• Journal of Welding and Joining
• /
• v.24 no.3
• /
• pp.22-26
• /
• 2006

It is necessary to investigate the welding performance and fracture resistance of welding part in structure. This study presented a most suitable condition of welding process for butt and lap joints by $CO_2$ arc welding which is widely used in the vehicle structure. Also it was conducted to tensile and fatigue test under various welding conditions. For butt and lap joints, the best conditions of welding voltage and current were 30V and 320A, respectively, in 3.2 and 4.5 mm thick steel plate. Under this condition it could be taken the highest tensile strength and fatigue strength, and a good bead appearance.

• Journal of Welding and Joining
• /
• v.27 no.2
• /
• pp.69-75
• /
• 2009

The effects of welding speed were investigated on penetration characteristics, defects and mechanical properties including formability test in Nd:YAG laser welded 1000MPa grade DP steels. A shielding gas was not used and bead-on-plate welding was performed with various welding speeds at 3.5kW laser power. Defects of surface and inner beads were not observed in all welding speeds. As the welding speed increased, the weld cross-section varied from the trapezoid having wider bottom bead, through X type, finally to V type in partial penetration range of welding speeds. The characteristic of hardness distribution was also investigated. The center of HAZ had maximum hardness, followed by a slight decrease of hardness as approaching to FZ. Significant softening occurred at the HAZ near BM. Regardless of the welding speed, the weld showed approximately the same hardness distribution. In the perpendicular tensile test with respect to the weld direction, all specimens were fractured at the softening zone. In the parallel tensile test to the weld direction, the first crack occurred at weld center and then propagated into the weld. Good formability over 80% was taken for all welding conditions.

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.246-248
• /
• 2004

Effects of the post treatment on the fatigue strength of a bead-on-plate weldment were investigated in order to improve fatigue strength of the weldment. The post treatment applied were the grinding of weld toe and hammer peening at the weld toe. The fatigue strength of the weldment after post treatment increases. It is attributed to the decrease of the residual stress and the maximum stress at the weld toe by the post treatments. Based on the result, the principal factor controlling the fatigue strength of the weldment was identified as the toe shape of the bead-on-plate weldment.

• Journal of Welding and Joining
• /
• v.27 no.6
• /
• pp.74-79
• /
• 2009

Titanium and titanium alloy can be reproduced immediately even if oxide films($TiO_2$) break apart in sea water. Therefore, since titanium demonstrates large specific strength and outstanding resistance to stress corrosion cracking, crevice corrosion, pitting and microbiologically influenced corrosion in sea water environment, it has been widely applied to heat exchanger for ships. In particular, with excellent elongation, pure titanium may be deemed as optimal material for production of heat exchanger plate which is used with wrinkles formed for efficient heat exchange. Conventional plate type heat exchanger prevented leakage of liquid through insertion of gasket between plates and mechanical tightening by bolts and nuts, but in high temperature and high pressure environment, gasket deterioration and leakage occur, so heat exchanger for LPG re-liquefaction device etc do not use gasket but weld heat exchanger plate for use. On the other hand, since welded plate cannot be separated, it is important to obtain high quality reliable welds. In addition, for better workability and production performance, lasers that can obtain weldment with large aspect ratio and demonstrate fast welding speed even in atmospheric condition not in vacuum condition are used in producing products. So far, 1st report and 2nd report compared and analyzed embrittlement degrees by bead colors of weldment through quantitative analysis of oxygen and nitrogen and measurement of hardness as fundamental experiment for the evaluation of titanium laser welding, and evaluated the welding performance and mechanical properties of butt welding. This study welded specimens in various conditions by using laser and GTA welding machine to apply edge welding to heat exchanger, and evaluated the mechanical strength through tensile stress test. As a result of tensile test, laser weldment demonstrated tensile strength 4 times higher than GTA welds, and porosity could be controlled by increasing and decreasing slope of laser power at overlap area.

• Special Issue of the Society of Naval Architects of Korea
• /
• 2007.09a
• /
• pp.118-127
• /
• 2007

SAW(Submerged Arc Welding) process is generally applied to a wide range of welding area in the fabrication of steel structure. This process has a good characteristic properties such as the high quality of welds and the high deposition rates, but in case of welding on a thick steel plate, it also has higher cold crack susceptibility than that of a thin steel plate. The purpose of this research is to find the main factor of crack generation and clarify the countermeasure for crack prevention, and then establish the optimum welding condition in a heavy thick steel plate. The results of this study are as follows, 1. The cause of crack generation is found the diffusible hydrogen penetrated into weld metal by decomposition of the remained moisture in SAW flux during welding. 2. For the removal of diffusible hydrogen, the raw materials of SAW flux are to be dehydrated at the high temperature in the initial manufacturing stage. 3. Mechanical properties of weld metal welded with the dehydrated SAW flux were evaluated very excellent, furthermore the weld metal has been proved to have low diffusible hydrogen content with 3.1ml /100g. 4. The weldability and quality welded with thick steel plates were improved by establishing the new optimum welding condition.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.80-84
• /
• 2011

The weight reduction of the transportations has become an important technical subject Al and Al alloys, especially Al 5052 alloys have been being applied as door materials for automobile. One of the most widely known car weight-reduction methods is to use light and corrosion-resistant aluminum alloys. However, because of high electrical and thermal conductivity and a low melting point, it is difficult to obtain good weld quality when working with the aluminum alloys. Also, Pulse MIG welding is the typical aluminum welding process, but it is difficult to apply to the thin plate, because of melt-through and humping-bead. In order to enhance weld quality, welding parameters should be considered in optimizing the welding process. In this experiment, Al 5052 sheets were used as specimens, and these materials were welded by adopting new Cold Metal Transfer (CMT) pulse process. The proper welding conditions such as welding current, welding speed, torch angle $50^{\circ}$ and gap 0~1mm are determined by tensile test and bead shape. Through this study, range of welding current are confirmed from 100A to 120A. And, the range of welding speed is confirmed from 1.2m/min to 1.5m/min.

• International Journal of Korean Welding Society
• /
• v.1 no.1
• /
• pp.31-38
• /
• 2001

For the horizontal fillet welding with one plate in a vertical position, there will be a higher tendency of weld metal falling down rather than for the butt-welding in flat position. Such phenomenon could bring about the overlap or deflection of weld pool, and consequently induce the poor mechanical strength of weldments. Therefore, a precise position control of welding torch in conjunction with the weld qualify plays an important role in welding robot applications. In the present study, an experimental method was proposed for deriving a mathematical model between the leg length and the welding conditions. Finally, an algorithm was proposed for weld seam tracking and improvement of the weld quality. The reliability of the proposed algorithm was evaluated through various experiments, which showed that the proposed algorithm can be very effective for tracking the weld line and simultaneously achieving the sound weld bead.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2001.05a
• /
• pp.276-281
• /
• 2001

Wet Underwater arc welding process is inverstigated by using experimentally developed flux coated underwater arc welding electrode and SS400 steel plate of 12mm thickness as base metal. Two kinds of different flux covered wet arc welding electrode of 3.2mm diameter (UW-1, UW-2) are individually developed and one of the improved underwater welding electrode (UW-2) may be put to practical use for underwater arc welding process.

• Proceedings of the KWS Conference
• /
• 1997.10a
• /
• pp.147-150
• /
• 1997

The characteristics of underwater welding of SWS490 steel were investigated. The bead-on-plate type welding with one or three pass using ilmenite and water-proofed type electrodes was performed by varying welding currents and the sizes of electrodes used. The amounts of hydrogen absorbed inter the weld metal were measured according to the JIS Z 3118 specification and the results were interpreted in terms of the cold cracking behaviours of the welded steel. The microstructural changes as well as the microhardness distribution after underwater welding were also investigated using Vickers microhardness tester and S.E.M (scanning electron microscopy) and O.M (optical microscopy). The results indicated that the cold cracking could be avoided by three pass welding under low current with an electrode with a small diameter.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.10a
• /
• pp.93-94
• /
• 2006