• Progress in Superconductivity and Cryogenics
• /
• v.5 no.3
• /
• pp.15-19
• /
• 2003

For the purpose of standardization of the critical current measurement, it is meaningful to describe how $I_{c}$ will behave as the stress/strain level changes. In this study, strain dependencies of the critical current $I_{c}$ in Ag-alloy sheathed multifilamentary Bi(2212) and Bi(2223) superconducting tapes were evaluated at 77K, 0T. The external reinforcement was accomplished by soldering AgMgNi alloy tapes onto single or both sides of the sample. With the external reinforcement to the Bi(2212) tape, the strength of the tapes increased but the critical current at the strain free state, $I_{c0}$ decreased in some cases. The strain for onset of the $I_{c}$ degradation, $\varepsilon$$_{\irr}$, increased with an increase of the reinforcing volume and then saturated to a certain value. The effect of external reinforcement on the degradation of $I_{c}$ due to the bending strain in the Bi(2223) tape was also examined. Contrary to the expectation, it showed a significant $I_{c}$ degradation even at a small strain of 0.4 %. The observations of damage morphologies gave a good explanation to the $I_{c}$ behavior.c/ behavior.r.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.17-20
• /
• 2002

The effects of relatively low lead content (0.2~0.3) on the 2223 phase formation and transport property of Bi-2223/Ag tapes have been investigated. The results show that lead contents have great impact on the phase assemblage of precursors, subsequently, on the phase formation and transport property of silver sheathed BSCCO-2223 tapes. Powders containing Pb=0.25 and Pb=0.3 resulted in the nearly identical $J_c$ values in fully processed tapes, but leaded to significant difference on the phase formation process. For the case of Pb=0.2, both low conversion fraction of 2212 to 2223 and low $J_c$ value were obtained in final reacted tape, which was probably due to lack of enough liquid phase to facilitate the phase transformation.

• Progress in Superconductivity
• /
• v.7 no.1
• /
• pp.97-101
• /
• 2005

Bi-22l2 tubes for fault current limiter (FCL) were fabricated by centrifugal melting process. $SrSO_4$ ($10\;wt.\;\%$) was added to Bi-2212 powder to lower the melting point of Bi-22l2 and to improve the mechanical properties. The BSCCO powder was completely melted at $1300\;^{\circ}C$ using the RF furnace and then poured into rotating steel mold. The steel mold, preheated at $450\;{\circ}C{\sim}550^{\circ}C$ for 2 hour was rotated at $1020{\sim}2520\;RPM$. The solidified BSCCO tube was cooled down to room temperature in the furnace for 48 hours and separated from the mold between Bi-2212 and the mold. $ZrO_2$ solution was used to separate it easily from the mold and Ag tape was attached in the mold inner wall of the mold to analysis electrical property. Bi-22l2 tube was often cracked when the cooling rate was high. BSCCO tubes with $70{\Phi}{\times}100\;mm,\;50{\Phi}{\times}100\;mm$ and $30{\Phi}{\times}150\;mm$ size were fabricated by centrifugal melting process. The $J_{c}s$ of tubes with $50{\Phi}{\times}100\;mm{\times}4.0\;t$ and $50{\Phi}{\times}100\;mm{\times}4.l\;t$ were 178 and $74.2\;A/cm^2$ at 77K, respectively. The processing condition for Bi-2212 tube fabrication was investigated using XRD and SEM analyses.