• Journal of the Korean Wood Science and Technology
• /
• v.26 no.3
• /
• pp.9-15
• /
• 1998

The strength and stiffness of structures would be weakened by thermal degradation of wood members which are exposed to a variety of heat including a fire. For this reason, thermal degraded wood members can't pertinently support the load. However, it is easy to repair or rehabilitate wood structures. So, the degraded wood members which can't support the load can be replaced with new members. For the sake of this advantage, there is a need for nondestructive evaluation(NDE) technique, which is very effective to assess wood members in service. In this paper, it was considered whether the stress wave method is adequate to estimate static bending MOE of thermal degraded wood. As the result, the relationship between static bending MOE and MOEsw in elevated temperature was found out significant. Therefore, the application of stress wave method for estimating static bending MOE of thermal degraded zzwood would be possible. However, it is thought that further research for the effects of exposure temperature, time, and thermal degradation on the relationship between static bending MOEb and MOEsw would be needed.

• Journal of Korea Foresty Energy
• /
• v.22 no.1
• /
• pp.44-48
• /
• 2003

Flexural properties were investigated on clear specimens made from small diameter thinned trees of pitch pine (Pinus rigida Mill.), Japanese red pine (Pinus densiflora Sieb. et Zucc), Japanese larch (Larix kaempferi Carr.), and sawtooth oak (Quercus acutissima Carr.). MOR and MOE values of small clear specimen were depended on the species. The highest density of sawtooth oak shows the highest values of MOR and MOE. However, the lowest density of Japanese larch shows the lowest values of MOR. It was also shown that flexural properties could be predicted by stress wave MOE, since the correlations between stress wave MOE and flexural properties were relatively good.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.1
• /
• pp.8-14
• /
• 1997

Stress wave velocity, wave impedance, and stress wave elasticity of small, clear bending specimens of five domestic softwoods (Pinus densiflora, Pinus koraiensis, Chamaecyparis obtusa, Cryptomeria japonica, and Larix leptolepis) and four tropical hardwoods(Kempas, Malas, Taun, and Terminalia) were correlated with static bending modulus of elasticity(MOE) and modulus of rupture(MOR). The degree of correlation between stress wave parameters and static bending properties was dependent on wood species tested. Stress wave elasticity and wave impedance were better predictors for static bending properties than stress wave velocity for each species individually and for softwood or hardwood species taken as a group, even though elasticity and impedance were nearly equally correlated with static bending properties apparently. Based upon the correlation coefficient between stress wave parameters and static properties, stress wave elasticity and wave impedance were found as stress wave parameters which can be used for the purpose of the reliable and successful prediction of bending properties. The degree of correlation between static MOE and MOR was also different according to wood species tested. Static MOE was nearly as well correlated with MOR as was stress wave elasticity. The results of this research are encouraging and can be considered as a basis for further work using full-size lumber. From the results of this study, it was concluded that stress wave measurements could provide useful predictions of static bending properties and was a feasible method for machine stress grading of domestic softwoods and tropical hardwoods tested in this study.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.3
• /
• pp.35-41
• /
• 2003

The mechanical and physical properties of wood are strongly dependent upon the slope of grain. Specially, tensile strength is more severely affected by the slope of grain. Therefore, tension tests were performed on small thin wood samples made from Pinus radiata with varying the slope of grain. Determining the tensile strength for clear thin wood samples the other variabilities associated with material, size, drying, defects, etc were discarded. Slope of grain was measured by the slope of grain indicator and actual slope of grain was also determined by a protractor. Correlation coefficients between machine measured and actual slope of grain for 40 pieces of 2×20 mm, 300 mm long Pinus radiata were 0.84 for wide face measurement. Results also showed that tensile strength and MOE from stress wave tests decreased with increasing the slope of grain. This study did not establish a relationships for tensile strength and MOE from stress wave with slope of grain. However, the trends of MOEs from stress wave test with both slope of grain are agreed well with Hankinson's equation. Predicted tension strength curve by Hankinson's equation was also agreed well with the experimental data over the range from 0 to 13 degrees for slope of grain.

• Journal of the Korean Wood Science and Technology
• /
• v.24 no.4
• /
• pp.7-14
• /
• 1996

두께가 20mm와 30mm이고 폭이 40mm와 60mm 인 길이 600mm의 낙엽송 제재목에 응력파 시험과 휨강도 시험을 실시하였다. 모든 시험편은 생재 상태로 구입 후 함수율 약 13%로 조습 처리하여 응력파 시험과 휨강도 시험을 시행하였다. 휨 영계수와 휨강도는 두께가 큰 것이 작게 나타났다. 최상의 상관관계는 휨 영계수와 양 표면에서 구한 값의 평균값을 사용한 응력파 속도 및 영계수 사이에 나타났다. 휨 영계수와 관계에서 응력파 영계수는 응역파 속도 보다 더 확연한 옹이의 영향을 보였다.

• Journal of the Korean Wood Science and Technology
• /
• v.24 no.3
• /
• pp.90-100
• /
• 1996

두께가 20mm 와 30mm 이고, 폭이 40mm 와 60mm인 600mm 길이의 낙엽송 제재목에 응력파 시험을 실시하였다. 모든 시험편은 생재 상태로 구입 후 함수율 27%, 22%, 17%과 12%조건으로 조습 처리하였다. 함수율 변화에 따른 응력파 속도와 영계수를 구하기 위한 응력파 시험을 4종류의 함수율 조건에서 실시하였다. 응력파 속도와 응력파 시험으로부터 구한 영계수는 시편의 함수율, 치수, 그리고 시험편의 옹이와 옹이 주변 목리의 상호작용에 의해 영향을 받았다. 모든 함수율 및 각 함수율 조건에서 응력파 속도는 응력파에 의해 구한 영계수와 양호한 상관관계를 나타냈다. 응력파 속도와 응력파 시험으로 구한 영계수는 함수율이 증가할 때 비선형적으로 감소하였으나, 함수율 25% 이상에서는 응력파에 의해 구한 영계수의 변화가 거의 없었다.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.1
• /
• pp.36-42
• /
• 2015

This study examined true modulus of elasticity (MOE) and modulus of rigidity (G) for domestic woods with different slenderness ratios (L/D) using the static bending and stress wave tests. Bending properties of small clear wood specimen of three domestic wood species were determined at 12% moisture content. The results of this study indicated that both MOR and MOE of domestic woods were affected by the slenderness ratio. As the slenderness ratio increased, MOR and MOE increased. G and true MOE of domestic timber beams were obtained at different slenderness ratios by flexure test and stress wave test. The values reported here can be useful if these species woods are used for structural purposes. However, the reported values are only indicative and do not represent the true average of wood species due to the limited number of specimens tested.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.1
• /
• pp.48-55
• /
• 2009

In the glulam beam deflection it is necessary to check the reliability of theory formula, because of wood anisotropy and wood qualities (knot, slop of grain). In this experiment, when bending stress occurred on glulam, practice deflection of glulam measuring with AICON DPA-Pro 3D system were compared with prediction deflection calculated as substituting MOE through non-destructive testing and static MOE through bending test in differential equation of deflection curve. MOE using ultrasonic wave tester of laminae, MOE using natural frequencies of longitudinal vibrations ($E_{cu}$, $E_{cf}$), MOE using ultrasonic wave tester of glulam ($E_{gu}$) and MOE using natural frequencies of longitudinal vibrations ($E_{gf}$) were substituted in this experiment. When practice deflection measured by 3D system was compared with prediction deflection calculated with differential equation of deflection curve, within proportional limit the ratio of practice deflection and prediction deflection was similar as 1.12 and 1.14, respectively. Deflection using ultrasonic wave tester was 0.89 and 0.95, Deflection using natural frequencies of longitudinal vibrations was 1.07 and 1.10. The results showed that prediction deflection calculated by substituting using non-destructive MOE of glulam having anisotropy in differential equation of deflection curve was agreed well with practice deflection.