• Polymer(Korea)
• /
• v.25 no.4
• /
• pp.568-574
• /
• 2001

PEO-like solid polymer electrolytes based on bisphenol A ethoxylate acrylate were synthesized and their electrochemical properties and mechanical stability were studied. Low molecular weight poly(ethylene glycol) dimethyl ether (PEGDMe) was added to increase the conductivity of the electrolyte. The maximum conductivity of the resulting polymer electrolyte was found to be 1.0 ${\times}$ 10$^{-3}$ S/cm [Bisphenol A ethoxylate diacrylate ([EO]/[phenol]= 15), PEGDMe250 80 wt%, LiCF$_3SO_3$] at 30$^{\circ}$C. Tensile strength of the free standing polymer electrolyte films was measured to be in the range of 0.4 ~ 5 MPa and these polymer electrolyte films did not show a crack even in 90$^{\circ}$ and 180$^{\circ}$ bending against ${\phi}$=3 mm bar. These electrolytes showed oxidation stability up to 4.5 V vs. lithium reference electrode.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.3
• /
• pp.595-605
• /
• 2018

In recent years, researches on organic-inorganic coating films have conducted a nanocomposite system composed of organic resin matrices having excellent flexibility and chemical stability and inorganic materials having excellent mechanical properties. The o-phenylphenoxyethyl acrylate (OPPEA) used as the acrylate monomer has a high refractive index of 1.58, and the bisphenol A ethoxylate diacrylate (BAEDA) has a low refractive index but improves the chemical stability of the organic resin. In addition, zirconia used as an inorganic material exhibits excellent durability and optical properties. In this study, the BAEDA contents in acrylate monomer were controlled to produce a film with suitable optical transparency. And optimum conditions were established by comparing the changes in surface properties of PET films detected with pencil hardness tester, Abbe's refractometer, and UV-vis spectrophotometer. The hydrophobicity and the dispersibility of zirconia in acrylate monomer were much improved after modification with ${\gamma}$-methacryloxypropyltrimethoxysilane (MPS), which is a silane coupling agent. And the existence of ester C=O bond peak at $1716cm^{-1}$ introduced by MPS through FT-IR ATR spectrophotometer confirmed the completion of surface modification of zirconia with MPS. In addition, the presence of silicon atom on the surface modified zirconia was also proved using X-ray fluorescence spectrometer. When the photocurable hybrid coating was prepared by introducing chemically modified zirconia into acrylate monomer, the refractive index of this coated PET film was improved by 1.2%, compared to the only acrylate coated PET film. The homogeneous distribution of zirconia in acrylate coating layer on PET film was also identified through SEM/EDS mapping analysis technique.