• Restorative Dentistry and Endodontics
• /
• v.30 no.3
• /
• pp.178-183
• /
• 2005

This study was done to evaluate whether vital bleaching agents could influence on the translucency of the bovine enamel. The anterior bovine teeth that were extracted one day before and without any gross discoloration were obtained and then were preserved in physiologic saline. 6 mm cylindrical tooth specimens were fabricated with diamond puncher perpendicularly on labial surface of bovine tooth. After embedded in transparent acrylic resin with labial surface being exposed, they were cut to a thickness of 1.2 mm with low speed diamond saw (Isomat, Buehler Co., Lake Bluff, IL, USA). They were smoothly ground to 1 mm thickness of enamel with sandpaper. 24 specimens were randomly divided into 3 groups and control group respectively. Opalescence (10% carbamide peroxide, Ultradent, South Jordan, USA), Rembrandt (10% carbamide peroxide, DenMat, USA) and Opalescence F (15% carbamide peroxide with fluoride, Ultradent, USA) were applied on labial sides of the bovine enamel for 7 days (bleaching agents were reapplied every 24 hours) and the opposite surface was contacted to cotton that soaked in distilled water. The control group was soaked in distilled water. Three stimulus value X, Y and Z were evaluated with colorimeter (Color ' Color Differencerneter, Model TC-6FX, Tokyo Denshoku Co., Japan) on the labial surface of all specimen three times on white and black background plate before the bleaching agents were applied and on 3rd, 5th and 7th day after applied. The degree of translucency was normally assessed by measuring the inverse property, opacity (contrast ratio). 10% Opalescence, 15% Opalescence-F, and control group showed no significant variation in the translucency of bovine enamel, However Rembrandt decreased the translucency of it (p < 0.01).

• Restorative Dentistry and Endodontics
• /
• v.26 no.4
• /
• pp.263-272
• /
• 2001

The aim of this study was to investigate the influence of four different light curing modes on the marginal leakage of Class V composite resin restoration. Eighty extracted human premolars were used. Wedge-shaped class Y cavities were prepared on the buccal surface of the tooth with high-speed diamond bur without bevel. The cavities were positioned half of the cavity above and half beyond the cemento-enamel junction. The depth, height, and width of the cavity were 2 mm, 3 mm and 2 mm respectively. The specimens were divided into 4 groups of 20 teeth each. All the specimen cavities were treated with Prime & Bond$^{R}$ NT dental adhesive system (Dentsply DeTrey GmbH, Germany) according to the manufacturer's instructions and cured for 10 seconds except group VI which were cured for 3 seconds. All the cavities were restored with resin composite Spectrum$^{TM}$ TPH A2 (Dentsply DeTrey GmbH, Germany) in a bulk. Resin composites were light-cured under 4 different modes. A regular intensity group (600 mW/${cm}^2$, group I) was irradiated for 30 s, a low intensity group (300 mW/${cm}^2$, group II) for 60 s and a ultra-high intensity group (1930 mW/${cm}^2$, group IV) for 3 s. A pulse-delay group (group III) was irradiated with 400 mW/${cm}^2$ for 2 s followed by 800 mW/${cm}^2$ for 10 s after 5 minutes delay. The Spectrum$^{TM}$ 800 (Dentsply DeTrey GmbH, Germany) light-curing units were used for groups I, II and III and Apollo 95E (DMD, U.S.A.) was used for group IV. The composite resin specimens were finished and polished immediately after light curing except group III which were finished and polished during delaying time. Specimens were stored in a physiologic saline solution at 37$^{\circ}C$ for 24 hours. After thermocycling (500$\times$, 5-55$^{\circ}C$), all teeth were covered with nail varnish up to 0.5 mm from the margins of the restorations, immersed in 37$^{\circ}C$, 2% methylene blue solution for 24 hours, and rinsed with tap water for 24 hours. After embedding in clear resin, the specimens were sectioned with a water-cooled diamond saw (Isomet$^{TM}$, Buehler Co., Lake Bluff, IL, U.S.A.) along the longitudinal axis of the tooth so as to pass the center of the restorations. The cut surfaces were examined under a stereomicroscope (SZ-PT Olympus, Japan) at ${\times}$25 magnification, and the images were captured with a CCD camera (GP-KR222, Panasonic, Japan) and stored in a computer with Studio Grabber program. Dye penetration depth at the restoration/dentin and the restoration/enamel interfaces was measured as a rate of the entire depth of the restoration using a software (Scion image, Scion Corp., U.S.A.) The data were analysed statistically using One-way ANOVA and Tukey's method. The results were as follows : 1. Pulse-Delay group did not show any significant difference in dye penetration rate from other groups at enamel and dentin margins (p>0.05) 2. At dentin margin, ultra-high intensity group showed significantly higher dye penetration rate than both regular intensity group and low intensity group (p<0.05). 3. At enamel margin, there were no statistically significant difference among four groups (p>0.05). 4. Dentin margin showed significantly higher dye penetration rate than enamel margin in all groups (p<0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.636-644
• /
• 2004

Recently, self-etching adhesive system have been developed and bonding procedures simplified into one or two steps, which are simultaneously applied to both enamel and dentin. These systems are easy to use and have the potential for good clinical success. The purpose of this study is to evaluate in vitro the microleakage on the cementum/dentin and enamel walls in composite resin restoration of Class V cavities, regarding the use of different adhesive systems. 30 human premolars were divided into 3 groups. A standardized Class V preparation was prepared on the buccal and lingual surface of each premolar. The preparation were made parallel to the cementoenamel junctions, with the gingival half of the preparation extending 1mm apical to the cementoenamel junction. After adhesive system was applied to teeth as manufacture's recommendation, hybrid resin composite was filled in bulk into the preparation and light polymerized according to manufacturer's recommendations. Specimen were stored in distilled water at $37^{\circ}C$ for 5 days and thermocycled 1000 times ($5^{\circ}C{\pm}2^{\circ}C\;and\;55^{\circ}C{\pm}2^{\circ}C)$, then immersed in a 2% methylene blue solution for 12 hours. After sectioning mesio distally through the restorations, the degree of dye penetration was scored under a stereomicroscope at ${\times}\;25$ magnification. The data were analyzed statistically using t-test and one-way ANOVA. The results were as follows: ${\cdot}$ There is no adhesive system which can prevent microleakage perfectly. ${\cdot}$ There is significant difference in microleakage between enamel margin and dentin margin (p<0.0001). ${\cdot}$ In enamel margin, self-etching primer systems did not show any significant difference comparing total-etching system. In denin margin, self-etching primer systems did not show any significant difference comparing one-bottle adhesive system used in combination with total-etching.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.343-355
• /
• 2007

The objectives of this study was to evaluate the durability of 4 resin cements by means of microtensile bond strength test combined with thermocycling method and fractographic FE-SEM analysis. Experimental groups were prepared according to thermocycling (0, 1,000, 5,000) and the kind of resin cements, those were Variolink II, Multilink, Panavia F 2.0, Rely X Unicem. Flat dentin surfaces were created on mid-coronal dentin of extracted third molars. Then fresh dentin surface was grounded with 320-grit silicon carbide abrasive papers to create uniform smear layers. Indirect composite block (Tescera, Bisco Inc., Schaumburg, IL, USA) was fabricated ($12\;{\times}\;12\;{\times}\;6\;mm^3$). It's surface for bonding to tooth was grounded with silicon carbide abrasive papers from 180- to 600-grit serially, then sandblasted witk $20\;-\;50\;{\mu}m$ alumina oxide. According to each manufacturer's instruction, dentin surface was treated and indirect composite block was luted on it using each resin cement. For Rely X Unicem, dentin surface was not treated. The bonded tooth-resin block were stored in distilled water at $37^{\circ}C$ for 24 hours. After thermocycling, the bonded tooth-resin block was sectioned occluso-gingivally to 1.0 mm thick serial slabs using all Isomet slow-speed saw (Isomet, Buehler Ltd, Lake Bluff, IL, USA). These sectioned slabs were further sectioned to $1.0\;{\times}\;1.0\;mm^2$ composite-dentin beams. The specimens were tested with universal testing machine (EZ-Test, Shimadzu, Japan) at a crosshead speed of 1.0 mm/min with maximum load of 500 N. The data was analyzed using one-way ANOVA and Duncan's multiple comparison test at $p\;{\leq}\;0.05$ level. Within the limited results, we conclude as follows; 1. The bond strength of Variolink II was evaluated the highest among experimental groups and was significantly decreased after 1,000 thermocycling (p < 0.05). 2. The bond strength of Multilink was more affected by thermocycling than the other experimental groups and significantly decreased after 1,000 thermocycling (p < 0.05). 3. Panavia F 2.0 and Rely X Unicem showed the gradually decreased tendency of microtensile bond strength according to thermocycling but there was no significant difference (p > 0.05). 4. Adhesive based-resin cements showed lower bond strength with or without thermocycling than composite based-resin cements. 5. Variolink II & Multilink showed high bond strength and mixed failure, which was occurred with a thin layer of luting resin cement before thermocycling and gradually increased adhesive failure along the dentin surface after thermocycling. The bonding performance of resin cement can be affected by application procedure and chemical composition. Composite based-resin cement showed higher bond strength and durability than adhesive based-resin cement.

• Restorative Dentistry and Endodontics
• /
• v.34 no.4
• /
• pp.309-323
• /
• 2009

In this study we evaluated the influence of both the thickness of residual enamel and the color of the composite resins applied to lingual surface on the labial surface color. Background plates were made by randomly (A1, A2, A6D, B1, B2, B3, C1, C2, C6D) selected colors of Filtek Supreme (3M ESPE, St. Paul, U.S.A.) composite resin. Crown portion of 9 maxillary central incisors were cut off and embedded with acrylic resin except labial surface. Samples of average thickness of 2.2 mm were obtained after cutting it in a thickness of 2.5 mm from the labial surface and sandpaper polish. The shade of composite resin background was measured using Spectrophotometer ($Spectrolino^{(R)}$, GretagMacbeth, Regensdorf, Switzerland). And CIE $L^{\ast}a^{\ast}b^{\ast}$value of 2.2 mm thickness tooth samples were measured on the 9 composite resin backgrounds. And then, the cutting side of tooth samples was ground to the extent of 1.9 mm, 1.6 mm, 1.3 mm, 1.0 mm and placed on composite resin backgrounds and measured $L^{\ast}a^{\ast}b^{\ast}$values with the same method. In all samples, $L^{\ast}$value and $b^{\ast}$value seemed to have a tendency of decreasing as thickness of tooth sample becomes thinner regardless of background colors (p < 0.05). But, $a^{\ast}$value didn't show the significant differences depending on the thickness.