cerium compounds such as Cerium hydroxide ($Ce(OH)_3$), Cerium chloride ($CeCl_3{\cdot}nH_2O$), Cerium carbonate hydrate ($Ce_2(CO_3)_3{\cdot}8H_2O$), Cerium oxide ($CeO_2$) were synthesized using recycled Ce precursor. Cerium(IV) oxide of nanoparticles were obtained by Ultra-sonication. Cerium-sodium- sulfate compound was synthesized through acid-leaching and addition of sodium sulfate from 99 wt% purity of Ce precursor as a starting material that was recycled from the waste polishing slurry. Moreover Cerium hydroxide was obtained from Cerium-sodium-sulfate compound by adding to sodium hydroxide solution. Then Cerium chloride was synthesized by adding of hydrochloric acid to Cerium hydroxide. Needle-shaped Cerium carbonate hydrate was synthesized in the continuous process and Cerium(IV) oxide with 30~40 nm size was subsequently obtained by the calcinations and dispersion.

• Resources Recycling
• /
• v.18 no.6
• /
• pp.24-29
• /
• 2009

Since cerium carbonate becomes porous cerium oxide by releasing carbon dioxide and vapour steam during calcination of cerium carbonate, nano size cerium oxide can be obtained by milling calcined cerium carbonate. Therefore cerium carbonate [$Ce_2(CO_3)3{\cdot}XH_2O$] is used generally for the preparation of nano size cerium oxide. In order to obtain nano size cerium oxide from cerium carbonate prepared by reactive crystallization of cerium chloride solution and ammonium bicarnonate solution, the effects of experimental variables in the milling and calcination of cerium carbonate, such as calcination temperature, milling time, rpm of planetary mill, amount of dispersant and ball size for milling on the size of cerium oxide was investigated in this study. Cerium oxide prepared with the conditions of calcination temperature of $700^{\circ}C$, milling time of 5 hour was 160nm mean particle size.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.62-68
• /
• 2016

A chromium-free Ce-based conversion coating formed by immersion in a solution containing cerium chloride and nitric acid on AZ31 magnesium alloy has been studied. The effects of acid pickling on the morphology and the corrosion resistance of the cerium conversion coating were investigated. The corrosion resistance of the conversion coating prepared on AZ31 Mg alloy after organic acid pickling was better than that of inorganic acid pickling. The morphology of the conversion-coated layer was observed using optical microscope and SEM. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.0 to $1.1{\mu}m$. The main elements of the conversion coating of AZ31 Mg alloy are Mg, O, Al, Ce and Zn by EDS analysis. The electrochemical polarization results showed that the Ce-based conversion coating could reduce the corrosion activity of the AZ31 Mg alloy substrates in the presence of chloride ions.

• Journal of Energy Engineering
• /
• v.13 no.2
• /
• pp.93-100
• /
• 2004

The smear media possible to sampling and radiation detection was prepared and evaluated for the surface contamination using indirect method. The films were made by impregnating Cerium Activated Yttrium Silicate (CAYS) in a polysulfone membrane. The membranes used solution as a dimethylformamide (DMF) and methylene chloride (MC), polysulfone as a polymer matrix and CAYS as a inorganic scintillator. The proximity membranes were prepared with single- and double-layered structure. The solidified methods were immersion to the nonsolvent bath such at water and ethanol and solvent evaporation. The measurement of the photon produced by interaction with radiation and inorganic scintillator used a photomultiflier tube (PMT), amplifier, and counter. In the comparison with the low background alpha/beta counter, the counter rate using inorganic scintillator proximity membrane for the $\^$14/C surface contamination was about 50%. Also. the $^3$H counting results revealed that the prepared membranes were efficient to monitor the surface contaminated with the low energy be-ray emitter nuclides.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.06a
• /
• pp.97-104
• /
• 2004

Double-layered polysulfone composite films, containing cerium activated yttrium silicate (CAYS) as a flour, were prepared from double casting of two polymeric solutions, and their morphology and physical strength were superior to those of single-layered composites. The prepared polymeric films consist of a dense bottom layer and a CAYS-holding top layer. The former is made of coagulating the polysulfone and methylene chloride binary solution and works as a supporter to improve the composite's physical strength, while the latter holding the inorganic fluor plays a role as an active site to detect the radioactive contamination. The prepared films revealed two distinguished, but tightly attached, double layers, their attachment being identified by morphology of the interface between two layers. As prepared by water immersion coagulation, the films have highly developed macropores, compared with a dense structure in the film prepared by evaporation. In the radionuclide detection test of the CAYS-impregnated composites, the films have reliable detection capacity at a radionuclide spotting test. The double-layered composites with the dense support layer show a better stability in holding the radionuclides spotted on the surface as well as an improvement in physical strength, compared with the single-layer composites having shortcomings such as being too porous or being brittle.