• Journal of the Korea Institute of Building Construction
• /
• v.4 no.1
• /
• pp.119-126
• /
• 2004

Generally, reinforced concrete is one of the most commonly used structural materials and it prevents corrosion of steel bar by high pH of interior, But, as time elapsed, reinforced concrete structure become deteriorated by many of combined deterioration factors and environmental conditions. And, there are large number of deteriorate mechanism of the reinforced concrete structure and it acts complexly. It is recognized that steel bar corrosion is the main distress behind the present concern regarding concrete durability. In this study, to institute combined deterioration environments, established acceleration condition and cycle for combined deterioration environments has a resemblance to environments which are real structures placed. After that to confirm corrosion properties of reinforced concrete due to permeability with covering depth and types of surface cover under combined deterioration environments, measured carbonation velocity coefficients, chloride ion diffusion coefficients, water absorption coefficients, air permeability coefficients and electric potential, corrosion area ratio, weight reduction, corrosion velocity of steel bar. The results showed that an increase in age also decrease carbonation velocity coefficients, increase Chloride ion diffusion coefficients and increases water absorption coefficients. As well, an increase in age also increases corrosion of steel bar. Data on the development of corrosion velocity of steel bar with types of surface cover made with none, organic B, organic A, inorganic B, and inorganic A is shown. As well, permeability and corrosion velocity of steel bar with covering depth is superior to 10mm than 20mm. And it is confirmed permeability and corrosion properties of steel bar are closely related.

• Journal of Korean Society of Coastal and Ocean Engineers
• /
• v.20 no.6
• /
• pp.575-582
• /
• 2008

Carbonation is one of major factors influencing on the durability of concrete structure. This paper investigates the effect of carbonation on the soundness of harbor concrete structure and quantifies the influence of carbonation based on in-situation data tested at 369 points in 69 harbor facilities. The relationships between carbonation depth and cover depth, and between carbonation depth and compressive strength are studied and the failure probability of durability, that is the initiation probability of steel corrosion, is evaluated on the basis of reliability concept. The in-situation test results showed that the ratio of carbonation depth to cover depth was less than 0.2, and the carbonation depth increased with age. In most cases, the failure probability of durability by carbonation was less than 10%. Therefore, it can be concluded that the influence of carbonation on the durability of harbor concrete structure is smaller than other factors deteriorating the durability of harbor concrete structure.

• Corrosion Science and Technology
• /
• v.4 no.2
• /
• pp.69-74
• /
• 2005

The carbonation of concrete is one of the major factors that cause durability problems in concrete structures. The rate of carbonation depends largely upon the diffusivity of carbon dioxide in concrete. The purpose of this study is to identify the diffusion coefficients of carbon dioxide for various concrete mixtures. To this end, several series of tests have been planned and conducted. The test results indicate that the diffusion coefficient increases with the increase of water-cement ratio. The diffusion coefficient decreases with the increase of relative humidity at the same water-cement ratio. The diffusion of carbon dioxide reached the steady state within about five hours after exposure. The content of aggregates also influences the diffusivity of carbon dioxide in concrete. It was found that the diffusion coefficient of cement paste is larger then that of concrete or mortar. The quantitative values of diffusivity of carbon dioxide in this study will allow more realistic assessment of carbonation depth in concrete structures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.4
• /
• pp.111-118
• /
• 2010

Reinforced steel corrosion due to concrete carbonation is one of main factors on the durability of RC structure. The carbonation velocity have an effect on carbon dioxide density, concrete quality and structural shape. Specially, these problems have increased in urban area. This study investigates the carbonation status of the bridges and quantifies the effect of carbonation based on various domestic field data. The failure probability of durability is evaluated on the basis of reliability concept. According to experimental results of the carbonation depth, the carbonation depth increased with structural age and carbonation velocity decreased with high strength of concrete. In most cases, the failure probability of durability by carbonation was more than 10%. Also, The results requires the minimum cover thickness of 70-80mm for target safety index(${\beta}$=1.3) proposed by Korean concrete specification.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.479-482
• /
• 2005

The galvanic currents between carbon steel and Cr-bearing rebars have been studied in concrete subjected to carbonation and chloride attack. The results revealed that in case of SD345 contacted with Cr-bearing rebar in concrete under chloride attack environment and carbonation environment, the corrosion acceleration by galvanic corrosion is not generated. Therefore, Cr-bearing rebar can be used together with the carbon steel in the new establishment structure.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.3
• /
• pp.115-122
• /
• 2006

Ten types of steel bars having different Cr contents were embedded in concretes with chloride ion contents of 0.3, 0.6, 1.2, and $2.4kg/m^3$ to fabricate specimens assuming such deteriorative environments. After being carbonated to the reinforcement level, these concretes were subjected to corrosion-accelerating cycles of heating/cooling and drying/wetting. The time-related changes in the corrosion area and corrosion loss of the Cr-bearing rebars were then measured to investigate their corrosion resistance. The results revealed that in a deteriorative environment prone to both carbonation and chloride attack, corrosion resistance was evident with a Cr content of 7% or more and 9% or more in concretes with chloride ion contents of 1.2 and $2.4kg/m^3$, respectively.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.10a
• /
• pp.41-42
• /
• 2016

As the importance of maintenance of reinforced concrete structure recently has emerged, the attention of durability of structure has been increasing. There are many studies about durability decline especially due to the carbonation. In order to study carbonation progress after surface repair of carbonated concrete, each carbonation penetration velocity from different repair materials of concrete structure is compared through the experiment of carbonation accelerating CO₂ concentration to 20% and 100%. As carbonation infiltration progress is predicted through this study, the counterplan of service life evaluation will be prepared on selection of repair materials of concrete structure.

• Computers and Concrete
• /
• v.26 no.6
• /
• pp.497-504
• /
• 2020

Concrete can lose its alkalinity by concrete carbonation causing steel corrosion. Thus, the determination of the carbonation depth is necessary. An empirical model is proposed in this research to predict the carbonation depth of concrete using Gene expression programming (GEP). The GEP model was trained and validated using a large and reliable database collected from the literature. The model was developed using the six parameters that predominantly control the carbonation depth of concrete including carbon dioxide CO2 concentration, relative humidity, water-to-cement ratio, maximum aggregate size, aggregate to binder ratio and carbonation period. The model was statistically evaluated and then compared to the Jiang et al. model. A parametric study was finally performed to check the proposed GEP model's sensitivity to the selected input parameters.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.2
• /
• pp.157-166
• /
• 2017

In general, carbonation and chlorine ions are the most harmful causes of deterioration of concrete structures. Recently, a method has been developed to control the corrosion of rebar in concrete containing chloride by impregnating a Surface coating material with a inhibitor. In this study, accelerated carbonation and differential thermogravimetric analysis (TG-DTA) and CASS tests were carried out to evaluate the characteristics of Surface coatings containing Organic Corrosion inhibitors which are excellent in corrosion inhibition and fix degradation causes $CO_2$ and $Cl^-$. As a result of the experiment, TG-DTA analysis and accelerated carbonation showed that $CO_2$ was directly reacted with amine derivative in concrete by the incorporation of Organic Corrosion inhibitor. In other words, $CO_2$ was immobilized and carbonation inhibition effect was confirmed. In addition, in the CASS test, the specimen coated with the Surface coating material containing the Organic Corrosion inhibitor with $Cl^-$ fixing property showed no corrosion until the 28th day and had excellent performance in preventing corrosion of a rebar by the chloride ion.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.721-726
• /
• 2003

The Durability of Concrete Structure is serverely degraded due to mainly carbonation, sulfate attack and chloride ion diffusion in concrete. The ultimate purpose of this study is to obtain how much the durability of Concrete Structure is improved according to the variation of physical properties in concrete or the frequency of surface coating on concrete. Where, variation of physical properties is a water-cement ratio or amount of air. The experiments are the chliride ion diffusion test, the lapid corrosion test, the lapid carbonation test, the test on resistance to freezing and thawing. Finally, this study shows that the effect by the surface coating method is better than the variation of physical properties in concrete.