Effect of Synthesis Method and Melamine Content of Melamine-Urea-Formaldehyde Resins on Bond-Line Features in Plywood

  • LUBIS, Muhammad Adly Rahandi;JEONG, Bora;PARK, Byung-Dae;LEE, Sang-Min;KANG, Eun-Chang
    • Journal of the Korean Wood Science and Technology
    • /
    • v.47 no.5
    • /
    • pp.579-586
    • /
    • 2019
  • This work examined effects of the synthesis method and melamine content of melamine-urea-formaldehyde (MUF) resins on the bond-line features (i.e. resin penetration and bond-line thickness) in plywood. Two synthesis methods (MUF-A and MUF-B) and three melamine contents (5, 10, and 20%) were employed to prepare MUF resins. The MUF-A resins at three melamine contents were prepared by a simultaneous reaction of melamine, urea, and formaldehyde, while the MFU-B resins were prepared by reacting melamine at the same levels with formaldehyde followed by urea. The results showed that higher melamine content increased the viscosity of MUF-A and MUF-B resins. The resin penetration of MUF-A resins decreased by 48% while those of MUF-B resins increased by 16% at 20% melamine content. As a result, the MUF-A resins had greater bond-line thickness than those of MUF-B resins as the melamine content increased. The MUF-B resins resulted in thinner bond-line and greater resin penetration compared to those of MUF-A resins. The results suggested that MUF-B resins prepared with 20% melamine content had a proper combination of resin penetration and bond-line thickness that could produce plywood panel with a better adhesion performance.

A Syudy on the Diffusion Joining of 7000 Al Alloy (7000계 Al 합금의 확산접합에 관한 연구)

  • Jin, Y.C.;Hong, E.S.;Kim, Y.S.;Lee, M.S.;Yoo, C.Y.
    • Journal of the Korean Society for Heat Treatment
    • /
    • v.6 no.1
    • /
    • pp.9-16
    • /
    • 1993
  • To investigate the properties of diffusion bonding of 7050 Al alloy, the diffusion bonding joints have been produced in self-made diffusion bonding hot-press which admits a defined application of the bonding pressure during the heating phase and also rapid cooling after the bonding process with various bonding condition. The strength of the bond increases with increasing the bonding time and temperature. Shear test at toom temperature showed that high strength up to 70% that of parent metal (320 MPa), 220 MPa for the specimen bonded 14 hr at $560^{\circ}C$, with 3 MPa. In this case, however, there is large deformation more than 20% reduction in thickness. The results were correlated with joint characteristics found by optical microstructure and by fractography by SEM. When the strengths of the bonds are more than 50% that of parent metal, a great deal of dimples stretched along the direction of shear stress are observed over the fractured surface of the bond. On the microstructure of the bond line, initial mophology of the bond line disapeared for the grain boundary migration with increasing the bonding time.

  • PDF

Moment Resistance Performance Evaluation of Larch Glulam Joint Bonded in Glass Fiber Reinforced Plastic Rods (봉형 GFRP를 삽입접착한 낙엽송 집성재 접합부의 모멘트저항 성능 평가)

  • Lee, In-Hwan;Song, Yo-Jin;Jung, Hong-Ju;Hong, Soon-Il
    • Journal of the Korean Wood Science and Technology
    • /
    • v.43 no.1
    • /
    • pp.60-67
    • /
    • 2015
  • In order to evaluate the bond performance of domestic larch glulam and the glass fiber reinforced plastic (GFRP) rod, the specimen with the GFRP rod bonded-in domestic larch glulam for pull-out test was produced. The test was carried out using various specimens with different gluing depth, width of glue-line and type of adhesive. The cantilever type rahmen structure specimen with bonded-in GFRP rods was produced based on the result of pull-out test, and its moment resistance performance was compared and examined with the moment resistance performance of slotted-in steel plate specimen. As a result of the pull-out test, the most excellent bond performance was found when the insertion depth of GFRP rods was 5 times larger than the diameter of GFRP rods. When the glue-line thickness was 1 mm, the bond performance improved by 17%~29% in comparison to the bond performance in the case of the glue-line thickness of 2 mm. Also, the bonded strength of the specimen used with poly-urethane adhesive was 2.9~4.0 times greater than the bonded strength of specimen used with resorcinol adhesive. The cantilever type rahmen structure specimen with bonded-in GFRP rods showed the moment resistance performance 0.82 times lower in comparison to the slotted-in steel plate specimen used with the drift pin, but the initial stiffness was similar as 0.93 times.

Effect of Hot-stamping on Microstructures and Tensile Properties of Al-Si Coated Boron Steel Welds with Laser Source (Al-Si 도금된 보론강 레이저 소스에 따른 레이저 용접부의 미세조직과 기계적 성질에 미치는 핫스탬핑 처리의 영향)

  • Oh, Myeong-Hwan;Kong, Jong-Pan;Kwon, Min-Suck;Kang, Chung-Yun
    • Journal of Welding and Joining
    • /
    • v.31 no.6
    • /
    • pp.96-106
    • /
    • 2013
  • In this study, the effect of laser source($CO_2$ and Nd:YAG) on the microstructure and tensile properties of laser welded Al-Si coated boron steel(1.2mmt) was investigated with before and after hot-stamping. In case of as welds condition, fracture occurred in base metal unrelated to the laser source. It could be explained that tensile strength of fusion zone composed of martensite and bainite is higher than that of base metal that contains a lot of ferrite despite dilution of Al and Si from coating layer to fusion zone. In case of hot-stamping condition, the fracture occurred in fusion zone irrelevant to laser source and the tensile strength was lower than hot stamped base metal. In the $CO_2$ laser welds, $Fe_3$(Al,Si) formed near the bond line was transformed into ferrite during hot-stamping. Therefore tensile strength of bond line is lower than that of base metal and center of fusion zone and the fracture occurred in the bond line. On the other hand, in the Nd:YAG laser welds, the higher concentration of Al formed the ferrite in the fusion zone during hot-stamping treatment. Also, the thickness of centerline was thinner than that of base metal. Therefore, it is considered that fracture occurred in centerline of fusion zone due to effect of concentration stress, and it leaded to a lower tensile strength and elongation.

Weld Quality Evaluation Method for the Resistance Spot Welds using X-ray Transmission Inspection (X-선 투과검사를 이용한 저항 점용접부 품질평가기법)

  • Lee, Jong-Dae;Lee, So-Jeong;Bang, Jung-Hwan;Yoon, Gil-Sang;Kim, Mok-Soon;Kim, Jun-Ki
    • Journal of Welding and Joining
    • /
    • v.32 no.6
    • /
    • pp.1-7
    • /
    • 2014
  • For the resistance spot welds of CR1180 and GA1180 TRIP steels, the weld quality evaluation method using the digitalized X-ray transmission imaging apparatus was investigated in comparison with the crosssectional examination method. In the case of the resistance spot welding of CR1180, three circular regions, such as WZ(white zone), GZ(grey zone) and DZ(dark zone), appeared on X-ray image and they corresponded to the diameters of indentation mark, nugget and corona bond, respectively. The variation of X-ray transmission thickness due to the thickness variation of the weld seemed to be mainly responsible for the formation of those contrasts. The X-ray image contrast formed from the variation of transmission thickness at the outer border line of DZ could also enable the inspections of the notch shape, nonuniformity of the welding pressure and spatter from its sharpness, concentricity and the normal straight line, respectively. The X-ray image of the resistance spot weld of galvannealed GA1180 TRIP steel was very similar to that of CR1180 TRIP steel except the crown shaped outer border line of DZ which was considered to be due to the melting behavior of zinc having the boiling temperature even lower than the melting temperature of steel.

GINGIVAL MARGIAL LEAKAGE AND BONDING PATTERN OF THE COMPOSITE RESIN INLAY ACCORDING TO VARIOUS THICKNESS OF DIE SPACER (Die spacer의 두께에 따른 복합레진 inlay의 치은 변연부 미세누출 및 접착양태에 관한 연구)

  • Park, Tae-Il;Shin, Dong-Hoon;Hong, Chan-Ui
    • Restorative Dentistry and Endodontics
    • /
    • v.20 no.1
    • /
    • pp.152-163
    • /
    • 1995
  • This experiment was performed to observe the adhesion pattern and microleakage in the gingival margin according to variation in the resin cement thickness which results from thickness of Die spacer. which is considered to effect the adaptability of the composite resin inlays. Clearfil CR inlays were fabricated on stone models with CR Sep applicated once and Nice fit twice, 4 times, and 6 times each. After 2nd curing within the CRC-100 oven, CR inlays were cemented with CR inlay cement. Dye(2% methylene blue) penetration and adhesion pattern were evaluated after sectioning of gingival margin into :3 pieces. The results were as follows ; 1. The thickness of resin cement showed unevenchanging pattern with that of die spacer, namely, it was increased until 4 times' application of Nice-Fit but was decreased with 6 times' application of that. 2. The degree of dye penetration wasn't affected by cement thickness within a limited value. 3. Most of dye penetration was shown through the interface between cement and enamel rather than the interface between cement and CR inlay. This shows that the affinity of resin cement for CR inlay was superior to the adhesive strength with tooth structure. 4. No gap was found at the interface between enamel and cement but some showed separation between dentin and cement. It is concidered that the contraction force of cement was less than the bond strength with the enamel. 5. Lots of voids were found in the CR inlay and resin cement. There was a pooling tendency of bonding agent and cement in the axiogingival line angle portion. 6. In some specimens, cracks were shown in enamel margin. From this it could be considered that cavity preparation and surface treatment weakened the tooth structure.

  • PDF

CONFOCAL LASER SCANNING MICROSCOPIC MORPHOLOGY OF DENTIN-RESIN INTERFACE AND ITS RELATIONSHIP WITH SHEAR BOND STRENGTH (상아질-레진 계면의 공초점 현미경적 형태 및 전단결합강도와의 관계)

  • Choi, Nak-Won;Cho, Byeong-Hoon;Son, Ho-Hyun
    • Restorative Dentistry and Endodontics
    • /
    • v.24 no.2
    • /
    • pp.310-321
    • /
    • 1999
  • In this in vitro study, confocal laser scanning microscopic morphology of dentin-resin interface and its relationship to shear bond strength were investigated after the exposed dentin surfaces were treated with 3 different kinds of dentin adhesive systems[three-step; Scotchbond Multi-Purpose Plus(SMPP), self-priming bonding resin; Single Bond(SB), self-etching primer; Clearfil Liner Bond 2(LB2)]. 52 extracted human molar teeth without caries and/or restorations. The experimental teeth were randomly divided into three groups of seventeen teeth each. In five teeth of each group, class V cavities(depth: 1.5mm) with 900 cavosurface angles were prepared at the cementoenamel junction on buccal and lingual surfaces. Bonding resins of each dentin adhesive system were mixed with rhodamine B. Primer of SMPP was mixed with fluorescein. In group 1. the exposed dentin was conditioned with etchant, applied with above primer and bonding resin of SMPP. In group 2, with etchant and self-priming bonding agent of SB. In group 3, with self-etching primer and bonding agent of LB2. After treatment with dentin adhesive systems, composite resin were applied and photocured. The experimental teeth were cut longitudinally through the center line of restoration and grounded so that about $90{\mu}m$-thick wafers of buccolingually orientated dentin were obtained. And, $70{\sim}80{\mu}m$-thick wafers sectioned horizontally, thus presenting a dentinal tubules at 900 to the cut surface of a remaining tooth, were obtained. Primer of SMPP mixed with rhodamine B was applied to these wafers. Confocal laser scanning microscopic investigations of these wafers were done within of 24 hours after treatment. To measure shear bond strength, the remaining twelve teeth of each group were grounded horizontally below the dentinoenamel junction, so that no enamel remained. After applying dentin adhesive systems on the dentin surface, composite was applied in the shape of cylinder. The cylinder was 5mm in diameter, and 2mm in thickness. Shear bond strength was measured using Instron with a cross-head speed of 0.5mm/min. It was concluded as follows ; 1. Hybrid layer of SMPP(mean: $4.56{\mu}m$) was thicker than that of any other groups. This value was not statistically significant thicker than that of SB(mean: $3.41{\mu}m$, p>0.05), and significant thicker than that of LB2(mean: $1.56{\mu}m$, p<0.05). There was a statistical difference between SB and LB2(p<0.05). 2. Although there were variations in the length of resin tag even in a sample, and in a group, most samples in SMPP and SB showed resin tags extending above $20{\mu}m$. But samples in LB2 showed resin tags of $10{\mu}m$ at best. 3. Besides primer's infiltration into demineralized peritubular dentin and dentinal tubules, fluorophore of primer was detected in the lateral branches of dentinal tubules. 4. All groups demonstrated statistically significant differences from one another(p<0.05), with shear bond strengths given in descending order as follows: SMPP(18.3MPa), SB(16.0MPa) and LB2(12.4MPa). 5. LB2 having thinnest hybrid layer($1.56{\mu}m$) showed the lowest shear bond strength(12.4MPa).

  • PDF