• 한국해양공학회지
• /
• 제1권2호
• /
• pp.123-129
• /
• 1987

Corrosion fatigue fracture of dual phase steel(SS41) and raw material steel(SS41) were investigated in 3.5% NaCl aqueous solution at PH 4,6,9 and 11. The fatigue limit of dual phase steel is increased approximately 1.8 times larger than that of raw material in air. The corrosion fatigue life of dual phase steel is about 5-10 times larger than that of raw material in 3.5% NaCl aqueous solution. The reduction of fatigue life is larger for the acidsalt solution than for the alkali salt solution. The reduction of stress level on the reduction ratio of corrosion fatigue life is large as pH 6-11. The reduction ratio of corrosion fatigue life of dual phase steel and raw material is nearly coincided at pH 2. While at pH4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. It has been found that the corrosion resistance effect of dual phase steel is smaller than that of raw material in corrosion fatigue crack propagation rate. As pH below 6 is changed, it can be clearly observed from raw material that the brittle intergranular fracture is characterized, and from the above result, the influence of corrosion of dual phase steel is small.

• 한국재료학회지
• /
• 제23권11호
• /
• pp.649-654
• /
• 2013

The effect of interstitial elements on the ductile-brittle transition behavior of austenitic Fe-18Cr-10Mn-2Ni alloys with different nitrogen and carbon contents was investigated in this study. All the alloys exhibited ductile-brittle transition behavior because of unusual low-temperature brittle fracture, even though they have a faced-centered cubic structure. With the same interstitial content, the combined addition of nitrogen and carbon, compared to the sole addition of nitrogen, improved the low-temperature toughness and thus decreased the ductile-brittle transition temperature (DBTT) because this combined addition effectively enhances the metallic component of the interatomic bonds and is accompanied by good plasticity and toughness due to the increased free electron concentration. The increase in carbon content or of the carbon-to-nitrogen ratio, however, could increase the DBTT since either of these causes the occurrence of intergranular fracture that lead to the deterioration of the toughness at low temperatures. The secondary ion mass spectroscopy analysis results for the observation of carbon and nitrogen distributions confirms that the carbon and nitrogen atoms were significantly segregated to the austenite grain boundaries and then caused grain boundary embrittlement. In order to successfully develop austenitic Fe-Cr-Mn alloys for low-temperature application, therefore, more systematic study is required to determine the optimum content and ratio of carbon and nitrogen in terms of free electron concentration and grain boundary embrittlement.

• 열처리공학회지
• /
• 제28권1호
• /
• pp.1-6
• /
• 2015

The ductile-to-brittle transition behavior of two austenitic Fe-18Cr-10Mn alloys with the combined addition of nitrogen and carbon was investigated in this study. The alloys exhibited a ductile-to-brittle transition behavior because of unusual brittle fracture at low temperatures unlike conventional austenitic alloys. The alloy with higher carbon content had higher yield and tensile strengths than that with lower carbon content due to the solid solution strengthening effect resulting from carbon addition. However, the increase in carbon content promoted the occurrence of intergranular fracture, and thus deteriorated the impact toughness. In order to develop successfully the austenitic Fe-18Cr-10Mn alloys with the excellent combination of strength and toughness in the future, therefore, more systematic studies are required to find the appropriate amount and ratio of nitrogen and carbon.

• 한국분말재료학회지
• /
• 제6권2호
• /
• pp.152-162
• /
• 1999

The present study is concerned with the effect of PM process variables on the microstructure by using atomized superalloy powders. It is suggested that the inhomogeneity of composition is strongly dependent on the process variables. The contents of segregation elements of plasma rotating electrode process (PREP) powders are larger than those of Ar atomization (AA) powders. As HIP treatment temperature in-increases, the secondary phases on the prior particle boundaries (PPB) have continuous,uniform distribution and high density, but the amount of PPB decreases suddenly at 1150$^{\circ}$C. Segregated phases on the PPB are identified to be MC type carbide. Brittle MC type carbides on the PPB provide fracture initiation sites and preferred fracture path, thereby leading to intergranular type brittle fracture.

• 연구논문집
• /
• 통권30호
• /
• pp.121-128
• /
• 2000

The failed tube received for this study has been used for approximately 10 year at $330^{\circ}C$ in a steam production boiler tube was fractured in the transversed direction to tube length, and fracture mode was typically intergranulas type without the plastic deformation. The fracture surface was covered by the oxide scale formed from the intermal high pressure steam at high temperature. The microstructure was not nearly thermal-degraded during the service. From this result, we can conclude that the oxide film was proferentialy formed into the grainboundary and this grainboundary oxide film was brittle-fractured by the thermal stress in the longitudinal direction to the tube brittle intergranular fracture mode.

• 한국군사과학기술학회지
• /
• 제13권5호
• /
• pp.769-774
• /
• 2010

It happened fractures on special bolt which supported main landing gear actuator up-lock rod of aircraft. Cracks were initiated mainly from the center hole and the external thread of the special bolt. To find out failure root causes, metallographic, fractographic analyses as well as test work were carried out. From the fractographic study by SEM work, fracture occurred by a brittle intergranular type failure. The fracture could be occurred primarily by solid-metal-induced embrittlement due to cadmium embrittler penetrated into the flaw existed after machining work for center hole and thread on the bolt during baking treatment processing to eliminate hydrogen. For its successful application, cadmium EP bolts require proper and adequate baking treatment after electroplating, and make no more drilled center hole on the bolt to prevent same failure.

• 한국재료학회지
• /
• 제12권6호
• /
• pp.436-441
• /
• 2002

Effect of Sn addition on the stress corrosion cracking(SCC) resistance of the Al-Cu-Mn cast alley was investigated by C-ring teat and electrical conductivity measurement, The electrical conductivity and SCC resistance increased by Sn addition. The alley containing 0,10%Sn showed maximum electrical conductivity and the best SCC resistance. At the same composition, the electrical conductivity and SCC resistance increased from peak aged condition to ever aged condition. The PFZ and coarse precipitates along the grain boundary were observed from TEM micrographs. The fracture mode of the alloy was confirmed as intergranular type and showed brittle fracture surface. The SCC mechanism of the alloy was concluded as the anodic dissolution model, The maximum hardness was increased from 130Hv in the Sn-free alloy to 156Hv in the 0.10%Sn added alloy.

• 한국재료학회지
• /
• 제11권4호
• /
• pp.266-271
• /
• 2001

Al-Cu-Mn 주조합금의 응력부식균열 저항성에 미치는 Cd첨가의 영향을 C-ring test와 전기전도도 시험을 통하여 조사하였다. Cd첨가량이 증가함에 따라 전기전도도가 증가하였고 SCC 저항성도 증가하였다. SCC 시험결과 균열이 입계를 따라 전파되는 입계파괴가 일어났으며, 파면은 취성파괴양상을 나타내었고, 입계를 따라 조대 석출물과 무석출대가 나타난 것으로 보아서 이 합금의 SCC 기구는 anodic dissolution model이라고 판단된다. Cd을 첨가하지 않은 경우 최대경도값은 127Hv였으나, Cd을 첨가한 경우 최대경도값은 138∼146Hv로 증가하였다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.256-261
• /
• 2007

The purpose of this study is to investigate the effect of shot peening on the fatigue strength and fatigue life of two kinds of aluminum alloys. The fatigue strength behavior of aluminum alloys were estimated by the stress ratio and shot velocities. The fatigue life and strength increased with increasing the test shot velocity. However, at the shot velocity range between 50m/s and 70m/s, the compressive residual stress phenomena were observed in test conditions of different shot velocity. The optimal shot velocity is acquired by considering the peak values of the compressive residual stress, dislocations, brittle striation, slip, and fisheye on the fracture surface of test specimen. It was observed from the SEM observation on the deformed specimen that the brittle striation, fisheye were showed in the intergranular fracture structure boundaries at the this velocities. Therefore, fatigue strength and fatigue life would be considered that shot velocity has close relationship with the compressive residual stress.

• Restorative Dentistry and Endodontics
• /
• 제32권2호
• /
• pp.130-137
• /
• 2007

본 연구의 목적은 니켈티타늄 전동파일의 피로파절에 있어서 표면 결함의 역할을 규명하고자 fatigue tester에서 반복적 인 fatigue force를 부여한 후 파절된 단면을 주사전자현미 경으로 관찰하여 파절 역학을 규명하는 것이다. 총 45개의 #30/.04 taper와 21 mm의 HEROShaper 니켈-티타늄 전동파일을 15개씩 3개의 군으로 분류하였다. 제 1군은 결함이 없는 새 HEROShaper파일, 제 2군은 제조과정에서 metal rollover나 machining marks와 같은 표면결함을 갖는 HEROShaper파일, 제 3군은 임상에서 4- 6개의 구치부 근관의 확대에 사용한 HEROShaper 파일을 사용하였다. 모든 파일들은 회전속도(300 rpm)와 pecking distance (3 mm)가 일정하게 맞춘 fatigue tester에서 파절될 때까지 시간을 측정한 후 통계분석을 통해 각 군간의 유의성을 분석하였고, 파절 단면의 farctographic analysis를 통해 파절역학을 규명하고자 하였다 실험결과 평균 파절시간에 있어서 group 1과 2, group 1과 3사이에는 통계학적으로 유의할 만한 차이가 있었으나 (p<0.05), group 2와 3사이에는 통계학적인 차이가 없었다. Fractographic analysis 결과 대부분의 파절면에서 microvoid와 dimple 소견을 갖는 ductile fracture양상이 관찰되었다. 또한 brittle fracture가 일어난 파절면에서는 파절선 전방에 수 많은 striation들이 관찰되었고 transgranular 및 intergranular cleavage 소견도 보였다. 표면결함이 있는 제 2, 3 군의 파절단면에서는 모든 시편에서 표면결함이 관찰되었다. 이와 같은 결과로 미루어 보아 표면결함이 반복 피로파절에서 미세균열의 기시점으로 중요한 역할을 하며 fractography분석법은 Ni-Ti 파일의 파절역학을 규명하는데 유용함을 알 수 있었다.