• The korean journal of orthodontics
• /
• v.14 no.2
• /
• pp.241-248
• /
• 1984

The mechanical properties of Cr-Ni alloy of austenitic stainless steel and Co-Cr alloy orthodontic wires were studied in tension. The wires (0.018 inch) were tested in the as-manufactured and heat-treated conditions. Instron type tension testing machine was used for this study. Mean values and standard deviations were computed. The results were as follows; 1. The Cr-Ni orthodontic wires of austenitic stainless steel are generally superior than the Co-Cr orthodontic wires in ultimate tensile strength, In the elongation, however, Co-Cr orthodontic wire are superior than Cr-Ni orthodontic wires. 2. Increase in the degree of strength by heat treatment are more clearly shown in Co-Cr orthodontic wires than Cr-Ni orthodontic wires. And the elongation is decreased by heat treatment in both case. 3. The changes of the degree of strength by cooling method we not clearly shown, but in Cr-Ni orthodontic wires, air cooling are more effective, in Co-Cr orthodontic wires, cooling effect are scarcely shown.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.189-194
• /
• 2003

It is important to evaluate strength of dissimilar weld zone to use dissimilar materials safely. This study examines mechanical characteristics of dissimilar weld zone between low alloy steel and austenitic stainless steel that satisfies welding related requirements of ASME Code, experimentally reviews metallurgical and mechanical properties at and adjacent to weld interface. It is confirmed that hardness singularity occurs at the weld interface, and that optimum buttering thickness is more than 5㎜ from view points of tensile & yield strength. From a macroscopic view, brittle fracture characteristics is observed in buttering weld zone by tensile test.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.670-677
• /
• 2003

Although Gas Tungsten Arc Welding (GTAW or TIG welding) is considered as high quality and precision welding process, it also has demerit of low melting rate. Narrow-gap TIG welding which has narrow joint width reduces the groove volume remarkably, so it could be shorten the welding time and decrease the overall shrinkage in heavy wall pipe welding. Generally Narrow-gap TIG welding is used as orbital welding process, it is important to select the optimum conditions for the automatic control welding This paper looks at the application and metallurgical properties on Narrow-gap TIG welding joint of heavy wall large austenitic stainless steel pipe to determine the deposition efficiency, the resultant shrinkage and fracture toughness. The fracture toughness depends slightly on the welding heat input.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.26 no.3
• /
• pp.198-205
• /
• 2006

The necessity of nondestructively inspecting austenitic steels, fiber-reinforced composites, and other inherently anisotropic materials has stimulated considerable interest in developing beam models for anisotropic media. The properties of slowness surface playa key role in the beam models based on the paraxial approximation. In this paper, we apply a modular multi-Gaussian beam (MMGB) model to study the effects of material anisotropy on ultrasonic beam profile. It is shown that the anisotropic effects of beam skew and excess beam divergence enter into the MMGB model through parameters defining the slope and curvature of the slowness surface. The overall beam profile is found when the quasilongitudinal(qL) beam propagates in the symmetry plane of transversely isotropic austenitic steels. Simulation results are presented to illustrate the effects of these parameters on ultrasonic beam diffraction and beam skew. The MMGB calculations are also checked by comparing the anisotropy factor and beam skew angle with other analytical solutions.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.3 no.1
• /
• pp.19-25
• /
• 1983

Some studies have been made on the effects of the attenuation on the result of ultrasonic examination of austenitic stainless steel weldment and also on the cause of false indications. The differences in the amplitudes and the metal paths of the ultrasonic examinations have been measured experimentally, for two kinds of waves, one passed through only the parent material and the other one through the weldment. The effect of probe angles and frequency on the examination data have been investigated using the shear wave. It has been found that the false indications were caused by back reflection from the weld metal surface due to the characteristics of ultrasonic wave propagation. It has been confirmed that the probe of $2.25\;MHz\;and\;60^{\circ}$ is the best choice in the ultrasonic examination and that the correction of amplitude for attenuations is necessary.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.65-78
• /
• 1997

The effect of $O_2$and Al contents and the variation of welding parameters such as arc currents, welding speed on the weld penetration was investigated. Examination of weld penetration using GTAW was accomplished in the ferritic STS410L and austenitic STS304. Good penetration could be controlled by the variation of $O_2$ and Al contents in STS304. However, influences of $O_2$ and Al contents on the ferritic STS410L are far less than those on the austenitic STS304. Welding parameters should be considered first before controlling $O_2$ and Al contents for a good penetration in ferritic STS410L. In the simulation study under the stationary heat sources, the results of simulation and experiment have a similar tendency.

• Journal of Advanced Marine Engineering and Technology
• /
• v.9 no.2
• /
• pp.153-158
• /
• 1985

The dependence of the corrosion potential on the stress corrosion cracking of 304 austenitic stainless steel was inspected by using the specimen of constant displacement type under the environment of 42% $MgCl_2$ boiled solution. The relationship of the corrosion potential to the intermittent propagation behaviour in stress corrosion cracking was cleared. As the results, a possible model of stress corrosion cracking of 304 austenitic stainless steel in $MgCl_2$ boiled solution was presented on the basis of the Film Rupture Model. This model is specified by the following process. Rupturing of passive film at notch tip .rarw. Dissolution of metal ion and formation of tunnel .rarw. Initiation of microcrack .rarw. Propagation of main crack .rarw. Recreation of passive film at new crack surface.

• Journal of Korea Foundry Society
• /
• v.17 no.1
• /
• pp.36-50
• /
• 1997

Invar-type austenitic cast irons are being used as low thermal expansive materials because of its good low thermal expansion characteristics and castability despite its low hardness. The effects of alloying elements such as Cr, Ti, V, and Mo on hardness and linear thermal expansion coefficient of the invar-type austenitic cast irons were investigated. A combined use of V and Mo addition was found to be the most effective for the improvement of hardness without causing an increase in the thermal expansion coefficient. With a combined addition of 4.6wt%V and 3.8wt%Mo, the hardness increased up to 180HB and the thermal expansion coefficient was kept at a relatively low value of $4.6{\times}10^{-6}/^{\circ}C$ in the temperature range from room to $250^{\circ}C$.

• Journal of Welding and Joining
• /
• v.11 no.1
• /
• pp.21-32
• /
• 1993

A cracking failure of a austenitic stainless steel elbow in a naphtha cracking line in a petrochenmical plant occurred, resulting in leakage of organic compound flowing inside the elbow. Due to the failure, emergency shutdown of the plant was enforced to repair the troubled part of the line. The repair cost as well as production loss during the unscheduled plant shutdown has cost the company a great amount of financial loss. In this studies, a failure analysis of the cracked elbow was performed using NDT, chemical analysis, microstructural analysis including optical microscopy as well as scanning electron microscopy with EPMA, mechanical testings such as tensile testing, hardness testing and Charphy impact test fractography. The results indicated that several problems such as a welding defect and presence of a detrimental phase which was found to be relate to improper postforming heat treatment process was identified and the failure was concluded to be due to a low temperature embrittlement of the defect-containing elbows.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.50-54
• /
• 1999

Feasibility study of the application of a developed annealed austenitic stainless steel at cryogenic temperature has been performed for membrane tank of LNG ship. Chemical properties of developed stainless steel are compared with a domestic commercial stainless steel and a foreign stainless steel which are used for LNG ships. Tensile properties at cryogenic temperature and fatigue strength at room temperature are measured for but and lap joints which are TIG welded specimens. Developed stainless steel having a small amount of titanium component shows the finest grain size in the HAZ, compared with the other stainless steel studied. Tensile strength, elongation and fatigue strength of the developed stainless steel are equal to those of the foreign stainless steel studied and are higher than the domestic commercial stainless steel studied.