• Structural Engineering and Mechanics
• /
• v.82 no.3
• /
• pp.295-312
• /
• 2022

This study investigates the effects of nano silica (NS) and micro steel fiber on the properties of ultra-high-performance concrete (UHPC). The experimental consists of three groups, each one with five percentages of NS content (0%, 2%, 4%, 6% and 8%) in addition to the 20% silica fume and 20% quartz powder proportioned according to the weight of cement added to the mixtures. In addition, three percentages of micro steel fibers (0%, 1% and 2%) were considered. Different mixtures with varying percentages of NS and micro steel fibers were prepared to set the water-to-binder ratio, such as 0.16% and 1.8% superplasticizer proportioned according the weight of the binder materials. The fresh properties, mechanical properties and elevated temperatures of the mixtures were calculated. Then, the results from the microstructure analyses were compared with that of the reference mixtureand it was found that 6% replacement of cement with NS was optimum replacement level. When the NS content was increased from 0% to 6%, the air content and permeability of the mixture decreased by 35% and 39%, the compressive and tensile strength improved by 21% and 18% and the flexural strength and modulus of elasticity increased by 20% and 11.5%, respectively. However, the effect of micro steel fibres on the compressive strength was inconclusive. The overall results indicate that micro steel fibres have the potential to improve the tensile strength, flexure strength and modulus of elasticity of the UHPC. The use of 6% NS together with 1% micro-steel fiber increased the concrete strength and reduce the cost of concrete mix.

• Journal of the Korean GEO-environmental Society
• /
• v.22 no.6
• /
• pp.27-32
• /
• 2021

Due to heavy rainfall and typhoons caused by climate change, it has become common to witness heavy rain that exceeds the design frequency of agricultural reservoirs. This has brought greater attention to the safety of irrigation facilities including agricultural reservoirs. Out of approximately 17,740 reservoirs available in Korea, 83.87% were built before 1970. To ensure the safety of these old reservoirs, their embankments are being repaired and reinforced using various techniques. Among these techniques, using the cement-bentonite cutoff wall makes it possible to construct diaphragm walls with slurry composed of cement and bentonite, while excavation. The advantages of this technique include that it is simple and fast, and ensures the uniformity of cutoff walls by enabling the immediate application of the replacement method to excavation areas; thus excellent performance is guaranteed. However, despite these advantages, the technique is not commonly used in Korea. Thus, this study investigated the changes in strength and permeability by varying the mix ratio of cement and bentonite. As a major experimental results, when the cement of 200 kg/m³ and the bentonite of 60 to 80 kg/m³ is most suitable for the repair and reinforcement of the reservoir embankments.

• Journal of the Korea Concrete Institute
• /
• v.23 no.2
• /
• pp.145-150
• /
• 2011

Presently, mass concrete structures are being built in federal and private projects of civil infrastructures and building structures. The hydration heat of mass concrete structures is the most important factor in the quality of concrete matrix and construction period. Moreover, internal cracks caused by hydration heat degrades durability, water tightness, and strength of concrete. To reduce hydration heat, it is necessary to blend belite cement (${\beta}-C_2S$) with industrial by-products (i.e. granulated slag and fly ash). In this experiment, 14 levels of binary binders and 4 levels of ternary binders were used to understand the effect of different replacement ratio on hydration heat, strength and microstructure (i.e. SEM and XRD) of mortar. Cumulative hydration heat at 28 days for the binary and ternary binders was affected by replacement ratio of fly ash and/or granulated slag. As fly ash content increased, hydration heat decreased. As granulated slag content increased, reduction rate of the hydration heat was lower than when fly ash was used. Especially, the hydration heat of ternary binder blended with 40% flyash and 30% granulated slag showed about 50% of hydration heat from using belite cement (P). The study results showed that the temperature rise of concrete matrix can be decreased by using blended belite binders producing low hydration heat and reasonable strength.

• Journal of the Society of Disaster Information
• /
• v.10 no.4
• /
• pp.566-571
• /
• 2014

Recently, with concentrated social and engineering interests on durability, diversified subsequent researches have been progressed. The Chloride-induced corrosion, carbonation, freeze-thaw etc, deterioration factors of concrete act to concrete not privately but complexly, Fly ash is most frequently used admixture which is using a reduction method of deterioration. And the fly ash effects on improvement of durability with enhancement of fluidity, decrease of crack with reduction of hydration heat, promotion of long-age strength and have a economic advantage which replaces cement as a binding material. But, fly ash have different qualities and occasionally reduce the durability and strength by adhesion of AE admixture with unburned carbon powder etc. In this study, the experiments will take about various replacement ratio of fly ash concrete, and will analyze, consider the results, after these will verify applicability and validity as admixture and binding material.

• Advances in concrete construction
• /
• v.16 no.3
• /
• pp.155-167
• /
• 2023

The penetrated chloride in concrete has different behavior with mix proportions and local exposure conditions, even in the same environments, so that it is very important to quantify surface chloride contents for durability design. As well known, the surface chloride content which is a key parameter like external loading in structural safety design increases with exposure period. In this study, concrete samples containing OPC (Ordinary Portland Cement), GGBFS (Ground Granulated Blast Furnace Slag), and FA (Fly Ash) had been exposed to submerged, tidal, and splash area for 5 years, then the surface chloride contents changing with exposure period were evaluated. The surface chloride contents were obtained from the chloride profile based on the Fick's 2nd Law, and the regression analysis for them was performed with exponential and square root function. After exposure period of 5 years in submerged and tidal area conditions, the surface chloride content of OPC concrete increased to 6.4 kg/m³ - 7.3 kg/m³, and the surface chloride content of GGBFS concrete was evaluated as 7.3 kg/m³ - 11.5 kg/m³. In the higher replacement ratio of GGBFS, the higher surface chloride contents were evaluated. The surface chloride content in FA concrete showed a range of 6.7 kg/m³ to 9.9 kg/m³, which was the intermediate level of OPC and GGBFS concrete. In the case of splash area, the surface chloride contents in all specimens were from 0.59 kg/m³ to 0.75 kg/m³, which was the lowest of all exposure conditions. Experimental constants available for durability design of chloride ingress were derived through regression analysis over exposure period. In the concrete with GGBFS replacement ratio of 50%, the increase rate of surface chloride contents decreased rapidly as the water to binder ratio increased.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.225-227
• /
• 2011

This study investigates the effect of crushed fine aggregate and chemical admixture (durability improvement agent, named DIA) on blast furnace slag-based brick. The control brick was made with recycled fine aggregate of 100% and, no cement was used. Test results showed that all specimens developed similar strength, except for the specimen without partial replacement of crushed fine aggregate at 3 days. However, it is interesting to note that this specimen without crushed fine aggregate resulted in the highest strength at 7 days. In addition, the DIA had a major effect on the absorption ratio of brick specimens. For the brick specimens with partial replacement of crushed fine aggregate with 10%, the addition of DIA with only 1% was enough to satisfy the code regulated by KS F 4004.

• Journal of the Korea Concrete Institute
• /
• v.12 no.4
• /
• pp.49-58
• /
• 2000

There are many methods to improve the performance of concrete. Especially, granuated blast furnace slag. by-products used in concrete as the replacement material of cement, could contribute to improve the fluidity, resistance of chemical attack and strength of concrete. Also, it could contribute to decrease the rate of generating hydration heat, in addition to cost-down of concrete and prevention of enviromental pollution. Therefore, in order to establish the systemical application of granuated blast furnace slag in normal concrete, the engineering properties of concrete, such as fluidity, strength, setting and hydration properties etc.. was evaluated. In this study, replacement ratio of granuated blast furnace slag was 0, 30, 50, 70(%), and target slump was 8, 12, 15, 18(cm). Results from the experiment, granuated blast furnace slag showed the outstanding effects of improving the engineering properties of concrete. From now on, positive application of granuated blast furnace slag is expected in the point of improving the performance and cost-down of concrete.

• Advances in materials Research
• /
• v.9 no.3
• /
• pp.203-218
• /
• 2020

This research paper presents the outcomes in terms of mechanical and microstructural characteristics of binary and ternary concrete when exposed to elevated temperature. Three parameter were taken into account, (a) elevated temperature (i.e., 200, 400, 600 and 800℃) (b) binary concrete with cementitious material sugarcane bagasse ash (SCBA) and ground granulated blast furnace slag (GGBFS) replacement percentage (i.e., 0, 15, 20, 25 and 30%) and (c) ternary concrete with cementitious material SCBA and GGBFS replacement percentage (i.e., 0, 15, 20, 25 and 30%). A total of 285 standard cube specimens (150 mm × 150 mm × 150 mm) containing Ordinary Portland Cement (OPC), SCBA, and GGBFS were made. These specimens then exposed to several elevated temperatures for 2 h, afterword is allowed to cool at room temperature. The following basic physical, mechanical, and microstructural characteristics were then determined and discussed. (a) mass loss ratio, (b) ultrasonic pulse velocity (UPV) (c) physical behavior, (d) compressive strength, and (e) field emission scanning electron microscope (FESEM). It was found that compressive strength increases up to 400℃; beyond this temperature, it decreases. UPV value and massloss decrease with increase in temperature as well as the change in color and crack were observed at a higher temperature.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.189-190
• /
• 2021

Recently, the spread of intense social distancing and untact culture due to COVID-19 has increased the time spent indoors. In addition, according to the International Cancer Institute, fine dust was classified as a first-class carcinogen, a substance found to be carcinogenic, such as asbestos and benzene. As a result, interest in indoor air quality is increasing, and many studies are underway to reduce air pollutants. This study is a basic experiment of a board made to improve indoor air quality. The basic characteristics of the board, flexural strength and compressive strength, are analyzed and the results of the test are as follows. Experiments have shown that flexural strength and compressive strength tend to decrease as the replacement rate of hydrocarbons increases. It is believed that the strength of the sludge has decreased due to the increase in internal voids due to the increase in non-surface area, volume and diameter of microfiber as it undergoes the carbonation process. In addition, it is believed that the amount of moisture needed for curing during the mixing process was reduced due to the absorption of hydrocarbons.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.2
• /
• pp.226-234
• /
• 2017

The physical properties of lightweight foamed concrete mixed with EPS waste and flame resistant EPS waste were investigated. For this purpose, the main variables considered were a cement content of 300 and $400kgf/m^3$ and an EPS replacement ratio of 0, 10, 20, 30, and 40% by the volume ratio of the foam. The water-cement ratio and the dilution concentration were fixed to 0.5 and 10% respectively. The test results showed that the apparent density meets degrees 0.5 and 0.6 of KS F4039, and they showed little difference between the two mixes of Type A and Type B, regardless of the unit cement content. The bending strength obtained through the compressive strength also met the degree of KS F 4039. The thermal conductivity was 1~3% higher for the mixes of EPS than the case of flame resistant EPS, but both mixes met the 0.4 degree of KS F4039. The absorption ratio showed the values above 20% with a 1~3% difference for the two mixes, which mean further studies will be needed to reduce the absorption ratio.