• 열처리공학회지
• /
• 제36권4호
• /
• pp.206-214
• /
• 2023

Tungsten carbide has many industrial applications due to its high electrical and thermal conductivity, high melting temperature, high hardness and good chemical stability. Because tungsten carbide is difficult to sinter, it is sintered with nickel or cobalt as a binder and is currently used in nozzles, cutting tools, and molds. Alumina is reported to be a viable binder for tungsten carbide due to its higher oxidation resistance and lower cost than nickel and cobalt. The ultrafine tungsten carbide-graphene-alumina composites were rapidly sintered in a high frequency induction heating active sintering unit. The microstructure and mechanical properties (fracture toughness and hardness) of the composites were investigated and analyzed by Vickers hardness tester and electron microscope. Since the high-frequency induction heating sintering method enables high-speed sintering, ultrafine composites can be prepared by preventing grain growth. In the tungsten carbide-graphene-alumina composites, the grain size of tungsten carbide increased with the amount of alumina participation. The hardness and fracture toughness of the tungsten carbide-5% graphene- x% alumina (x = 0, 5, 10,15) composites were 5.1, 8.6, 8.6, and 8.4 MPa-m^1/2 and 2384, 2168, 2165, and 2102 kg/mm², respectively. The fracture toughness increased without a significant decrease in hardness. Sinterability was improved by adding alumina to tungsten carbide-graphene.

• 소성∙가공
• /
• 제19권3호
• /
• pp.191-196
• /
• 2010

Tungsten-carbide as typical difficult-to-cut material has excellent mechanical properties such as high thermal resistivity, mechanical strength and chemical durability. However, it is next to impossible for tungsten-carbide to be fabricated the needed parts by cutting process. In this study, for establishing the micro fabrication method of tungsten-carbide for micro injection or compression molding core, the investigation on micro cutting characteristics of tungsten-carbide green part which is made by powder injection molding process and easy to cut relatively was performed. For this, micro endmilling experiments of tungsten-carbide green part were performed according to various cutting conditions. Finally, the wear trend of micro endmill and the appearance of micro rib according to feed-rate and cutting depth per step were analyzed through SEM images of micro cutting feature and microscope images of micro tools.

• 연구논문집
• /
• 통권26호
• /
• pp.95-102
• /
• 1996

The carbide growth behavior of MAR-M247 LC alloy was investigated by directional solidification and quench method. The carbide volume fraction, trapping and growth behavior were correlated with the growth rate. It was found that the carbide volume fraction decreases at slower growth rate. This decreasing was caused by lower solid-liquid interface trapping ability at the slower growth rate.

• 한국재료학회지
• /
• 제13권6호
• /
• pp.381-388
• /
• 2003

Directional solidification experiments were carried out at 0.5-150 $\mu\textrm{m}$/s in the Co-base superalloy ECY 768. As increasing solidification rate, the dendrite length increased and it reached the maximum at 150 $\mu\textrm{m}$/s, where the tip temperature is close to the liquidus. The liquidus and eutectic temperatures could be estimated by comparing the dendrite lengths and the temperature gradients at the solid/liquid interface and those were estimated as $1424.6^{\circ}C$ and $1343^{\circ}C$ respectively. Between the dendrites just below final freezing temperature, MC carbide and $M_{23}$$C_{6}$ carbide were found. It was confirmed that the script or blocky shape was Ta or W-rich MC carbide, and the lamellar shape was Cr-rich eutectic carbide. The solid/liquid interface morphology clearly showed that the Cr-rich eutectic carbide formed just after the script type MC carbide.

• 대한금속재료학회지
• /
• 제48권7호
• /
• pp.589-597
• /
• 2010

In the present study, the effect of variation in alloying elements on the carbide formation behavior during casting and homogenization treatment of M2 high speed steels was investigated. M2 high speed steels of various compositions were produced by vacuum induction melting. Contents of C, Cr, W, Mo, and V were varied from the basic composition of 0.8C, 0.3Si, 0.2Mn, 4.0Cr, 6.0W, 5.0Mo, and 2.0V in weight percent. Homogenization treatment at $1150^{\circ}C$ for 1.5 hr followed by furnace cooling was performed on the ingots. Area fraction and chemical compositions of eutectic carbide in as-cast and homogenized ingots were analyzed. Area fraction of eutectic carbide appeared to be higher in the ingots with higher contents of alloying elements the area fraction of eutectic carbide also appeared to be higher on the surface regions than in the center regions of ingots. As a result of the homogenization treatment, $M_2C$ carbide, which was the primary eutectic carbide in the as-cast ingots, decomposed into thermodynamically stable carbides, MC and $M_6C$. The latter carbide was found to be the main one after homogenization. Fine carbides uniformly distributed in the matrix was found to be MC type carbide and coarsened by homogenization.

• 한국분말재료학회지
• /
• 제21권2호
• /
• pp.93-96
• /
• 2014

Cobalt coated tungsten carbide-cobalt composite powder has been prepared through wet chemical reduction method. The cobalt sulfate solution was converted to the cobalt chloride then the cobalt hydroxide. The tungsten carbide powders were added in to the cobalt hydroxide, the cobalt hydroxide was reduced and coated over tungsten carbide powder using hypo-phosphorous acid. Both the cobalt and the tungsten carbide phase peaks were evident in the tungsten carbide-cobalt composite powder by X-ray diffraction. The average particle size measured via scanning electron microscope, particle size analysis was around 380 nm and the thickness of coated cobalt was determined to be 30~40 nm by transmission electron microscopy.

• 한국결정성장학회지
• /
• 제20권2호
• /
• pp.80-84
• /
• 2010

The temperature-programmed reduction of titanium oxide ($TiO_2$) with pure $CH_4$ was used for the preparation of titanium carbide crystallites. The synthesized materials had the different surface areas, indicating that the structural properties of these materials were strong functions of two different heating rates and space velocity employed. The titanium carbide crystallites were active for $NH_3$ decomposition. Since the reactivity varied with changes in the particle size, ammonia decomposition reactivity over the titanium carbides crystallites appeared to be related to the different active species. The reactivities of titanium carbide crystallites were two and three times lower than those of the vanadium and molybdenum carbide crystallites, respectively. These results suggested that the difference in activities might be related to the degree of electron transfer between metals and carbon.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.139-139
• /
• 2010

Rhenium-Iridium(Re-Ir) thin films were deposited onto the tungsten carbide(WC) molding core by sputtering system. The Re-Ir thin films on tungsten carbide molding core were analyzed by scanning electron microscope(SEM) and surface roughness. The Re-Ir coating technique has been intensive efforts in the field of coating process because the coating technique and process have been their feature, like hardness, high elasticity, adrasion resistance and mechanical stability and also have been applied widely the industrial and biomedical areas. In this report, tungsten carbide(WC) molding core was manufactures using high performance precision machining and the efforts of Re-Ir coating on the surface roughness.

• 한국세라믹학회지
• /
• 제17권3호
• /
• pp.145-150
• /
• 1980

This paper deals with the clay-bonded silicon carbide refractory saggars in terms of its oxidation resistance. Oxidation is one of the major causes of failure in silicon carbide refractory saggars during its services. Various anti-oxidation additives are coated on or added into silicon carbide refractories and their effects are studied while other conditions are equal. Several conclusions can be derived for optimum anti-oxidation additive as: 1. The additive should wet each silicon carbide grain completely during its firing. 2. The additive should have high viscosity at temperatures around $1, 350^{\circ}C$ where most silicon carbide refractory saggars are being used. 3. The additive should have ability to absorb or desorb oxygen depending on the local atmosphere inside of saggar during it service. 4. The addition should be kept as minimum as possible to prevent any "sweating" or "bloating" phenomena.ing" phenomena.mena.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 추계학술대회논문집
• /
• pp.36-39
• /
• 2004

Glass molding is an advantageous method to manufacture glass micro optical components. However, it is difficult to make Tungsten Carbide core for glass microlens array. We have developed novel method to fabricate Tungsten Carbide core for micro glass components using pressure forming. Silicon masters were fabricated by micro machining. Tungsten Carbide core was fabricated by pressure forming and sintering. And we made high quality surface of Tungsten Carbide core by using the magnetic-field-assisted polishing process.