• Journal of the Korean Wood Science and Technology
• /
• 제40권2호
• /
• pp.91-100
• /
• 2012

This study analysis the effect of various temperatures (20, 35 and $50^{\circ}C$) on the formaldehyde emission from wood composites, which were particleboard (PB), medium density fiberboard (MDF), high density fiberboard (HDF) and laminated HDF (L-HDF) by Japanese desiccator method. Also, to reduce formaldehyde emission by wood composites, it has been suggested that undergo a bake-out conditions. On average, the level of formaldehyde emission increased many times with a $15^{\circ}C$ increase in temperature from 20 to $35^{\circ}C$ for PB, MDF, HDF and L-HDF, respectively. Formaldehyde emissions from wood composites could be expected to increase with increasing ambient temperature. At $35$ for 28 days bake-out treatment of boards, the free formaldehyde emission reduced 67.8% (PB), 40.1% (MDF), 37.8% (HDF), and 35.2% (L-HDF). On the other hand, after the bake-out at $50^{\circ}C$ for 28 days, the formaldehyde concentration decreased by 88.2, 66.9, 62.2 and 59.3% of the concentration before the bake-out for PB, MDF, HDF and L-HDF, respectively. An interesting of the bake-out treatment at $50^{\circ}C$ after 14 days, formaldehyde emission grade of PB & MDF down $E_2$ to $E_1$, and HDF & L-HDF down $E_1$ to $E_0$.

• 대한금속재료학회지
• /
• 제49권6호
• /
• pp.448-453
• /
• 2011

Pre-aging heat treatment after solution heat treatment (SHT) of Al-0.4 wt%Mg-1.2 wt%Si-0.1 wt%Mn alloy sheets for auto-bodies was carried out to investigate the effect of pre-aging and its conditions on the bake-hardening response. Mechanical properties were evaluated by a tensile and Vickers hardness test. Microstructural observation was also performed using a transmission electron microscope (TEM). It was revealed that pre-aging treatments play a great role in the bake-hardening response. In addition, it was found that the sphere-shaped nanosized clusters that can directly transit to the needle-shaped ${\beta}$" phase during the paint-bake process, not being dissolved into the matrix, are formed at 343 K. The result, reveals that the dominant factor of the bake-hardening response is the pre-aging temperature rather than the pre-aging time.

• 열처리공학회지
• /
• 제33권4호
• /
• pp.161-172
• /
• 2020

The tensile property of A5082 and A6060 aluminium wrought alloys was investigated, in terms of the strain rate sensitivity on alloy conditions by heat treatment and bake hardenability on pre-strain prior to strain ageing. The tensile test was carried out in a range of strain rate of 4.17 × 10^-5 s^-1 ~ 4.17 × 10^-5 s^-1 in room temperature and the nominal range of pre-strain was 3.0 ~ 10.5%. The tensile deformation of A5082 alloys is characterized as typical case of dynamic strain ageing with negative strain rate sensitivity for all conditions, and the tensile strength indicates a similar level regardless of alloy conditions, except only in full annealed condition. The stress-relief annealing on A6060 alloys can induce practical decrease in strength level of over approximately 100 MPa without any ductility loss, compared to as-rolled condition, while a full annealed and aged condition leads remarkable strengthening effect with the decrease of tensile elongation. Additionally, the bake hardenability of A5082 alloy by strain ageing indicates a negative dependence upon the increase of pre-strain, while A6060 alloy exhibits a positive sign even in low level relatively compared with conventional SPCC.

• Journal of the Korean Wood Science and Technology
• /
• 제34권3호
• /
• pp.30-37
• /
• 2006

본 연구는 각종 실내디자인에 이용되는 목질보드의 포름알데히드(HCOH) 방산 특성과 몇 가지 VOC 저감 방법에 대한 포름알데히드의 방산량 변화를 측정하였다. 포름알데히드 방산량은 온도가 증가함에 따라 뚜렷이 증가하는 경향을 보였고, 측정 전 처리조건에 따라 포름알데히드 방산량의 현저한 변화가 나타났다. bake-out 처리후의 목질보드의 포름알데히드 방산량은 대조구와 비교하여 감소함을 나타냈다. 시편에 urethane, cashew, water stain, oil stain coating을 했을 때 각 마감재료에 따라 포름알데히드 방산량의 차이가 확인되었으며, edge sealing 처리 후 두드러진 감소경향이 나타났다. $TiO_2$ coating은 일반광보다는 자외선 램프의 포름알데히드 저감효율이 좋았고, 자외선 램프의 조사시간이 길어지면 포름알데히드의 감소량도 증가하였다.