• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.1
• /
• pp.30-36
• /
• 2006

Fretting fatigue behavior of SCM420 steel commonly used in the automotive industry for structural applications was investigated in this study. In addition, the effect of bridge pad on the fretting fatigue test was evaluated from different pad materials and following conclusions were drawn. Simple fatigue limit of SCM 420 steel was determined to be 350 MPa while this value was 225 MPa and 285.5 MPa with SCM420H and with SM45C pad, respectively. Reduction in fatigue limit was, thus found to be 35.7% and 17.9% with SCM 420H pad and SM45C pad, respectively. Results of fracture surface observation revealed that typical striation pattern of fatigue failure existed as well as dimpled and cleavage frature appearance was found in final fractured region. From the EDS compositional analysis, test sample and pad part all had high signals for oxygen and iron, suggesting that worn particles might be iron oxide, although exact chemical composition has to be confirmed. Considerable reduction in fatigue life was apparent in SCM 420 steel under fretting fatigue against simple fatigue. Such reduced fatigue life by fretting damage should be considered as an important factor not only in the viewpoint of repairing but also inevitably in the design stage of structural components.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.1
• /
• pp.10-15
• /
• 2011

Recently, renewable energy sources such as wind turbine, solar cell are interested in preventing global warming which is caused by the consumption of fossil fuel. SCM440(H) and SNCM439 have been used in the major components of the wind turbine gear because of excellent mechanical properties. In the present study, the heat treated mechanical properties of SCM440(H) and SNCM439 with 150 mm diameter were compared with those with 25 mm diameter which is generally accepted material for structural application. Heat treated SCM440(H) showed better mechanical properties such as tensile strength, hardness and impact absorbed energy compared with those in SNCM439. Hardenss value between as-quenched and as-quenched followed by tempering showed big difference in SNCM439, however the difference in SCM440(H) was relatively small. Heat treated mechanical properties of the alloys with 25 mm diameter were more uniform value than those with 150 mm diameter.

• Transactions of Materials Processing
• /
• v.10 no.1
• /
• pp.35-41
• /
• 2001

The high temperature deformation behavior of SCM 440 can be characterized by the hot torsion test in the temperature ranges of $900^{\circ}C$~$1100^{\circ}C$ and strain rate ranges of 0.05/sec~5/sec. The aim of this paper is to establish the quantitative equation of the volume fraction of dynamic recrystallization (DRX) as a function of processing variables, such as strain rate ($\varepsilon$), temperature (T), and strain ('$\varepsilon$). During hot deformation, the evolution of microstructure could be analyzed from work hardening rate ($\theta$). For the exact prediction of dynamic softening mechanism the critical strain ($\varepsilon_c$), the strain for maximum softening rate ($\varepsilon^*$ and Avrami' exponent (m') were quantitatively expressed by dimensionless parameter, Z/A, respectively. The transformation-effective strain-temperature curve for DRX could be composed. It was found that the calculated results were agreed with the experimental data for the steel at any deformation conditions.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.12
• /
• pp.3899-3908
• /
• 1996

In order to clarify the effects of nonmetallic inclusion contents insteels (SM45C & SCM440) on the tool life, cutting experiment was performed under various cutting conditions. Tool life, cutting force, roughness of machined surface and cutting mechanism are examined on these two kinds of steel. The following conclusions were obtained from the analysis (1) Cutting force of the steels was not affected by chemical component and nonmetallic inclusion. (2) If the rate of amount, Ca/S has a value grater than about 0.2 and addition of less amount of Al, Mn, tool wear of tips decreasesinturning. (3) It is also proved that higher contents of nonmetallic inclusion improve roughness of the surface. (4) Less amount of Ca, higher amount of S, Mn and Al improve the chip breakability.

• Journal of the Korean Society of Safety
• /
• v.20 no.1 s.69
• /
• pp.18-23
• /
• 2005

This study deals with the friction and wear characteristics of C-N coated SCM415 steel. The PSII(plasma source ion implantation) apparatus was built and a SCM415 test piece with steel substrate was treated with carbon nitrogen by this apparatus. The composition and structure of the surface layer were analyzed and compared with that of PVD(physical vapor decomposition) coated TiN layer. It was found that both of friction coefficient of C-N coating and TiN coating decreased with increasing load, however, C-N coating showed relatively lower faction coefficient than that of TiN coating. The micro-vickers hardness of C-N film is 3200 Hv, which is $32\~43\%$ higher than that of TiN film. The critical load of C-N film is 52N, which is $25\%$ higher than that of TiN film. The hardness of C-N film fabricated by Plasma ion implantation is $61\~70\%$ higher than that of base material, and faction coefficient is $14\~50\%$ lower than that of base material. It is also interesting to note that the friction was changed from adhesive wear mode to light oxidizing wear mode.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.265-269
• /
• 2004

Plasma nitrocarburising and post oxidation were performed on SCM435 steel by a pulsed plasma ion nitriding system. Plasma oxidation resulted in the formation of a very thin ferritic oxide layer 1-2 $\mu\textrm{m}$ thick on top of a 15～25 $\mu\textrm{m}$ $\varepsilon$-F $e_{2-3}$(N,C) nitrocarburized compound layer. The growth rate of oxide layer increased with the treatment temperature and time. However, the oxide layer was easily spalled from the compound layer either for both oxidation temperatures above $450^{\circ}C$, or for oxidation time more than 2 hrs at oxidation temperature $400^{\circ}C$. It was confirmed that the relative amount of $Fe_2$$O_3$, compared with $e_3$$O_4$, increased rapidly with the oxidation temperature. The amounts of ${\gamma}$'-$Fe_4$(N,C) and $\theta$-$Fe_3$C, generated from dissociation from $\varepsilon$-$Fe_{2-3}$ /(N,C) phase during $O_2$ plasma sputtering, were also increased with the oxidation temperature.e.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.133-134
• /
• 2012

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.707-713
• /
• 1998

The influence of plasma carburizing process on the surface hardness of SCM415 low-alloy steel (0.15% C) was investigated under the various process conditions of gas composition. gas pressure, plasma current density. temperature and time. The effective case depth was found to depend on the amount of methan gas containing carbon. thus the deepest case depth and the uniform hardeness were obtained with the 100% methan gas. The case depth increased with the plasma current density. The effective plasma carburizing temperature of SCM415 steel was found to be higher than 85$0^{\circ}C$, and the case depth was proportional to the square root of carburizing time under the same current density. The bending fatigue strength of the plasma carburized specimen is' higher than those of as- received specimen or reheat-quenched specimen.

• Journal of Oral Medicine and Pain
• /
• v.25 no.1
• /
• pp.117-128
• /
• 2000

The present study explored the influence of temporomandibular disorders(TMD) with anterior open bite on swallowing. Fifteen subjects with anterior open bite(group A), 9 subjects with anterior open bite and TMD(group B), and 24 subjects without malocclusion or TMD symptoms (group C) were included. BioPAK system(Bioresearch Inc., Milwaukee, WI, USA) was used to record the muscle activities of anterior temporal, masseter, sternocleidomastoid(SCM) and anterior digastric muscles during maximum clenching and swallowing. Positional change of the mandible during swallowing was also recorded using the same system. The obtained results were as follows: 1. Group A, B, and C did not show significant differences each other in the muscle activity of resting position in most of head and neck muscles. 2. Group B showed significantly lower muscle activity in maximum clenching than group C in anterior temporal(p<0.01), masseter(p<0.05), SCM(p<0.05) and digastric muscles(p<0.05). 3. Group A showed significantly lower muscle activity during swallowing than group C in anterior temporal and masseter muscles(p<0.01). Group B showed significantly lower muscle activity during swallowing than group C in anterior temporal(p<0.01), masseter(p<0.01), and SCM muscles(p<0.05). 4. Group A and B showed increased positional change of the mandible during swallowing measured from vertical, anteroposterior and lateral aspects, and prolonged swallowing(p<0.05). 5. After given instructions for normal swallowing pattern, group A and B showed increased muscle activity during swallowing in anterior temporal, masseter and SCM muscles(p<0.01). Positional change of the mandible and time elapsed for swallowing also decreased after the instruction(p<0.01). 6. Occlusal splint did not change the muscle activity during swallowing. However, vertical change(p<0.01) and swallowing time(p<0.05) were decreased with splint.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.16 no.2
• /
• pp.44-49
• /
• 2017

In this study, the cutting conditions of moving speed, number of main axial revolutions, etc. are changed for the chrome molybdenum steel (SCM415) material and carbide ball end mill tool to study the changes for processing intensity in the cutting process. The results that confirm the intensity of the measured value of the specimen for SCM415 display the intensity with an average 1.0667 HrC. After the fact cutter, it was able to confirm the average intensity of 8.3815 HrC. In addition, the intensity value after image processing may determine the average intensity survey value of 5.8690 HrC and the different intensity values with image processing after face cutting are shown for an average of ${\pm}2.5125HrC$. The different value of intensity with the specimen and image processing is confirmed for an average of 4.8024 HrC. The results of comparing the intensity following the number of main axial revolutions and moving speed show that the intensity is highest for 3,000 rpm and F200, and lowest for 4,000 rpm and F200.