• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.234-240
• /
• 2003

Hardened cement pastes of OPC which contains 10 wt% CSA type expansive additives were immersed in aqueous solution of 10 wt% MgS $O_4$.7$H_2O$ and then investigated by compressive strength, XRD. SEM and DSC etc.. According to the results including the hydration products and the microstructure of the hardened paste, the case of CSA type expansive additives［No. 6(C/(equation omitted) : 2.29, A/(equation omitted) : 0.16)] prepared from raw materials increased the resistance to $Mg^{2＋}$, S $O_4$$^{2-}$ ion diffusion than that of OPC paste due to the densification by the formation of fine ettringite in the first stage and the hydrates according to $\beta$-C$_2$S hydration in the late period.

• Geomechanics and Engineering
• /
• v.25 no.1
• /
• pp.41-48
• /
• 2021

In cold regions, the integrity of the infrastructures built on weak soils can be extensively damaged by weathering actions due to the cyclic freezing and thawing. This damage can be mitigated by exploiting soil stabilization techniques. Generally, ordinary Portland cement (OPC) is the most commonly used binding material for investigating the chemo-hydromechanical behavior. However, due to the environmental issue of OPC producing a significant amount of carbon dioxide emission, calcium sulfoaluminate (CSA) cement can be used as one of the eco-sustainable alternatives. Although recently several studies have examined the strength development of CSA treated sand, no research has been concerned about CSA cement-stabilized sand affected by cyclic freeze and thaw. This study aims to conduct a comprehensive laboratory work to assess the effect of the cyclic freeze-thaw action on strength and durability of CSA cement-treated sand. For this purpose, unconfined compressive strength (UCS) and ultrasonic pulse velocity (UPV) tests were performed on the stabilized soil specimens cured for 7 and 14 days which are subjected to 0, 1, 3, 5, and 7 freeze-thaw cycles. The test results show that the strength and durability index of the samples decrease with the increase of the freeze-thaw cycles. The loss of the strength and durability considerably decreases for all soil samples subjected to the freeze-thaw cycles. Overall, the use of CSA as a stabilizer for sandy soils would be an eco-friendly option to achieve sufficient strength and durability against the freeze-thaw action in cold regions.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.859-866
• /
• 2003

When calcium sulfoaluminate-based expansive cement was hydrated, ettringite and monosulfate were mainly formed. The crack of hardened cement was prevented by compensating drying shrinkage due to formation of the above hydrates. In order to study the hydration properties of calcium sulfoaluminate-based expanding cement, 3CaOㆍ3Al$_2$O$_3$ㆍCaSO$_4$(C$_4$A$_3$S) was prepared by chemical synthesis, and then the hydration of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.$2H_2O$-C$_3$A system_was characterized. Good $C_4$A$_3$S phase was prepared at $1300^{\circ}C$ by chemical synthesis, and the main hydration product of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.2$H_2O$ system was ettringite. In the case of hydration $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$ㆍ 2$H_2O$-C$_3$A system, ettringite was formed in the early period and it was transformed into monosulfate while consumed gypsum.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.483-489
• /
• 2005

For the raw materials of 3CaO$\cdot$3Al$_{2}$O$_{3}$ $\cdot$CaSO$_{4}$(CSA) clinker manufacturing, the applications of industrial wastes such as waste shell, spent oil-refining catalyst and desulfurized gypsum were examined. The c1inkerbility of the raw mix and the behaviour of formation of clinker minerals were studied and then some hydraulic properties of cements containing the clinker were also investigated. By virtue of the high reactivity of thermally decomposed raw materials, CSA clinkers were obtained at relatively low temperature of 1250$^{\circ}C$ and thus oil-refining catalysts were more desirable than aluminium hydroxide as an aluminous raw material. The expansive cement samples showed somewhat lower flow value than that of OPC, but their compressive strengths were developed earlier and higher than that of OPC due to formation of ettringite in the early hydration time, which indicated the possibility of practical use of low-cost CSA clinker using industrial wastes only.

• Journal of Environmental Science International
• /
• v.29 no.6
• /
• pp.605-612
• /
• 2020

To improve the initial strength and stability of lightweight-foamed concrete, which shows suitable sound absorption and insulation characteristics, the effect of CO₂-reduced cement on the properties of the concrete was investigated. Various mixing ratios were applied by substituting a certain amount of slag and Calcium Sulfo Aluminate (CSA) in CO₂-reduced Ordinary Portland Cement (OPC) and the physical properties of the samples were examined using the Korean Standard. The kiln temperatures of the CSA were 100-200℃ ; these values are lower than those of OPC and can lead to energy saving. In addition, the low limestone content reduces greenhouse gas emissions by 20 %. Adding a small amount of CSA in OPC content activates Ca-Al-H₂-based hydrates, and the initial compressive strength of the concrete is improved. As the CSA content increased, the thermal conductivity of the concrete decreased by up to 8% compared to plain concrete, thus indicating an improvement in its insulation. Therefore, the settlement stability was improved as the addition of CSA shortened the setting time.

• Journal of the Korean GEO-environmental Society
• /
• v.13 no.2
• /
• pp.59-65
• /
• 2012

Solidification/Stabilization(S/S) is one of the remediation technologies that have been applied for treating inorganic hazardous wastes. This study investigated the reduction of arsenic concentration of arsenic-contaminated soil using by S/S. The binder plays a role in controlling the mobility and solubility of the contaminants in S/S process, so it is important to determine the optimum binder content. Therefore, this study evaluated the effectiveness of S/S using four different binders(cement, zero valent iron, and monosulfate and ettringite(cement-based synthesized materials) at the binder content ranged between 5%(wt.) and 20%(wt.). The leachability of arsenic in 1 N HCl was different depending on the types of binders: cement(71.41%) > monosulfate(47.45%) > ettringite(46.36%) > ZVI(33.08%) at the binder content of 20%. Additionally, three kinds of a mixture binder were prepared using cement and additives(monosulfate, ettringite, calcium sulfoaluminate(CSA)) and tested for arsenic reduction. The highest arsenic removal capacity was found at the mass ratio of cement to the additive, 4:1 in all experiments using a mixture binder, regardless of the additives types. A mixture binder(cement and additives) resulted in higher arsenic removal relative to the arsenic removal when cement was used alone.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.388-394
• /
• 2000

The C4A3S clinker was prepared by the solid-state reaction. The mixture of raw materials; calcite, kaoline and gypsum, was fired at 135$0^{\circ}C$ for 1hr and cooled rapidly in air. C4A3S type expansive was made with C4A3S clinker, CaO and CaSO4. The cement replaced by 10 wt.% C4A3S type expansive was investigated by the measurement of the strength(compressive, tensile, flexural) and length change at various curing conditions. Hydration products were mainly ettringite, monosulfate and Ca(OH)2. The densification and the expansion due to the formation of ettringite during the hydration increased strength and reduced the drying shrinkage of hardened cement.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.12-20
• /
• 2017

This report presents the results of an investigation on the fundamental properties of mortars high fluidity high volume slag cement(HVSC) activated with sodium silicate($Na_2SiO_3$). The ordinary Portland cement(OPC) was replaced by ground granulated blast furnace slag(GGBFS) from 40% to 80% and calcium sulfoaluminate(CSA) was 2.5% or 5.0% mass. The $Na_2SiO_3$ was added at 2% and 4% by total binder(OPC+GGBFS+CSA) weight. A constant water-to-binder ratio(w/b)=0.35 was used for all mixtures. The research carried out the mini slump, V-funnel, setting time, compressive strength and drying shrinkage. The experimental results showed that the contents of superplasticizer, V-funnel, setting time and drying shrinkage increased as the contents of CSA and $Na_2SiO_3$ increase. The compressive strength increases with and an increase in CSA and $Na_2SiO_3$. One of the major reason for these results is the accelerated reactivity of GGBFS with CSA and $Na_2SiO_3$. The maximum performance was CSA 5.0% + $Na_2SiO_3$ 4% specimens.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.74-82
• /
• 2017

This research presents the results of the strength and drying shrinkage properties to study the effect of ground granulated blast furnace slag(GGBFS), fly ash(FA) and calcium sulfoaluminate(CSA) for activated ternary blended slag cement. The activated ternary blended cement(ATBC) mortar were prepared having a constant water-cementitious materials ratios of 0.4. The GGBFS contents ratios of 100%, 80%, 70% and 60%, FA replacement ratios of 10%, 20%, 30% and 40%, CSA ratios of 0%, 10%, 20% and 30% were designed. The superplasticizer of polycarboxylate type were used. The activator was used of 10% sodium hydroxide(NaOH) + 10% sodium silicate($Na_2SiO_3$) by weight of binder. Test were conducted for mini slump, setting time, V-funnel, water absorption, compressive strength and drying shrinkage. According to the experimental results, the contents of superplasticizer, V-funnel and compressive strength increases with an increase in CSA contents for all mixtures. Moreover, the setting time, water absorption ratios and drying shrinkage ratio decrease with and increase in CSA. One of the major reason for the increase of strength and decrease of drying shrinkage is the accelerated reactivity of GGBFS with alkali activator and CSA. The CSA contents is the main parameter to explain the strength development and decreased drying shrinkage in the ATBC.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.561-568
• /
• 2022

In this study, the mechanical properties and self-healing performance of cement mortar containing clinker binder, calcium sulfoaluminate(CSA), and sodium sulfate(Na₂SO₄) were evaluated. The mechanical properties of cement mortar were investigated by measuring compressive strength and flexural strength, and the healing performance was evaluated through hydrostatic water permeability test and gas diffusion test. In addition, the healing products precipitated in the cracks were visually observed through an optical microscope and a scanning electron microscope(SEM). As a result, the incorporation of the clinker binder-based inorganic additives improved the initial and 28-day strength by about 20 %. Depending on the healing performance evaluation method, there was a difference in the healing rate, and the healing rate showed a tendency to be underestimated. Nevertheless, CaCO₃ was precipitated as the main healing product inside the 0.3 mm crack when the inorganic additives were mixed with cement mortar, improving the self-healing performance.