A Study on the Effect of Oyster Shell Surfase Modified with Rare Earth Coupling Agent on Eco-Friendly Bio-EPDM Foam (Rare earth coupling agent로 표면개질된 Oyster shell이 친환경 Bio-EPDM 발포체에 미치는 영향 연구)

  • Seo, Eun Ho;Lim, Sung Wook;Park, Kyung Soon;Park, Eun Young
    • Textile Coloration and Finishing
    • /
    • v.33 no.4
    • /
    • pp.317-326
    • /
    • 2021
  • In this study, we investigated for Bio-EPDM foam with oyster shell surface modified earth coupling agent. Experiments were carried out to confirm the bio-EPDM/Oyster shell foam applying content of earth coupling agent. The cure characterization were evaluated by measuring the mooney viscosity and oscillating disc rheometer (ODR). Mechanical properties such as hardness, tensile strength, elogation at break and tear strength were measured, and changes of mechanical properties were also evaluated after immersion in NaCl solution. In addition degree of volume change was measured after immersing the Bio-EPDM foam in NaCl solution and the low-temperature permanent compression set was evaluated at 4℃. To evaluate the low-temperature characteristics of Bio-EPDM/Oyster shell, the glass transition temperature was measured using Differential Scanning Calorimeter (DSC). As a result as the content of the earth coupling agent increased up to 3phr, the crosslinking density and mooney viscosity increased, and the mechanical properties and low-temperature permanent compression set improved, but from 4phr, it was rather decreased. The change in the glass transition temperature was insignificant, and the foam cell appeared to be uniform when the earth coupling agent was applied.

Thermoplastic Polyurethane (TPU)/Ethylene-Propylene-Diene Monomer Rubber (EPDM) and TPU/Polybutadiene Rubber (BR) Blends for the Application of Footwear Outsole Materials (신발겉창 재료용 열가소성 폴리우레탄 (TPU)/에틸렌-프로필렌-디엔 고무와 TPU/부타디엔 고무 블렌드)

  • Kim, Ji-Hoo;Kim, Gue-Hyun
    • Elastomers and Composites
    • /
    • v.48 no.3
    • /
    • pp.195-200
    • /
    • 2013
  • The main objective of this study is to improve abrasion resistance and wet slip resistance of thermoplastic polyurethane (TPU) by blending with ethylene-propylene-diene monomer rubber (EPDM) or polybutadiene rubber (BR) for the application of the footwear outsole materials. With addition of 10 wt% of EPDM or BR, TPU/EPDM and TPU/BR blends exhibited higher NBS abrasion resistance, tensile properties and wet slip resistance than TPU. However, with further increasing content of EPDM and BR, abrasion resistance and tensile properties of the blends decreased. Improvement in abrasion resistance and tensile properties with 10 wt% of addition of EPDM or BR may be due to better microphase separation of TPU.

Study on Surface Chemical Structure and Mechanical Properties of EPDM Rubber with Microwave Irradiation Time

  • Eom, SeoBin;Lee, Sun Young;Park, Sung Han;Lee, Seung Goo
    • Elastomers and Composites
    • /
    • v.53 no.3
    • /
    • pp.124-130
    • /
    • 2018
  • Recently, microwaves have been used for desulfurization because they can selectively dissociate C-S and S-S bonds present in vulcanized rubber. In this study, we investigated the changes in structural and physical properties of EPDM (Ethylene propylene diene monomer) rubber by irradiating it with microwaves for different durations. The surface chemical composition of the irradiated EPDM rubber was analyzed by FT-IR, XPS, and EDS analyses. It was confirmed by XPS that C-S and S-S S2p peak heights greatly decreased when microwave irradiation was performed for more than 5 min. In the EPDM sample irradiated with microwaves for 10 min, the number of S-O bonds significantly increased owing to oxidation. As the microwave irradiation time was increased, SEM images showed cracks and voids on the EPDM surface. The 20% decomposition temperature of the EPDM rubber sample was investigated by TGA, and it was found to be about $435.23^{\circ}C$ for the EPDM rubber irradiated for 10 min. The crosslinking density of the EPDM rubber was determined by measuring the degree of swelling, and the highest value was observed for the E5 sample irradiated for 5 min. The degree of swelling of the E10 sample irradiated for 10 min was lower than that of the E5 sample. These results indicate that when irradiated with microwaves for more than a certain time, desulfurization occurs and the side chain of the EPDM rubber dissociates and forms additional crosslinking bonds.

Impact of Sound Insulation in a Combine Cabin

  • Kim, Chiho;Jung, Ho Jun;Jo, Jin Seok;Kim, Myong il;Lee, Bongho;Park, Tae Jong;Seo, Kwangwook;Kim, Hyeon Tae
    • Journal of Biosystems Engineering
    • /
    • v.40 no.3
    • /
    • pp.159-164
    • /
    • 2015
  • Purpose: Recently, environmental pollution and safety problems in agricultural production have become important issues. Initially, bio-production machines focused on high production efficiency rather than workers' safety and comfort, but this trend slowly has changed as time went on. Methods: This study was carried out to identify sound efficiently and reliably for noise reduction by using a combine cabin model. Ethylene propylene diene monomer (M-class) rubber (EPDM) was applied to improve noise reduction performance from parts connected directly to the front, rear, left side, and bottom side of the cabin. Results: As a result, an average noise reduction of 1.85 dB was achieved in the normal hearing range between 500 Hz to 2 kHz. Conclusions: Reducing the cabin noise levels can reduce a worker's fatigue, improve working environment, and contribute to future low-noise and high-quality cabin environment.

Mechanical Properties of Polyethylene/Polypropylene/Waste Tire Rubber Powder Composites (폴리에틸렌/폴리프로필렌/폐타이어고무분말 복합체의 기계적 특성)

  • Choi, Jeong-Su;Park, Cha-Cheol
    • Elastomers and Composites
    • /
    • v.46 no.4
    • /
    • pp.318-323
    • /
    • 2011
  • To recycle the waste tire rubber powder, rubber powder composite for waterproof sheet was prepared, and analyzed the effect of the kind of resin and the amount of crosslinking agent on the mechanical property of the composites. The elongation-at-break of the PE composite increased more than 3 times as EPDM was added into rubber composites. As the content of the crosslinking agent increased, the tensile strength of composite increased as well. When recycled polypropylene was used, the increase in composite's tensile strength was more than 3 times. Therefore to use the recycled PP in composite is more effective rather than PP in term mechanical properties.