• Journal of Fisheries and Marine Sciences Education
• /
• v.10 no.2
• /
• pp.226-238
• /
• 1998

With the advent of high speed and high output diesel engines, cavitation erosion-corrosion of wet cylinder liners is one of the most prevalent types of failure. The cavitation erosion-corrosion at cylinder liners in water cooled diesel engines is considered to be to the collapse of cavitation bubbles attributed to the cylinder liner vibration. To suppress cavitation damage in cylinder liner, the addition of an inhibitor would be more general method and innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. In this study, photomicrographs from vibratory facility cavitation specimens and from an eroded liner of a field diesel engine are compared. The behavior of cavitation bubbles grown in fluid is observed under vibration conditions by taking direct photographs with high speed camera. In order to determine the contributions of pure cavitation erosion and of pure corrosion to the total cavitation damage are be studied by following an experimental programme which includes three types of test: (1)pure cavitation erosion test, (2)pure corrosion test, and (1)cavitation erosion-corrosion test. Also cavitation damage under vibratory cavitation is reduced by using flow in tap water.

• Corrosion Science and Technology
• /
• v.19 no.6
• /
• pp.318-325
• /
• 2020

Generally, Al alloys of 5000 and 6000 series show excellent weldability, workability, and specific strength, and are widely used in ship building. A combined experiment via cavitation erosion and corrosion damage involving 6061-T6 Al alloy was performed using potentiodynamic polarization under cavitation erosion (hybrid experiments) with amplitude (cavitation strength). The corrosion current density was approximately 52-fold higher at 30 μm than under static conditions, suggesting that the amplitude greatly affected the damage. The degree of damage increased with increasing cavitation amplitude. After the hybrid experiment, the corrosion rate was compared according to the weight loss and damage depth, and the relationship between the two values was expressed as alpha value. The alpha (α) values at amplitudes of 5 μm, 10 μm and 30 μm were 5.11, 12.81 and 8.74, respectively, suggesting that the α value at 10 μm was greater than at 5 μm, and indicating local corrosion damage. However, the α value at 30 μm was smaller than that of 10 μm, which is attributed to higher damage via uniform corrosion than damage induced by local corrosion.

• Corrosion Science and Technology
• /
• v.14 no.5
• /
• pp.239-246
• /
• 2015

Stainless steel is generally known to have characteristics of excellent corrosion resistance and durability, but in a marine environment it can suffer from localized corrosion due to the breakdown of passivity film due to chloride ion in seawater. Furthermore, the damage behaviors are sped up under a cavitation environment because of complex damage from electrochemical corrosion and cavitation-erosion. In this study the characteristics of electrochemical corrosion and cavitation erosion behavior were evaluated on 16.7Cr-10Ni-2Mo stainless steel under a cavitation environment in natural seawater. The electrochemical experiments have been conducted at both static conditions and dynamic conditions inducing cavitation with different current density parameters. The surface morphology and damage behaviors were compared after the experiment. After the cavitation test with time variables morphological examinations on damaged specimens were analyzed by using a scanning electron microscope and a 3D microscope. the galvanostatic experiment gave a cleaner surface morphology presented with less damage depth at high current density regions. It is due to the effect of water cavitation peening under the cavitation condition. In the cavitation experiment, with amplitude of $30{\mu}m$ and seawater temperature of $25^{\circ}C$, weight loss and cavitation-erosion damage depth were dramatically increased after 5 hours inducing cavitation.

• Corrosion Science and Technology
• /
• v.19 no.5
• /
• pp.239-249
• /
• 2020

The characteristics of cavitation-erosion damage with changes in the amplitude of 5052-O aluminum alloy for ships were investigated in a seawater environment. In the cavitation-erosion experiment, the cavitation environment was created using a vibration-generating device with a piezo-electric effect. The amplitudes of 5 ㎛, 10 ㎛, and 30 ㎛ were created by changing the geometric shape of the cavitation horn. The resistance characteristics of cavitation-erosion damage were evaluated by weight loss and pitting area. The damaged surface was analyzed using scanning electron microscopy (SEM) and 3D optical microscopy. As the amplitude increased, the amount of damage and the area of the damaged surface increased, and the damage was concentrated at the center and edge of the specimen. The pit was created after the initial incubation period with increasing experimental time, and then the pits were merged to grow and propagate into craters, and eventually, the surface was detached and damaged. The cavitation-erosion damage after 30 minutes with amplitude of 10 ㎛ and 30 ㎛ was 1.48 and 2.21 times compared to 5 ㎛, respectively.

• Corrosion Science and Technology
• /
• v.12 no.5
• /
• pp.239-244
• /
• 2013

Marine equipment exposed to harsh environments requires not only excellent corrosion resistance but also improvement of physical characteristics against natural material degradation. With growing interests in ocean energy resources, the higher reliability for marine equipment has become more important in terms of material characteristics. ALBC3 alloy represents excellent corrosion resistance and is widely used in corrosive environments. However, cavitation damage occurs frequently due to its poor durability in high flow rate of marine environment. In this research, shot peening technology was employed as a surface modification with shot peening stand-off distance to mitigate cavitation damage. The effects of shot peening on extent of cavitation damage and weight loss were evaluated for both shot peened and non-peened specimens. The results revealed that the application of shot peeing decreased cavitation damage for all experimental conditions in comparison with the non-peened specimens. The optimum stand-off distance was determined to be 10 cm, since more than 35 % of cavitation damage reduction was observed.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.33 no.3
• /
• pp.202-208
• /
• 1997

The component materials threatened by cavitation include ship propellers as well as turbine runners, pump impellers, pipe lines and radiators. Today it is known that cavitation damage takes place on many other components including on the coding water side of the cylinder liners of diesel engines. Cavitation erosion - corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. To suppress cavitation erosion as well as cavitation erosion - corrosion to hydraulic equipment, innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. In this study, we investigated that the cavitation erosion - corrosion damage under vibratory cavitation can be reduced by adding of side now velocity to the cavitation bubble group in order to eliminate bubbles formed in sea water environment.

• Corrosion Science and Technology
• /
• v.19 no.5
• /
• pp.250-258
• /
• 2020

Recently, 5000 series and 6000 series Al alloys have been used as hull materials for small and medium-sized ships because of their excellent weldability, corrosion resistance, and durability in marine environments. Al ships can navigate at high speed due to their light weight. However, cavitation-erosion problems cause reducing durability of Al ship at high speed. In this investigation, 5052-O, 5083-H321, and 6061-T6 Al alloy materials were used to evaluate the damage characteristics with amplitude (cavitation strength). As a result of the electrochemical experiments, the corrosion current density and corrosion potential of 6061-T6 in seawater were 8.52 × 10-7 A/㎠ and -0.771 V, respectively, presenting the best corrosion resistance. The cavitation-erosion experiment showed that 5052-O had the lowest hardness value and cavitation-erosion resistance. 5052-O also had a very short incubation period. As the experiment progressed for 5052-O, pitting formed and grew in a short time, and was observed as severe cavitation-erosion damage that eliminated in large quantities. Among the three specimens, 5083-H321 presented the highest hardness value and the damage rate was the smallest after the initiation of pitting.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.32-39
• /
• 2016

In this study, Al and Zn arc thermal spray coatings were carried out onto the substrate of SS400 steel to improve corrosion resistance and durability of hull structural steel for ship in marine environment. Therefore cavitation-erosion test was conducted to evaluate the durability of painted and thermal spray coated specimens. And then the damaged surface morphology and weight loss were obtained to compare with each other, respectively. As a result, the painted specimen was the poorest cavitation resistance characteristics because surface damage behavior appeared to be exfoliated in bulk shape during the cavitation experiment. And Zn thermal spray coating layer presented the significant surface damage depth due to relatively low surface hardness and local cavitation damage tendency. On the other hand, as a result of the weight loss analysis, the painting layer presented the poorest cavitation resistance and the Al thermal spray coating layer relatively showed the best results after cavitation experiment.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.6
• /
• pp.264-271
• /
• 2012

Due to the good corrosion resistance and machinability, copper alloy is commonly employed for shipbuilding, hydroelectric power and tidal power industries. The Cu alloy, however, has poor durability, and the seawater application at fast flow condition becomes vulnerable to cavitation damage leading to economic loss and risking safety. The HVOF(High Velocity Oxygen Fuel) thermal spray coating with WC-10Co4Cr were therefore introduced as a replacement for chromium or ceramic to minimize the cavitation damage and secure durablility under high-velocity and high-pressure fluid flow. Cavitation test was conducted in seawater at $15^{\circ}C$ and $25^{\circ}C$ with an amplitude of $30{\mu}m$ on HVOF WC-10Co4Cr coatings produced by thermal spray. The cavitation at $15^{\circ}C$ and $25^{\circ}C$ exposed the substrate in 12.5 hours and in 10 hours, respectively. Starting from 5 hours of cavitation, the coating layer continued to show damage by higher than 160% over time when the temperature of seawater was elevated from $15^{\circ}C$ to $25^{\circ}C$. Under cavitation environment, although WC-10Co4Cr has good wear resistance and durability, increase in temperature may accelerate the damage rate of the coating layer mainly due to cavitation damage.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.32 no.3
• /
• pp.302-309
• /
• 1996

Cavitation erosion-corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. If the liquids corrosive to the material, a condition typically encountered in industry, the component materials may suffer serious damage by a combination of mechanical and electrochemical attack. To suppress cavitation erosion as well as cavitation erosion-corrosion to hydraulic equipments, innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. This study was tested by using the piezoelectric vibrator with 20kHz, 24${\mu}$m for cavitation generation. And also, the vibratory cavitation erosion-corrosion tests on commercial mild steel SS41were carried out. We carefully observed the erosion pattern and surface photography. The geometrical mechanism of pit growth, which is to be likely these processing; shallow typelongrightarrowundercut typelongrightarrowwide shallow type.