• Polymer(Korea)
• /
• v.24 no.1
• /
• pp.23-28
• /
• 2000

Autoadhesion strength of PS/PS Interfaces in solvent welding was determined as a function of processing conditions by butt joint test. It was verified that the chain mobility and surface roughness at PS/PS interface were enhanced by the applied solvent having a similar solubility parameter as PS and resulted in the dramatic improvement of autoadhesion strength at PS/PS interface. It was found that the mechanism of solvent welding is dependent upon the chain mobility due to the diffusion of solvent to PS interface and the contact area at interface. When the welding temperature is lower than the boiling point of applied solvent, the effect of chain mobility on autoadhesion strength was dominated, while contact area took more important role when welding temperature is above the boiling point of solvent. Autoadhesion strength increased with increasing contact time and contact temperature but :he effect of solvent on autoadhesion strength became smaller.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.403-409
• /
• 2009

In the 1840s, Goodyear found out sulfur cure system, but cure time was too slow. So producing of rubber product takes a long time. In 1904, Oenslager et al. found that aniline is accelerated sulfur cure system. Recently, many rubber industries needed high yield and good quality. So, many researchers have studied a rubber system with fast vulcanization time and good mechanical properties. In this study, cure characteristics and mechanical properties of NR/BR compounds by accelerator with MBTS(2,2' Dithiobisbenzothiazole), TMTM(Tetramethylthiuram Monosulfide), ZDMC (Zinc dimethyldithiocarbamate), CBS(N-Cyclohexyl benzothiazolyl-2-sulfenamide), DPG(Diphenylguanidine) were evaluated. The results of the study indicate that cure charateristics($t_{90}$: 235 sec, $T_{max}$: 5.77 Nm) and mechanical properties (100, 300% modulus : 2,180, 5.656 Mpa and tear strength: 59.58 kgf/cm) of NR/BR compounds shows efficient acceleration with MBTS 1.5 phr, TMTM 0.5 phr, DPG 0.15phr. This is due to the synergistic activity of ternary accelerator system in rubber vulcanization.